Method for providing centrifugal fiber spinning coupled with pressure extrusion
Assignee: Individual
•
Filing: 1988-07-05
•
Granted: 1990-02-06
•
Expires: 2008-07-05
Abstract
Abstract A method wherein there is provided a source of fiber forming material, with said fiber forming material being pumped into a die having a plurality of spinnerets about its periphery. The die is rotated at a predetermined adjustable speed, whereby the liquid is expelled from the die so as to form fibers. It is preferred that the fiber forming material be cooled as it is leaving the holes in the spinnerets during drawdown. The fibers may be used to produce fabrics, fibrous tow and yarn through appropriate take-up systems. The pumping system provides a pumping action whereby a volumetric quantity of liquid is forced into the rotational system independent of viscosity or the back pressure generated by the spinnerets and the manifold system of the spinning head, thus creating positive displacement feeding. Positive displacement feeding may be accomplished by the extruder alone or with an additional pump of the type generally employed for this purpose. A rotary union is provided for positive sealing purposes during the pressure feeding of the fiber forming material into the rotating die.
Inventors
- 👤 Herbert W. Keuchel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 22:11
CPC Classifications
D; D01; D01D; D01D5/00; D01D5/18
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
112 words
A process for forming fibers comprising supplying a source of molten polymer fiber-forming material; pumping said fiber-forming material from said source to at least one spinneret on a rotatable die, said fiber-forming material being pumped under pressure through a substantially leak-proof closed channel connecting said source to said at least one spinneret on said rotatable die; controlling the extrusion rate of said material through said spinneret by controlling the volumetric quantity of said fiber-forming material being pumped to said at least one spinneret through said channel; and rotating said die during extrusion of said fiber-forming material; whereby said molten polymer fiber-forming material is expelled from said spinnerets so as to produce fibers.
Claim 2
Dependent Claim
112 words
A process for forming fibers comprising supplying a source of molten polymer fiber-forming material; pumping said fiber-forming material from said source to at least one spinneret on a rotatable die, said fiber-forming material being pumped under pressure through a substantially leak-proof closed channel connecting said source to said at least one spinneret on said rotatable die; controlling the extrusion rate of said material through said spinneret by controlling the volumetric quantity of said fiber-forming material being pumped to said at least one spinneret through said channel; and rotating said die during extrusion of said fiber-forming material; whereby said molten polymer fiber-forming material is expelled from said spinnerets so as to produce fibers.
Claim 3
Dependent Claim
18 words
The process of claim 1 further comprising heating said material during passage between said source and said die.
Claim 4
Dependent Claim
16 words
The process of claim 1 further comprising variably controlling the speed of rotation of said die.
Claim 5
Dependent Claim
48 words
The process of claim 1 wherein said fiber-forming material is a material selected from the group consisting of polyolefin polymers and copolymers; thermoplastic polyurethane polymers and copolymers; polyesters such as polyethylene and polybutylene terepthalate; nylons; polyionomers; polyacrylates; polybutadienes and copolymers; hot melt adhesive polymer systems; and reactive polymers.
Claim 6
Dependent Claim
24 words
The process of claim 1 wherein the speed of said die rotation is about 500 revolutions per minute to about 3000 revolutions per minute.
Claim 7
Dependent Claim
112 words
A process for forming an article comprising fibers comprising supplying a source of molten polymer fiber-forming material; pumping said fiber-forming material from said source to a plurality of spinnerets on a rotatable die, said fiber-forming material being pumped under positive pressure through a substantially leak-proof closed channel connecting said source to said plurality of spinnerets on said rotatable die; controlling the extrusion rate of said material through said spinnerets by controlling the volumetric quantity of said fiber-forming material being pumped to said spinnerets through said channel; and rotating said die during extrusion of said fiber-forming material; whereby said molten polymer fiber-forming material is expelled from said spinnerets so as to produce fibers.
Claim 8
Dependent Claim
112 words
A process for forming an article comprising fibers comprising supplying a source of molten polymer fiber-forming material; pumping said fiber-forming material from said source to a plurality of spinnerets on a rotatable die, said fiber-forming material being pumped under positive pressure through a substantially leak-proof closed channel connecting said source to said plurality of spinnerets on said rotatable die; controlling the extrusion rate of said material through said spinnerets by controlling the volumetric quantity of said fiber-forming material being pumped to said spinnerets through said channel; and rotating said die during extrusion of said fiber-forming material; whereby said molten polymer fiber-forming material is expelled from said spinnerets so as to produce fibers.
Claim 9
Dependent Claim
18 words
The process of claim 6 further comprising heating said material during passage between said source and said die.
Claim 10
Dependent Claim
16 words
The process of claim 6 further comprising variably controlling the speed of rotation of said die.
Claim 11
Dependent Claim
48 words
The process of claim 6 wherein said fiber-forming material is a material selected from the group consisting of polyolefin polymers and copolymers; thermoplastic polyurethane polymers and copolymers; polyesters such as polyethylene and polybutylene terepthalate; nylons; polyionomers; polyacrylates; polybutadienes and copolymers; hot melt adhesive polymer systems; and reactive polymers.
Claim 12
Dependent Claim
24 words
The process of claim 6 wherein the speed of said die rotation is about 500 revolutions per minute to about 3000 revolutions per minute.
Claim 13
Dependent Claim
12 words
The process of claim 6 further comprising forming a fabric from fibers.
Claim 14
Dependent Claim
13 words
The process of claim 6 further comprising forming a yarn from said fibers.
Claim 15
Dependent Claim
18 words
The process of claim 6 further comprising bonding said fibers on a plate extending coaxially about said die.
Claim 16
Dependent Claim
21 words
The process of claim 13 further comprising directing air under pressure outwardly of the perimeter of said die toward said plate.
Claim 17
Dependent Claim
21 words
The process of claim 6 further comprising bonding said fibers on a perforated surface so as to produce a non-woven fabric.
Claim 18
Dependent Claim
17 words
The process of claim 6 further comprising bonding said fibers on the outside surface of a mandrel.
Claim 19
Dependent Claim
15 words
The process of claim 6 wherein said mandrel has the shape of an inverted bucket.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-02-05 | 1993-08-07 | 1994-02-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-02-05 | 1997-08-07 | 1998-02-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-02-05 | 2001-08-07 | 2002-02-06 | $7700.00 | Window Closed / Lapsed |