Abstract
Abstract A flexible epoxy coated fabric has good hand, good wear resistance, good hydrolytic resistance, and good ultraviolet light resistance. An optional but desirable binder is a true coating and not an impregnation of the fabric in that at least 50 percent of the binder material resides on the surface of the fabric. A flexible epoxy material is utilized as a coating and generally has an intermediate hydrocarbon portion having at least 25 carbon atoms for each chain. The fabric is suitable as a substitute for leather in clothing, and upholstery as in automotive upholstery.
Inventors
- 👤 Richard W. Stamper
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:21
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/18; C08G59/20; C08G59/32; D; D06; D06N; D06N3/00; D06N3/12; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/24438; Y10T428/27; Y10T428/273; Y10T428/277; Y10T428/31504; Y10T428/31511; Y10T428/31515; Y10T442/00; Y10T442/20; Y10T442/2352; Y10T442/2369; Y10T442/259; Y10T442/273
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
58 words
An epoxy coated fabric, comprising: a fabric support coated with a flexible epoxy resin, said resin consisting essentially of an epoxy resin having an apparent bending modulus of from about 20 to about 2,000 psi as measured by ASTM D47-86 or an admixutre of said epoxy resin with up to 10% by weight of a rigid epoxy resin.
Claim 2
Dependent Claim
58 words
An epoxy coated fabric, comprising: a fabric support coated with a flexible epoxy resin, said resin consisting essentially of an epoxy resin having an apparent bending modulus of from about 20 to about 2,000 psi as measured by ASTM D47-86 or an admixutre of said epoxy resin with up to 10% by weight of a rigid epoxy resin.
Claim 3
Dependent Claim
64 words
An epoxy coated fabric, comprising: a fabric support coated with a flexible epoxy resin, wherein said flexible epoxy resin is (1) derived from an epoxy having the formula ##STR2## wherein n, independntly, is a whole number of at least about 25 for either of the chains or (2) an admixture of that epoxy resin with up to 10% weight of a rigid epoxy resin.
Claim 4
Dependent Claim
64 words
An epoxy coated fabric, comprising: a fabric support coated with a flexible epoxy resin, wherein said flexible epoxy resin is (1) derived from an epoxy having the formula ##STR2## wherein n, independntly, is a whole number of at least about 25 for either of the chains or (2) an admixture of that epoxy resin with up to 10% weight of a rigid epoxy resin.
Claim 5
Dependent Claim
27 words
An epoxy coated fabric according to claim 2, wherein at least 50 percent by weight of said epoxy resin resides on the surface of said fabric support.
Claim 6
Dependent Claim
27 words
An epoxy coated fabric according to claim 3, wherein the amount of said flexible epoxy is from about 1 ounce to about 50 ounces per square yard.
Claim 7
Dependent Claim
27 words
An epoxy coated fabric according to claim 4, wherein the amount of said flexible epoxy is from about 1 ounce to about 15 ounces per square yard.
Claim 8
Dependent Claim
26 words
An epoxy coated fabric according to claim 5, wherein said intermediate hydrocarbon portion of said flexible epoxy has from about 30 to about 40 carbon atoms.
Claim 9
Dependent Claim
26 words
An epoxy coated fabric according to claim 6, wherein the amount of said flexible epoxy is from about 2 to about 6 ounces per square yard.
Claim 10
Dependent Claim
31 words
An epoxy coated fabric as set forth in claim 2, wherein said epoxy coating has an apparent bending modulus according to ASTM D747-86 of from about 20 to about 20,000 psi.
Claim 11
Dependent Claim
29 words
An epoxy coated fabric according to claim 7, wherein said epoxy coating has an apparent bending modulus according to ASTM D747-86 of from about 30 to about 200 psi.
Claim 12
Dependent Claim
56 words
An epoxy coated fabric according to claim 9, wherein said fabric support is woven, wherein said fabric support is made from polyester fibers, and wherein said flexible epoxy resin contains up to 10 percent by weight of a rigid epoxy resin based upon the total weight of said rigid epoxy resin and said flexible epoxy resin.
Claim 13
Dependent Claim
49 words
An epoxy coated fabric according to claim 4, wherein said epoxy coating is applied to a grained release sheet, subsequently pressed onto said fabric support, heated to cure said epoxy and then said release sheet is removed to yield an epoxy coated fabric having a grain on the surface.
Claim 14
Dependent Claim
49 words
An epoxy coated fabric according to claim 6, wherein said epoxy coating is applied to a grained release sheet, subsequently pressed onto said fabric support, heated to cure said epoxy and then said release sheet is removed to yield an epoxy coated fabric having a grain on the surface.
Claim 15
Dependent Claim
95 words
A flexible epoxy coated lamina, comprising: a first discrete layer comprising a fabric; a second discrete layer comprising a flexible binder; and a third discrete layer comprising a flexible epoxy, said binder layer adhering said flexible epoxy layer to said fabric layer and said flexible epoxy resin is (1) derived from an epoxy having the formula ##STR3## wherein n, independently, is a whole number of at least about 25 for at least one of said chains or (2) an admixture of that epoxy resin with up to 10% by weight of a rigid epoxy resin.
Claim 16
Dependent Claim
95 words
A flexible epoxy coated lamina, comprising: a first discrete layer comprising a fabric; a second discrete layer comprising a flexible binder; and a third discrete layer comprising a flexible epoxy, said binder layer adhering said flexible epoxy layer to said fabric layer and said flexible epoxy resin is (1) derived from an epoxy having the formula ##STR3## wherein n, independently, is a whole number of at least about 25 for at least one of said chains or (2) an admixture of that epoxy resin with up to 10% by weight of a rigid epoxy resin.
Claim 17
Dependent Claim
35 words
A flexible epoxy coated lamina, according to claim 12, and wherein said binder layer and said epoxy layer have an apparent bending modulus according to ASTM D747-86 of from about 20 to about 2,000 psi.
Claim 18
Dependent Claim
52 words
A flexible epoxy coated lamina, according to claim 14, wherein at least 50 percent by weight of said flexible binder resides on the surface of said fabric layer, and wherein said flexible epoxy layer and said flexible binder layer have an apparent bending modulus of from about 30 to about 200 psi.
Claim 19
Dependent Claim
46 words
A flexible epoxy coated lamina, according to claim 15, wherein the amount of said flexible epoxy is from about about 1 to about 50 ounces per square yard and wherein the amount of said binder is from about 0.5 to about 4.0 ounces per square yard.
Claim 20
Dependent Claim
63 words
A flexible epoxy coated lamina, according to claim 16, wherein said n of each epoxy chain independently is from about 30 to about 40, wherein the amount of said flexible epoxy is from about 1 to about 15 ounces per square yard, and wherein at least 70 percent by weight of said flexible epoxy resin resides on the surface of said fabric layer.
Claim 21
Dependent Claim
79 words
A flexible epoxy coated lamina, according to claim 17, wherein the amount of said flexible epoxy is from about 2 to about 6 ounces per square yard, wherein the amount of said flexible binder is from about 1.5 to about 2.5 ounces per square yard, wherein said binder is a polyurethane, an acrylic polymer, a polyvinyl chloride polymer, or combinations thereof, and wherein the apparent bending modulus of said flexible epoxy is from about 80 to about 90 psi.
Claim 22
Dependent Claim
77 words
A flexible epoxy coated lamina, according to claim 13, wherein said epoxy layer is applied to a grained release sheet, wherein said binder layer is subsequently applied to said flexible epoxy layer, wherein said fabric layer is subsequently applied to said binder layer, wherein said flexible epoxy layer is cured by heating the same, and wherein said release sheet is subsequently removed to yield said flexible epoxy coated lamina having a grain on said flexible epoxy surface.
Claim 23
Dependent Claim
77 words
A flexible epoxy coated lamina, according to claim 17, wherein said epoxy layer is applied to a grained release sheet, wherein said binder layer is subsequently applied to said flexible epoxy layer, wherein said fabric layer is subsequently applied to said binder layer, wherein said flexible epoxy layer is cured by heating the same, and wherein said release sheet is subsequently removed to yield said flexible epoxy coated lamina having a grain on said flexible epoxy surface.
Claim 24
Dependent Claim
41 words
A flexible epoxy coated lamina, according to claim 18, wherein said flexible epoxy resin contains up to 10 percent by weight of a rigid epoxy resin based upon the total weight of said rigid epoxy resin and said flexible epoxy resin.
References Cited (Backward Citations)
US3184332A
Cited
US3591400A
Cited
US3934067A
Cited
US4219598A
Cited
US4310593A
Cited
US4329387A
Cited
US4537834A
Cited
US4623574A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-02-12 | 1993-08-14 | 1994-02-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-02-12 | 1997-08-14 | 1998-02-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-02-12 | 2001-08-14 | 2002-02-13 | $7700.00 | Window Closed / Lapsed |