Powder particles for fine-grained hard material alloys
Assignee: Santrade Ltd
•
Filing: 1988-02-25
•
Granted: 1990-01-16
•
Expires: 2008-02-25
Abstract
Abstract The present invention relates to powder particles consisting of hard principles and binder metal for the manufacture of superior, uniquely fine-grained hard material alloys and to a procedure for the preparation of said particles. The preparation is performed in an economical way because the procedure starts from conventional melt metallurgical raw materials. A pre-alloy consisting of hard principle forming and binder phase forming elements is subjected to a heat treatment such as nitriding and carburizing after being crushed. The final product is particles composed by hard principle phases and binder metal phases formed "in situ" in an effective binding.
Inventors
- 👤 Carl S. G. Ekemar
- 👤 Rolf G. Oskarsson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 05:04
CPC Classifications
B; B22; B22F; B22F9/00; B22F9/02; B22F9/04; B22F2009/041
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
167 words
Powder particles for the preparation of a fine-grained hard material alloy for cutting tools consisting essentially of hard principles and binder metal with greater contents of hard principles than in high speed steel, in which the hard principles are compounds of one or more elements in the groups IVA, VA and VIA of the periodical system and Si with C, N and/or B, and the binder metal being based upon Fe, Co and/or Ni, characterized in that the hard principles are formed in situ, the particle is composed of binder metal alloy in an effective binding with the fine-grained hard principles, the volume fraction of hard principles in the particles is 35-90 percent by volume and where Si, Ti, Zr, Hf, V, Nb and/or Ta are ≧55 atomic percent of the hard principle forming metals, balance being Cr, Mo and/or W, and the mean size of the particles is 1-16 μm and at the most 5% of the number of particles have a size of >30 μm.
Claim 2
Dependent Claim
167 words
Powder particles for the preparation of a fine-grained hard material alloy for cutting tools consisting essentially of hard principles and binder metal with greater contents of hard principles than in high speed steel, in which the hard principles are compounds of one or more elements in the groups IVA, VA and VIA of the periodical system and Si with C, N and/or B, and the binder metal being based upon Fe, Co and/or Ni, characterized in that the hard principles are formed in situ, the particle is composed of binder metal alloy in an effective binding with the fine-grained hard principles, the volume fraction of hard principles in the particles is 35-90 percent by volume and where Si, Ti, Zr, Hf, V, Nb and/or Ta are ≧55 atomic percent of the hard principle forming metals, balance being Cr, Mo and/or W, and the mean size of the particles is 1-16 μm and at the most 5% of the number of particles have a size of >30 μm.
Claim 3
Dependent Claim
33 words
Powder particles according to claim 1, characterized in that the C, N and/or B in the hard principles of the particles is replaced by O in an amount up to 20 atomic percent.
Claim 4
Dependent Claim
37 words
Power particles according to claim 1, characterized in that the hard principles consist of grains having a mean grain size of 0.02-0.80 μm of which at the most 5% of the number of grains are >1.5 μm.
Claim 5
Dependent Claim
36 words
Powder particles according to claim 1, characterized in that the binder metal alloy contains at the most 15 atomic percent Mn, at the most 10 atomic percent Al and at the most 1 atomic percent Cu.
Claim 6
Dependent Claim
22 words
Powder particles according to claim 1, characterized in that the fraction of hard principles in the particles is 35-70 percent by volume.
Claim 7
Dependent Claim
18 words
Powder particles according to claim 1, characterized in that the mean grain size of the particles is 2-8μm.
Claim 8
Dependent Claim
19 words
Powder particles according to claim 3, characterized in that the mean grain size of the grains is 0.03-0.60 μm.
Claim 9
Dependent Claim
30 words
Powder particles according to claim 5, characterized in that the binder metal alloy contains at the most 12 atomic percent Mn, 8 atomic percent Al and 0.8 atomic percent Cu.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-01-15 | 1993-07-17 | 1994-01-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-01-15 | 1997-07-17 | 1998-01-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-01-15 | 2001-07-17 | 2002-01-16 | $7700.00 | Window Closed / Lapsed |