Method of forming silicone film
Assignee: Tokyo Ohka Kogyo Co Ltd
•
Filing: 1988-11-16
•
Granted: 1990-01-16
•
Expires: 2008-11-16
Abstract
Abstract A silicone film is formed by drying a solution coated on a substrate at a temperature below 150° C. to form a silicone film on the substrate, treating the silicone film in an oxygen plasma, and heating the silicone film treated in the plasma at a temperature of 150° C. or higher.
Inventors
- 👤 Muneo Nakayama
- 👤 Akira Hashimoto
- 👤 Toshihiro Nishimura
- 👤 Akira Uehara
- 👤 Isamu Hijikata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 05:11
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/12; C08J7/123; B; B05; B05D; B05D3/00; B05D3/14; B05D3/141; B05D3/145; B29; B29C; B29C59/00; B29C59/14; C09; C09D; C09D183/00; C09D183/04; G; G02; G02F; G02F1/00; G02F1/01; G02F1/13; G02F1/133; G02F1/1333; G02F1/1337; G02F1/133711; B05D2518/00; B05D2518/10; B05D3/02; C08J2383/00; C08J2383/04; H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6326; H10P14/6342; H10P14/65; H10P14/6516; H10P14/6529; H10P14/6532; H10P14/66; H10P14/668; H10P14/6681; H10P14/6684; H10P14/6686
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
74 words
A method of forming a silicone film, comprising the steps of: (a) coating a solution for forming a silicone film on a substrate and drying the coated solution at a temperature below 150° C. to form a silicone film on the substrate; (b) treating the silicone film in a plasma produced from a gas mainly composed of oxygen; and (c) heating the plasma treated silicone film at a temperature of at least 150° C.
Claim 2
Independent Claim
74 words
A method of forming a silicone film, comprising the steps of: (a) coating a solution for forming a silicone film on a substrate and drying the coated solution at a temperature below 150° C. to form a silicone film on the substrate; (b) treating the silicone film in a plasma produced from a gas mainly composed of oxygen; and (c) heating the plasma treated silicone film at a temperature of at least 150° C.
Claim 3
Dependent Claim
42 words
A method according to claim 1, wherein said solution for forming a silicone film comprises an organosilanol solution prepared by dissolving at least one of organoalkoxysilane and organohalidesilane into an organic solvent and adding water to the solution to hydrolyze the latter.
Claim 4
Dependent Claim
22 words
A method according to claim 2, wherein said organosilanol solution is prepared by dissolving a hydrolyzate of organoalkoxysilane in an organic solvent.
Claim 5
Dependent Claim
16 words
A method according to claim 3, wherein said organoalkoxysilane comprises a mixture of monomethyltrimethoxysilane and tetramethoxysilane.
Claim 6
Dependent Claim
24 words
A method according to claim 4, wherein said mixture comprises a ratio of 1 mole of monomethyltrimethoxysilane to 0.5 through 5 moles of tetramethoxysilane.
Claim 7
Dependent Claim
21 words
A method according to claim 1, wherein said gas mainly composed of oxygen contains at least 80% by volume of oxygen.
Claim 8
Dependent Claim
25 words
A method according to claim 1, wherein said silicone film is treated in the plasma at a temperature ranging from 50° C. to 200° C.
Claim 9
Dependent Claim
22 words
A method according to claim 1, wherein said plasma treated silicone film is heated at a temperature of at least 300° C.
Claim 10
Dependent Claim
31 words
A method according to claim 1, wherein said silicone film is treated in the plasma by an induction-type plasma reaction treatment apparatus having a plasma generator and a reaction treatment assembly.
Claim 11
Dependent Claim
35 words
A method according to claim 9, wherein said reaction treatment assembly has a table for placing said substrate thereon and a plurality of evacuating discharge holes positioned near an outer circumferential surface of said table.
Claim 12
Dependent Claim
26 words
A method according to claim 10, wherein said discharge holes confront said outer circumferential surface of said table and are equally angularly spaced around said table.
Claim 13
Dependent Claim
28 words
A method according to claim 9, wherein said induction-type plasma reaction treatment apparatus is of a single-substrate type for treating one substrate at a time in the plasma.
Claim 14
Dependent Claim
20 words
A method according to claim 9, wherein said plasma generator is disposed upwardly of and near said reaction treatment assembly.
Claim 15
Dependent Claim
24 words
A method according to claim 9, wherein said plasma generator is in the shape of a bell jar and positioned directly above said substrate.
Claim 16
Dependent Claim
30 words
A method according to claim 9, wherein said plasma generator comprises a chamber member defining a plasma generating space therein and a pair of electrodes disposed around said chamber member.
Claim 17
Dependent Claim
26 words
A method according to claim 15, wherein one of said electrodes is connected to a high-frequency power supply and the other electrode is connected to ground.
Claim 18
Dependent Claim
153 words
A method according to claim 1, wherein said silicone film is treated in the plasma by an induction-type plasma reaction treatment apparatus; said plasma reaction treatment apparatus having a plasma generator and a reaction treatment assembly; said plasma generator comprising a first, bell-jar shaped enclosure member defining a plasma generating space therein and a pair of electrodes disposed around said first enclosure member and confronting each other, one of said electrodes being connected to a high-frequency power supply and the other electrode to ground; and said reaction treatment assembly comprising a second enclosure member defining therein a reaction treatment space communicating with and positioned downwardly of said plasma generating space, a support member for supporting and setting said substrate in said reaction treatment space to position said substrate directly below said plasma generating space, and evacuating discharge holes positioned near an outer circumferential edge of said substrate set in said reaction treatment space.
Claim 19
Dependent Claim
68 words
A method according to claim 1, wherein said silicone film is treated in the plasma by an induction-type plasma reaction treatment apparatus; said plasma reaction treatment apparatus having a plasma generator and a reaction treatment assembly; and said plasma generator comprising an enclosure member and a plurality of electrodes disposed outside and inside, respectively, of said enclosure member and defining a plasma generating space in said enclosure member.
Claim 20
Dependent Claim
38 words
A method according to claim 18, wherein said electrodes include an outer electrode fitted over said enclosure chamber and connected to a high-frequency power supply and an inner electrode disposed in said enclosure chamber and connected to ground.
Claim 21
Dependent Claim
35 words
A method according to claim 9, wherein said plasma generator and said reaction treatment assembly together provide an enclosed space for containing said substrate having said silicone film coated thereon during the plasma treatment step.
Claim 22
Dependent Claim
31 words
A method according to claim 9, wherein said plasma generator includes an upper portion of a chamber member and said reaction treatment assembly includes a lower portion of the chamber member.
Claim 23
Dependent Claim
23 words
A method according to claim 10, wherein said plurality of evacuating discharge holes are positioned lower than an upper surface of said table.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-01-15 | 1993-07-17 | 1994-01-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-01-15 | 1997-07-17 | 1998-01-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-01-15 | 2001-07-17 | 2002-01-16 | $7700.00 | Window Closed / Lapsed |