Preparation of mullite whiskers from AlF3, SiO2, and Al2 O3 powders
Assignee: United States Department of the Navy
•
Filing: 1989-02-08
•
Granted: 1990-03-20
•
Expires: 2009-02-08
Abstract
Abstract A process for preparing mullite whiskers by (1) forming an anhydrous, intimate, uniform mixture of AlF3, Al2O3, and fused SiO2 powders in an amount selected to produce stoichiometric mullite or a solid solution of Al2O3 in stoichiometric mullite; (2) heating the mixture in anhydrous SiF4 atmosphere at a temperature of from about 700 DEG to about 950 DEG C. to form barlike topaz crystals; (3) heating the barlike topaz in an anhydrous SiF4 atmosphere a a temperature of from about 1150 DEG C. to about 1700 DEG C. to produce the mullite whiskers.
Inventors
- 👤 Inna G. Talmy
- 👤 Deborah A. Haught
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 08:28
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/16; C04B35/18
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
191 words
A process for forming mullite whiskers comprising the following steps in order: (1) forming a loose uniform mixture of anhydrous AlF 3 , Al 2 O 3 , and fused SiO 2 powders in amounts selected to produce mullite whiskers containing Al 2 O 3 in an amount of from 70.50 weight percent up to the amount that produces a saturated solution of Al 2 O 3 in stoichiometric mullite, with SiO 2 comprising the remainder of the mullite, wherein from more than zero to 75 percent of the Al 2 O 3 in the mullite is supplied by the Al 2 O 3 powder with the remainder being supplied by the AlF 3 powder; (2) heating the mixture in an anhydrous SiF 4 atmosphere at a temperature of from about 700° C. to about 950° C. until the AlF 3 , SiO 2 , and Al 2 O 3 react to form barlike topaz crystals; and (3) heating the barlike topaz crystals in an anhydrous SiF 4 atmosphere at a temperature of from about 1150° C. to about 1700° C. until the barlike topaz crystals are converted to mullite whiskers.
Claim 2
Dependent Claim
191 words
A process for forming mullite whiskers comprising the following steps in order: (1) forming a loose uniform mixture of anhydrous AlF 3 , Al 2 O 3 , and fused SiO 2 powders in amounts selected to produce mullite whiskers containing Al 2 O 3 in an amount of from 70.50 weight percent up to the amount that produces a saturated solution of Al 2 O 3 in stoichiometric mullite, with SiO 2 comprising the remainder of the mullite, wherein from more than zero to 75 percent of the Al 2 O 3 in the mullite is supplied by the Al 2 O 3 powder with the remainder being supplied by the AlF 3 powder; (2) heating the mixture in an anhydrous SiF 4 atmosphere at a temperature of from about 700° C. to about 950° C. until the AlF 3 , SiO 2 , and Al 2 O 3 react to form barlike topaz crystals; and (3) heating the barlike topaz crystals in an anhydrous SiF 4 atmosphere at a temperature of from about 1150° C. to about 1700° C. until the barlike topaz crystals are converted to mullite whiskers.
Claim 3
Dependent Claim
71 words
The process of claim 1 wherein the AlF 3 , Al 2 O 3 , and fused SiO 2 powders are used in amounts selected to produce mullite whiskers containing Al 2 O 3 in an amount of from 71.80 weight percent up to the weight percent that produces a saturated solution of Al 2 O 3 in stoichiometric mullite, with SiO 2 comprising the remainder of the mullite whisker composition.
Claim 4
Dependent Claim
45 words
The process of claim 2 wherein the AlF 3 , Al 2 O 3 , and fused SiO 2 powders are used in amounts selected to produce mullite whiskers containing from 71.80 to 73.00weight percent Al 2 O 3 with SiO 2 being tee remainder.
Claim 5
Dependent Claim
46 words
The process of claim 3 wherein the AlF 3 , Al 2 O 3 , and fused SiO 2 powders are used in amounts selected to produce mullite whiskers containing from 71.80 to 72.00 weight percent Al 2 O 3 with SiO 2 being the remainder.
Claim 6
Dependent Claim
23 words
The process of claim44 wherein AlF 3 , and fused SiO 2 powders are used in amounts selected to produce stoichiometric mullite whiskers.
Claim 7
Dependent Claim
157 words
A process for forming barlike crystalline topaz comprising the following steps in order: (1) forming a loose uniform mixture of anhydrous AlF 3 , Al 2 O 3 , and fused SiO 2 powders in amounts selected to produce topaz which will produce mullite containing Al 2 O 3 in an amount of from 70.50 weight percent up to the amount that produces a saturated solution of Al 2 O 3 in stoichiometric mullite, with SiO 2 comprising the remainder of the mullite,, wherein from more than zero to 75 percent of the aluminum in the topaz is supplied by the Al 2 O 3 powder with the remainder being supplied by the AlF 3 powder; and (2) heating the mixture in an anhydrous SiF 4 atmosphere at a temperature of from 700° C. to about 950° C. until the AlF 3 , SiO 2 , and Al 2 O 3 react to for barlike topaz crystals.
Claim 8
Dependent Claim
157 words
A process for forming barlike crystalline topaz comprising the following steps in order: (1) forming a loose uniform mixture of anhydrous AlF 3 , Al 2 O 3 , and fused SiO 2 powders in amounts selected to produce topaz which will produce mullite containing Al 2 O 3 in an amount of from 70.50 weight percent up to the amount that produces a saturated solution of Al 2 O 3 in stoichiometric mullite, with SiO 2 comprising the remainder of the mullite,, wherein from more than zero to 75 percent of the aluminum in the topaz is supplied by the Al 2 O 3 powder with the remainder being supplied by the AlF 3 powder; and (2) heating the mixture in an anhydrous SiF 4 atmosphere at a temperature of from 700° C. to about 950° C. until the AlF 3 , SiO 2 , and Al 2 O 3 react to for barlike topaz crystals.
Claim 9
Dependent Claim
38 words
The process of claim 6 wherein from more than zero to 50 percent of the aluminum in the topaz is supplied by the Al 2 O 3 powder with the remainder being supplied by the AlF 3 powder.
Claim 10
Dependent Claim
73 words
The process of claim 6 wherein the AlF 3 , Al 2 O 3 , and fused SiO 2 powders are used in amounts selected to produce barlike topaz crystals which will produce mullite containing Al 2 O 3 in an amount of from 71.80 weight percent up to the amount that produces a saturated solution of Al 2 O 3 in stoichiometric mullite with SiO 2 comprising the remainder of the mullite.
Claim 11
Dependent Claim
51 words
The process of claim 8 wherein the AlF 3 , Al 2 O 3 , and fused SiO 2 powders are used in amounts selected to produce barlike topaz crystals which will produce mullite containing from 71.80 to 73.00 weight percent Al 2 O 3 with SiO 2 being the remainder.
Claim 12
Dependent Claim
51 words
The process of claim 9 wherein the AlF 3 , Al 2 O 3 , and fused SiO 2 powders used in amounts selected to produce barlike topaz crystals which will produce mullite containing from 71.80 to 72.00 weight percent of Al 2 O 3 with SiO 2 being the remainder.
Claim 13
Dependent Claim
35 words
The process of claim 10 wherein the AlF 3 , Al 2 O 3 , and fused SiO 2 powders are used in amounts selected to produce barlike topaz crystals which will produce stoichiometric mullite.
Claim 14
Dependent Claim
38 words
The process of claim 11 wherein from more than zero to 50 percent of the aluminum in the topaz is supplied by the Al 2 O 3 powder with the remainder being supplied by the AlF 3 powder.
References Cited (Backward Citations)
US2195949A
Cited
CA857341A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-19 | 1993-09-18 | 1994-03-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-19 | 1997-09-18 | 1998-03-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-19 | 2001-09-18 | 2002-03-20 | $7700.00 | Window Closed / Lapsed |