Method of manufacturing dehumidifier element
Assignee: Seibu Giken Co Ltd
•
Filing: 1988-07-01
•
Granted: 1990-03-27
•
Expires: 2008-07-01
Abstract
Abstract A dehumidifier element is produced by alternately laminating corrugated paper and flat liner paper, both papers being of low density and composed of inorganic fiber such as ceramic fiber, to form a honeycomb matrix having many small channels penetrating through opposite surfaces. The formed matrix is fired with hot air to remove organic substances contained in the sheets, or the sheets may be fired before the lamination. The matrix is impregnated with water glass after the laminating process, or the sheets are impregnated before the laminating process. In either case, the formed matrix is soaked in an aqueous solution of aluminum sulphate or magnesium sulphate to form a silicate hydrogel on the papers and in the apertures between fibers of the papers. The shaped matrix and the metal silicate hydrogel are washed and dried to obtain a dehumidifying element having physical strength. The metal sulphate solution is cooled to precipitate and remove sodium sulphate from the solution. Additional sulphate is added to the metal sulphate solution for repeating the manufacturing process for another dehumidifier element. The main constituent of the element is metal silicate aerogel deposited in the apertures between the fibers of the inorganic fiber paper and on the inorganic fiber paper, which acts as an adsorbent.
Inventors
- 👤 Tosimi Kuma
- 👤 Hiroshi Okano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 21:30
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/26; B01D53/261; B01D53/28; B31; B31D; B31D3/00; B31D3/005; F; F24; F24F; F24F3/00; F24F3/12; F24F3/14; F24F3/1411; F24F3/1423; F24F3/147; F24F2003/1458; F24F2003/1464; F24F2203/00; F24F2203/10; F24F2203/1004; F24F2203/1032; F24F2203/1036; F24F2203/1048; F24F2203/1056; F24F2203/1068; F24F2203/1084; F24F2203/1096; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1007; Y10T156/1016; Y10T156/1021
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
286 words
A method of manufacturing a dehumidifier element comprising the steps of: (a) alternately laminating a flat sheet and a corrugated sheet of low density papers, the main constituent of the papers being inorganic fiber selected from the group consisting of ceramic fiber, glass fiber, rock fiber, carbon fiber, slag fiber and mixtures of not less than two of said fibers, to form a honeycomb matrix having many small channels; (b) heating the matrix to a temperature of 200°-500° C. to remove organic substances contained in the matrix and to decrease the density of sheets; (c) impregnating the matrix with an aqueous solution of sodium silicate water glass; (d) heating and drying the impregnated matrix so that the sodium silicate water glass becomes hydrated water glass or half-solid state water glass; (e) soaking the matrix in an aqueous solution of metal sulphate selected from the group consisting of aluminum sulphate and magnesium sulphate to react with the sodium silicate water glass to form silicate hydrogel on the sheets in the matrix and in the apertures between fibers in the sheets; (f) washing and drying the matrix to change the silicate hydrogel into silicate aerogel and to obtain the dehumidifier element; (g) cooling the aqueous solution of metal sulphate to precipitate and remove sodium sulphate, which is produced as a by-product of the reaction with the sodium silicate water glass and is dissolved in the aqueous solution of metal sulphate; and (h) adding sodium silicate to the aqueous solution of sodium silicate after the reaction and adding additional metal sulphate to the aqueous solution of metal sulphate after reaction to prepare the solution to repeat said steps (c) to (e) for a next dehumidifier element to be manufactured.
Claim 2
Independent Claim
286 words
A method of manufacturing a dehumidifier element comprising the steps of: (a) alternately laminating a flat sheet and a corrugated sheet of low density papers, the main constituent of the papers being inorganic fiber selected from the group consisting of ceramic fiber, glass fiber, rock fiber, carbon fiber, slag fiber and mixtures of not less than two of said fibers, to form a honeycomb matrix having many small channels; (b) heating the matrix to a temperature of 200°-500° C. to remove organic substances contained in the matrix and to decrease the density of sheets; (c) impregnating the matrix with an aqueous solution of sodium silicate water glass; (d) heating and drying the impregnated matrix so that the sodium silicate water glass becomes hydrated water glass or half-solid state water glass; (e) soaking the matrix in an aqueous solution of metal sulphate selected from the group consisting of aluminum sulphate and magnesium sulphate to react with the sodium silicate water glass to form silicate hydrogel on the sheets in the matrix and in the apertures between fibers in the sheets; (f) washing and drying the matrix to change the silicate hydrogel into silicate aerogel and to obtain the dehumidifier element; (g) cooling the aqueous solution of metal sulphate to precipitate and remove sodium sulphate, which is produced as a by-product of the reaction with the sodium silicate water glass and is dissolved in the aqueous solution of metal sulphate; and (h) adding sodium silicate to the aqueous solution of sodium silicate after the reaction and adding additional metal sulphate to the aqueous solution of metal sulphate after reaction to prepare the solution to repeat said steps (c) to (e) for a next dehumidifier element to be manufactured.
Claim 3
Dependent Claim
28 words
A method of manufacturing a dehumidifier element according to claim 1, wherein the sheets are impregnated with the aqueous solution of sodium silicate water glass beforesaid laminating step.
Claim 4
Dependent Claim
43 words
A method of manufacturing a dehumidifier element according to claim 1, wherein the flat sheet and the corrugated sheet are impregnated with an aqueous solution of sodium silicate water glass and are heated to a temperature of 200°-500° C. before said laminating step.
Claim 5
Dependent Claim
48 words
A method of manufacturing a dehumidifier element according to claim 1, wherein step (a) further comprises laminating the sheets with the aqueous solution of sodium silicate water glass as an adhesive which reacts with the metal sulphate to produce silicate aerogel having adsorption activity and maintaining adhesive activity.
Claim 6
Dependent Claim
29 words
A method of manufacturing a dehumidifier element according to claim 1, wherein said heating step comprises treating the matrix with air having a temperature range of 200° C.-500° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-26 | 1993-09-25 | 1994-03-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-26 | 1997-09-25 | 1998-03-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-26 | 2001-09-25 | 2002-03-27 | $7700.00 | Window Closed / Lapsed |