US4908053A — Process for producing chalcogenide glass fiber

Claim 1

Independent Claim 82 words

A process for producing a chalcogenide glass fiber which comprises placing a cylindrical chalcogenide glass preform vertically in a cylindrical crucible furnished with a nozzle in its bottom portion, heating the crucible only at vicinity of the nozzle, and continuously drawing the glass into a fiber with the temperature of the crucible at the vicinity of the nozzle being maintained at such a level that the viscosity of the glass is within the range of 10 3 to 10 7 .5 poises.

Claim 2

Dependent Claim 82 words

A process for producing a chalcogenide glass fiber which comprises placing a cylindrical chalcogenide glass preform vertically in a cylindrical crucible furnished with a nozzle in its bottom portion, heating the crucible only at vicinity of the nozzle, and continuously drawing the glass into a fiber with the temperature of the crucible at the vicinity of the nozzle being maintained at such a level that the viscosity of the glass is within the range of 10 3 to 10 7 .5 poises.

Claim 3

Dependent Claim 48 words

A process according to claim 1, wherein a fiber is drawn from the preform as it is heated in the crucible where an inert gas atmosphere is maintained with the pressure in said crucible being held higher than atmospheric pressure but not higher than 5 kg/cm 2 .

Claim 4

Dependent Claim 59 words

A process according to claim 1, wherein the inside diameter R 1 of the nozzle in the bottom portion of the crucible is no smaller than 500 μm, with the upper limit being 0.95 as expressed by R 1 /R 2 where R 1 is the nozzle inside diameter and R 2 is the outside diameter of the preform.

Claim 5

Dependent Claim 41 words

A process according to claim 1, wherein the cylindrical preform has a diameter smaller than the inside diameter of said crucible, and the gap between the crucible and the perform is at least 2% of the inside diameter of said crucible.

Claim 6

Dependent Claim 39 words

A process according to claim 1, wherein said chalcogenide glass preform consists of a core glass in a rod shape that is inserted into a tube of a cladding glass having a lower refractive index than said core glass.

Claim 7

Dependent Claim 49 words

A process according to claim 5, wherein a fiber is drawn from the preform in the crucible with the pressure of the gas around the cladding tube of the preform being held higher than that of the gas in the gap between the cladding tube and the core rod.

Claim 8

Dependent Claim 52 words

A process according to claim 6, wherein the inert gas in the gap between the cladding tube of the preform and the core rod has a pressure of no higher than 10 -1 Torr, and the inert gas around the cladding tube has a pressure of at least 0.2 kg/cm 2 .

Claim 9

Dependent Claim 31 words

A process according to claim 5, wherein the cladding tube is allowed to adhere to the core rod thereby to form a unitary assembly before they are placed within the crucible.

Claim 10

Dependent Claim 103 words

A process according to claim 8, wherein the cladding tube is allowed to adhere to the core rod by inserting the core rod into the cladding tube and holding the combination in a closed vessel in which an inert atmosphere is maintained; and softening the cladding tube locally and continuously from one end to the other with the pressure of the inert gas in the gap between the cladding tube and the core rod being held no higher than 10 -1 Torr and with the pressure of the inert gas around the cladding tube being held no lower than 0.2 kg/cm 2 .

Claim 11

Dependent Claim 82 words

A process according to claim 5, wherein the cladding tube is fabricated by charging a cylindrical closed vessel with a chalcogenide glass of which said cladding tube is to be made; heating, with the cylindrical vessel being held horizontally, the chalcogenide glass to a temperature higher than its softening point and holding it at that temperature as the vessel is rotated around its longitudinal axis; and thereafter cooling the chalcogenide glass to the annealing point with the cylindrical vessel being kept rotating.

Claim 12

Dependent Claim 27 words

A process according to claim 10, wherein said cylindrical vessel is rotated at a speed of at least 20 rpm during the fabrication of the cladding tube.

Claim 13

Dependent Claim 203 words

A process for producing a chalcogenide glass fiber which comprises placing: a cylindrical chalcogenide glass preform vertically in a cylindrical crucible furnished with a nozzle in its bottom portion, said glass preform including a core glass in a rod shape that is inserted into a tube of a cladding glass having a lower refractive index than said core glass, the cladding tube adhering to the core rod thereby to form a unitary assembly, said assembly being inserted in a closed vessel in which an inert atmosphere is maintained; and softening the cladding tube locally and continuously from one end to the other with the pressure of the inert gas in the gap between the cladding tube and the core rod being held no higher than 10 -1 Torr and with the pressure of the inert gas around the cladding tube being held no lower than 0.2 kg/cm 2 ; heating the crucible only at the vicinity of the nozzle; and continuously drawing the glass into a fiber with the temperature of the crucible at the vicinity of the nozzle being maintained at such a level that the viscosity of the glass is within the range of 10 3 to 10 7 .5 poises.

Claim 14

Dependent Claim 203 words

A process for producing a chalcogenide glass fiber which comprises placing: a cylindrical chalcogenide glass preform vertically in a cylindrical crucible furnished with a nozzle in its bottom portion, said glass preform including a core glass in a rod shape that is inserted into a tube of a cladding glass having a lower refractive index than said core glass, the cladding tube adhering to the core rod thereby to form a unitary assembly, said assembly being inserted in a closed vessel in which an inert atmosphere is maintained; and softening the cladding tube locally and continuously from one end to the other with the pressure of the inert gas in the gap between the cladding tube and the core rod being held no higher than 10 -1 Torr and with the pressure of the inert gas around the cladding tube being held no lower than 0.2 kg/cm 2 ; heating the crucible only at the vicinity of the nozzle; and continuously drawing the glass into a fiber with the temperature of the crucible at the vicinity of the nozzle being maintained at such a level that the viscosity of the glass is within the range of 10 3 to 10 7 .5 poises.

Claim 15

Dependent Claim 139 words

A process according to claim 1, wherein a fiber is drawn from the preform as it is heated in the crucible where an inert gas atmosphere is maintained with the pressure in said crucible being held higher than atmospheric pressure but not higher than 5 kg/cm 2 ; the inside diameter R 1 of the nozzle in the bottom portion of the crucible is no smaller than 500 μm, with the upper limit being 0.95 as expressed by R 1 /R 2 where R 1 is the nozzle inside diameter and R 2 is the outside diameter of the preform; and the cylindrical preform placed within the crucible has a diameter smaller than the inside diameter of said crucible, and the gap between the crucible and the preform is at least 2% of the inside diameter of said crucible.

Claim 16

Dependent Claim 30 words

A process according to claim 6, wherein the pressure of the gas in the gap between the cladding tube and the core rod is not greater than 10 -1 Torr.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1993-03-12	1993-09-11	1994-03-13	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1997-03-12	1997-09-11	1998-03-13	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	2001-03-12	2001-09-11	2002-03-13	$7700.00	Window Closed / Lapsed

Process for producing chalcogenide glass fiber

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag