Abstract
Abstract Method of applying in accordance with a pattern thin layers of oxidic superconductive material onto a substrate, it not being necessary to subject the superconductive material to mechanical or chemical treatments. At its surface the substrate is provided in accordance with a desired pattern with two different material compositions. The first composition is chosen such that the oxidic material applied thereon is superconductive at a desired surface temperature. The second composition is chosen such that the oxidic material applied thereon is not superconductive.
Inventors
- 👤 Maritza G. J. Heijman
- 👤 Peter C. Zalm
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 13:43
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; H10N60/0296; H10N60/0661; H10N60/80; H10N60/85; Y; Y10; Y10S; Y10S505/00; Y10S505/725; Y10S505/73; Y10S505/742
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
167 words
A method of forming a patterned copper oxide based superconductor on a substrate operable at a particular service temperature comprising forming an exposed pattern of a first composition on the exposed surface of a second composition or forming an exposed pattern of said second composition on the exposed surface of said first composition wherein said first composition and said second composition are selected such that upon deposition of copper oxide based material under conditions necessary to form the superconductive properties, the region overlying said first composition forms a superconductive layer while the region overlying said second composition interacts under said depositing conditions in such a manner as to render the deposited copper oxide based superconductor material nonsuperconducting at the desired service temperature, applying said copper oxide based superconductive material to a surface containing both first and second compositions under conditions suitable to form the superconductive properties and obtaining a patterned substrate having a superconductive region overlying said first composition and a nonsuperconducting region overlying said second composition.
Claim 2
Independent Claim
167 words
A method of forming a patterned copper oxide based superconductor on a substrate operable at a particular service temperature comprising forming an exposed pattern of a first composition on the exposed surface of a second composition or forming an exposed pattern of said second composition on the exposed surface of said first composition wherein said first composition and said second composition are selected such that upon deposition of copper oxide based material under conditions necessary to form the superconductive properties, the region overlying said first composition forms a superconductive layer while the region overlying said second composition interacts under said depositing conditions in such a manner as to render the deposited copper oxide based superconductor material nonsuperconducting at the desired service temperature, applying said copper oxide based superconductive material to a surface containing both first and second compositions under conditions suitable to form the superconductive properties and obtaining a patterned substrate having a superconductive region overlying said first composition and a nonsuperconducting region overlying said second composition.
Claim 3
Dependent Claim
44 words
The method of claim 1 wherein the exposed areas of the first and second composition are formed by providing a portion of a surface of a substrate of said first composition with a thin layer of said second composition in accordance with a pattern.
Claim 4
Dependent Claim
44 words
The method of claim 1 wherein the exposed areas of the first and second compositions are formed by providing a portion of a surface of a substrate of said second composition with a thin layer of said first composition in accordance with a pattern.
Claim 5
Dependent Claim
16 words
A method as claimed in claim 1, characterized in that the first composition is strontium titanate.
Claim 6
Dependent Claim
26 words
A method as claimed in claim 1, characterized in that the first composition is a noble metal selected from the group consisting of silver and gold.
Claim 7
Dependent Claim
15 words
A method as claimed in claim 1, characterized in that the second composition is silicon.
Claim 8
Dependent Claim
16 words
A method as claimed in claim 1, characterized in that the second composition is aluminum oxide.
References Cited (Backward Citations)
US4316785A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-02-12 | 1993-08-14 | 1994-02-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-02-12 | 1997-08-14 | 1998-02-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-02-12 | 2001-08-14 | 2002-02-13 | $7700.00 | Window Closed / Lapsed |