Hot melt type seal agent for a lamp
Assignee: Aica Kogyo Co Ltd
•
Filing: 1988-07-19
•
Granted: 1990-02-13
•
Expires: 2008-07-19
Abstract
Abstract The present invention relates to the hot melt type seal agent for adhering and sealing a head lamp of a vehicle, wherein a lens and a housing are integrally one unit. The necessary component materials of the hot melt type seal agent of the present invention include a mixture produced by butyl rubber, SEBS block copolymer and olefin with high softening point. The hot melt type seal agent of the present invention withstands temperature changes in the head lamp and the gas pressure that is filled therein. Consequently, good adhesion, waterproof and high gas-tight performances are achieved.
Inventors
- 👤 Atsushi Tomita
- 👤 Hidekatsu Sumi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 13:45
CPC Classifications
C; C09; C09J; C09J123/00; C09J123/02; C09J123/18; C09J123/20; C09J123/22; C09J153/00; C09J153/02; C09J153/025; C08; C08L; C08L2666/00; C08L2666/02; C08L2666/24
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
105 words
A hot melt type seal agent for a lamp comprising butyl rubber, styrene-ethylene-butylene-styrene block copolymer and olefin wax with a softening point higher than 110° C., the seal agent having a softening point higher than 110° C. measured by the ring and ball method, wherein the weight ratio of said butyl rubber to said block copolymer is between 90:10 and 40:60, and the amounts by weight of (1) said butyl rubber plus said block copolymer and (2) said olefin wax are from 20 to 50% and 5 to 30%, respectively, said seal agent further includes 0.5 to 5 weight % of a silane coupling agent.
Claim 2
Dependent Claim
105 words
A hot melt type seal agent for a lamp comprising butyl rubber, styrene-ethylene-butylene-styrene block copolymer and olefin wax with a softening point higher than 110° C., the seal agent having a softening point higher than 110° C. measured by the ring and ball method, wherein the weight ratio of said butyl rubber to said block copolymer is between 90:10 and 40:60, and the amounts by weight of (1) said butyl rubber plus said block copolymer and (2) said olefin wax are from 20 to 50% and 5 to 30%, respectively, said seal agent further includes 0.5 to 5 weight % of a silane coupling agent.
Claim 3
Dependent Claim
23 words
The hot melt type seal agent according to claim 1, wherein the softening point of the olefin wax is higher than 130° C.
Claim 4
Dependent Claim
32 words
The hot melt type seal agent according to claim 1, wherein the seal agent further comprises at least one material selected from the group consisting of tackifier, softener, filler, antioxidant, and colorant.
Claim 5
Dependent Claim
24 words
The hot melt type seal agent according to claim 3, wherein the seal agent is produced by kneading a mixture of the component materials.
Claim 6
Dependent Claim
43 words
The hot melt type seal agent according to claim 4, wherein the amount by weight of the material other than the butyl rubber, the styrene-ethylene-butylene-styrene block copolymer and the olefin wax which is present in the seal agent is from 20 to 75%.
Claim 7
Dependent Claim
31 words
The hot melt type seal agent according to claim 3, wherein the tackifier is at least one material selected from the group consisting of terpene resin, terpene-phenol resin, rosin and hydrogenated-rosin.
Claim 8
Dependent Claim
30 words
The hot melt type seal agent according to claim 1, wherein the olefin wax is an olefin comprising a carboxyl group with an equivalent molecular weight of less than 6,000.
Claim 9
Dependent Claim
21 words
The hot melt type seal agent according to claim 1, wherein the butyl rubber is a copolymer of isobutylene and diene-hydrocarbon.
Claim 10
Dependent Claim
15 words
The hot melt type seal agent according to claim 8, wherein the diene-hydrocarbon is isoprene.
References Cited (Backward Citations)
US4039364A
Cited
US4509821A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-02-12 | 1993-08-14 | 1994-02-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-02-12 | 1997-08-14 | 1998-02-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-02-12 | 2001-08-14 | 2002-02-13 | $7700.00 | Window Closed / Lapsed |