Method of producing a coated fiber-containing composite

Claim 2

A process for producing a composite comprised of boron nitride coated fibrous material in a ceramic matrix which comprises the following steps: (a) providing matrix-forming ceramic particulate material and organic binding material; (b) forming a slurry of said matrix-forming material and organic binding material in a liquid medium; (c) depositing a coating of boron nitride on fibrous material leaving no significant portion thereof exposed; (d) providing said boron nitride coated fibrous material substantially as a layer; (e) casting said slurry onto said coated fibrous material in an amount sufficient to form a tape therewith; (f) evaporating said liquid medium forming a tape; (g) assembling a plurality of said tapes to produce a layered structure; (h) laminating the layered structure to form a laminated structure; (i) heating said laminated structure to remove said organic binding material leaving no significant deleterious residue; and (j) hot pressing the resulting porous structure at a sufficient temperature under a sufficient pressure for a sufficient period of time to consolidate said structure to produce said composite having a porosity of less than about 10% by volume, said composite containing no significant amount of reaction product of said coated fibrous material and said matrix, said ceramic matrix having a thermal expansion coefficient which ranges from lower than that of said coated fibrous material to less than about 15% higher than that of said coated fibrous material, at least about 10% by volume of said composite being comprised of said coated fibrous material.

Claim 3

The process according to claim 1, wherein said fibrous material contains at least about 1% by weight of carbon.

Claim 4

The process . . . silicon carbide, silicon nitride, and any combinations thereof.

Claim 5

The process . . . silicon carbide, silicon nitride, and any combinations thereof.

Claim 6

The process . . . Si-C-O-metal, Si-C-O-N-metal, and any combinations thereof, where . . . material.

Claim 7

The process . . . Si-C-O-metal, Si-C-O-N-metal, and any combinations thereof, where . . . material.

Claim 8

The process . . . Si-N-O-metal, Si-C-O-N-metal and any combinations thereof, wherein . . . material.

Claim 9

The process . . . Si-N-O-metal, Si-C-O-N-metal and any combinations thereof, wherein . . . material.

Claim 10

The process according to claim 1, wherein said fibrous material is selected from the group consisting of fibers, filaments, strands, bundles, whiskers, cloth, felt, and any combination thereof.

Claim 11

The process according to claim 1, wherein said slurry contains a member selected from the group consisting of whiskers and boron nitride coated whiskers ranging to about 50% by volume of said matrix-forming ceramic material.

Claim 12

The process according to claim 1, wherein said matrix-forming material is comprised of an oxide-based crystalline ceramic.

Claim 13

The process according to claim 1, wherein said matrix-forming ceramic particulate material is selected from the group consisting of aluminum oxide, mullite, silicon carbide, silicon nitride, and zircon.

Claim 14

The process according to claim 1, wherein before said layered structure is assembled, an organic solution of organic binder is sprayed on faces of tapes to be contacted with each other and dried to leave a sticky film of organic binder in amount sufficient to at least significantly enhance adhesion.

Claim 15

The process according to claim 1, wherein said matrix has a thermal expansion coefficient ranging from lower than that of said coated fibrous material to about the same as that of said coated fibrous material.

Claim 16

The process according to claim 1, wherein said coated fibrous material is comprised of a plurality of continuous coated filaments wherein said coated filaments are spaced from each other.

Claim 17

The process according to claim 1, wherein said boron nitride coated fibrous material is comprised of a plurality of continuous coated filaments spaced from each other, and wherein said slurry contains a member selected from the group consisting of whiskers and boron nitride coated whiskers ranging to about 50% by volume of said matrix-forming ceramic material.

Claim 18

The process according to claim 1, wherein said matrix-forming ceramic particulate material is mullite.

Claim 19

The process according to claim 1, wherein said matrix-forming ceramic particulate material is silicon carbide.

Claim 20

The process according to claim 1, wherein said matrix-forming ceramic particulate material is silicon nitride.

Claim 21

The process according to claim 1, wherein said slurry contains whiskers ranging to about 50% by volume of said matrix-forming ceramic material.

Claim 22

The process according to claim 1, wherein said slurry contains silicon carbide whiskers ranging to about 50% by volume of said matrix-forming ceramic material.

Claim 23

The process according to claim 1, wherein said slurry contains silicon nitride whiskers ranging to about 50% by volume of said matrix-forming ceramic material.

Claim 24

A process for producing a composite comprised of boron nitride coated fibrous material in a zircon matrix which comprises the following steps: (a) providing matrix-forming zircon particulate material and organic binding material; (b) forming a slurry of said matrix-forming material and organic binding material in a liquid medium; (c) depositing a coating of boron nitride on fibrous material leaving no significant portion thereof exposed; (d) providing said boron nitride coated fibrous material substantially as a layer; (e) casting said slurry onto said coated fibrous material in an amount sufficient to form a tape therewith; (f) evaporating said liquid medium forming a tape; (g) assembling a plurality of said tapes to produce a layered structure; (h) laminating the layered structure to form a laminated structure; (i) heating said laminated structure to remove said organic binding material leaving no significant deleterious residue; and (j) hot pressing the resulting porous structure at a sufficient temperature under a sufficient pressure for a sufficient period of time to consolidate said structure to produce said composite having a porosity of less than about 10% by volume, said composite containing no significant amount of reaction product of said coated fibrous material and said matrix, said matrix having a thermal expansion coefficient which ranges from lower than that of said coated fibrous material to less than about 15% higher than that of said coated fibrous material, at least about 10% by volume of said composite being comprised of said coated fibrous material.

Claim 25

A process for producing a composite comprised of boron nitride coated fibrous material in a zircon matrix which comprises the following steps: (a) providing matrix-forming zircon particulate material and organic binding material; (b) forming a slurry of said matrix-forming material and organic binding material in a liquid medium; (c) depositing a coating of boron nitride on fibrous material leaving no significant portion thereof exposed; (d) providing said boron nitride coated fibrous material substantially as a layer; (e) casting said slurry onto said coated fibrous material in an amount sufficient to form a tape therewith; (f) evaporating said liquid medium forming a tape; (g) assembling a plurality of said tapes to produce a layered structure; (h) laminating the layered structure to form a laminated structure; (i) heating said laminated structure to remove said organic binding material leaving no significant deleterious residue; and (j) hot pressing the resulting porous structure at a sufficient temperature under a sufficient pressure for a sufficient period of time to consolidate said structure to produce said composite having a porosity of less than about 10% by volume, said composite containing no significant amount of reaction product of said coated fibrous material and said matrix, said matrix having a thermal expansion coefficient which ranges from lower than that of said coated fibrous material to less than about 15% higher than that of said coated fibrous material, at least about 10% by volume of said composite being comprised of said coated fibrous material.

Claim 26

The process according to claim 20, wherein said fibrous material contains at least about 1% by weight of carbon.

Claim 27

The process according to claim 20, wherein said fibrous material is selected from the group consisting of aluminum oxide, mullite, elemental carbon, silicon carbide, silicon nitride, and any combinations thereof.

Claim 28

The process according to claim 20, wherein said fibrous material contains at least about 50% by weight of silicon and at least about 25% by weight of carbon based on the weight of said fibrous material and is selected from the group consisting of Si--C--O, Si--C--O--N, Si--C--O--Metal, Si--C--O--N--Metal, and any combinations thereof, wherein said O, N and metal are each present in an amount of at least about 1% by weight of said fibrous material.

Claim 29

The process according to claim 20, wherein said fibrous material contains at least about 50% by weight of silicon and at least about 25% by weight of nitrogen based on the weight of said fibrous material and is selected from the group consisting of Si--N--O, Si--C--O--N, Si--N--O--Metal, Si--C--O--N--Metal, and any combinations thereof, wherein said O, C and Metal are each present in an amount of at least about 1% by weight of said fibrous material.

Claim 30

The process according to claim 20, wherein said fibrous material is selected from the group consisting of fibrous, filaments, strands, bundles, whiskers, cloth, felt, and any combinations thereof.

Claim 31

The process according to claim 20, wherein said slurry contains boron nitride coated whiskers ranging to about 50% by volume of said matrix-forming zircon material.

Claim 32

The process according to claim 20, wherein said coated fibrous material is comprised of a plurality of continuous coated filaments wherein said coated filaments are spaced from each other.

Claim 33

The process according to claim 20, wherein said boron nitride coated fibrous material is comprised of a plurality of continuous coated filaments spaced from each other, and wherein said slurry contains a member selected from the group consisting of whiskers and boron nitride coated whiskers ranging to about 50% by volume of said matrix-forming zircon material.

Claim 34

The process according to claim 20, wherein said slurry contains whiskers ranging to about 50% by volume of said matrix-forming zircon material.

Claim 35

The process according to claim 20, wherein said slurry contains silicon carbide whiskers ranging to about 50% by volume of said matrix-forming zircon material.

Claim 36

The process according to claim 20, wherein said slurry contains silicon nitride whiskers ranging to about 50% by volume of said matrix-forming zircon material.

Claim 37

A process for producing a composite comprised of boron nitride coated fibrous material in an aluminum oxide matrix which comprises the following steps: (a) providing matrix-forming aluminum oxide particulate material and organic binding material; (b) forming a slurry of said matrix-forming material and organic binding material in a liquid medium; (c) depositing a coated of boron nitride on fibrous material leaving no significant portion thereof exposed; (d) providing said boron nitride coated fibrous material substantially as a layer; (e) casting said slurry onto said coated fibrous material in an amount sufficient to form a tape therewith; (f) evaporating said liquid medium forming a tape; (g) assembling a plurality of said tapes to produce a layered structure; (h) laminating the layered structure to form a laminated structure; (i) heating said laminated structure to remove said organic binding material leaving no significant deleterious residue; and (j) hot pressing the resulting porous structure at a sufficient temperature under a sufficient pressure for a sufficient period of time to consolidate said structure to produce said composite having a porosity of less than about 10% by volume, said composite containing no significant amount of reaction product of said coated fibrous material and said matrix, said matrix having a thermal expansion coefficient which ranges from lower than that of said coated fibrous material to less than about 15% higher than that of said coated fibrous material, at least about 10% by volume of said composite being comprised of said coated fibrous material.

Claim 38

A process for producing a composite comprised of boron nitride coated fibrous material in an aluminum oxide matrix which comprises the following steps: (a) providing matrix-forming aluminum oxide particulate material and organic binding material; (b) forming a slurry of said matrix-forming material and organic binding material in a liquid medium; (c) depositing a coated of boron nitride on fibrous material leaving no significant portion thereof exposed; (d) providing said boron nitride coated fibrous material substantially as a layer; (e) casting said slurry onto said coated fibrous material in an amount sufficient to form a tape therewith; (f) evaporating said liquid medium forming a tape; (g) assembling a plurality of said tapes to produce a layered structure; (h) laminating the layered structure to form a laminated structure; (i) heating said laminated structure to remove said organic binding material leaving no significant deleterious residue; and (j) hot pressing the resulting porous structure at a sufficient temperature under a sufficient pressure for a sufficient period of time to consolidate said structure to produce said composite having a porosity of less than about 10% by volume, said composite containing no significant amount of reaction product of said coated fibrous material and said matrix, said matrix having a thermal expansion coefficient which ranges from lower than that of said coated fibrous material to less than about 15% higher than that of said coated fibrous material, at least about 10% by volume of said composite being comprised of said coated fibrous material.