Preparation of amorphous metal core for use in transformer
Assignee: ABB Inc USA
•
Filing: 1987-07-30
•
Granted: 1990-01-09
•
Expires: 2007-07-30
Abstract
Abstract Disclosed is a method of preparing an amorphous metal core 1 for use in a transformer. The uncut legs 7, 8 and 9 of the core 1 are covered with an adhesive impregnated substrate 10, the edges 11 of which are bent over to make contact with the core 1. A release sheet 12 and a plate 13 are placed over the adhesive impregnated substrate, the plate 13 is pressed against the core 1, and the adhesive is cured. The process is repeated with the edges on the opposite side of the core.
Inventors
- 👤 Terrence E. Chenoweth
- 👤 Eugenius S. Hammack
- 👤 Wallace L. McDonald
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 12:50
CPC Classifications
H; H01; H01F; H01F27/00; H01F27/24; H01F27/25; B; B29; B29C; B29C63/00; B29C63/0017; B29C63/0021; B29C70/00; B29C70/04; B29C70/28; B29C70/30; B29C70/34; B29C70/345; B29C70/68; B29C70/86; B29C70/865; H01F41/00; H01F41/02; H01F41/0206; H01F41/0213; H01F41/0226; B29C35/00; B29C35/02; B29C35/08; B29C35/0805; B29C2035/0827; B29C33/00; B29C33/56; B29C33/68; Y; Y10; Y10S; Y10S428/00; Y10S428/906; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T428/00; Y10T428/24; Y10T428/2419
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
65 words
An amorphous metal core having an adhesive impregnated substrate of woven cloth or matted material selected from the group consisting of glass, polyesters, polyimides, polyamides and mixture thereof that is impregnated with a curable adhesive comprising a thixotrope bonded to at least a portion of each edge, where said substrate extends beyond said edge, is bent over said edge, and is bonded to said core.
Claim 2
Dependent Claim
65 words
An amorphous metal core having an adhesive impregnated substrate of woven cloth or matted material selected from the group consisting of glass, polyesters, polyimides, polyamides and mixture thereof that is impregnated with a curable adhesive comprising a thixotrope bonded to at least a portion of each edge, where said substrate extends beyond said edge, is bent over said edge, and is bonded to said core.
Claim 3
Dependent Claim
18 words
A core according to claim 1 wherein said substrate is glass cloth and said adhesive is UV cured.
Claim 4
Dependent Claim
31 words
A core according to claim 1 wherein said one leg of said core is cut and said substrate covers all edges of said core except the edges of said cut leg.
Claim 5
Dependent Claim
20 words
A core according to claim 1 wherein said adhesive contains about 4 to about 6% by weight of a thixotrope.
Claim 6
Independent Claim
112 words
A method of preparing an annealed amorphous metal core for use in a transformer comprising: (A) covering at least portions of the edges of said core with an insulating substrate of woven cloth or matted material selected from the group consisting of glass, polyesters, polyimides, polyamides and mixtures thereof that is impregnated with a curable adhesive comprising a thixotrope, said substrate extending beyond said edges; (B) bending the portions of said substrate that extend beyond said edges over said edges and into contact with said core; (C) placing a plate over the portion of said substrate that covers said edges and pressing said plate against said core; and (D) curing said adhesive.
Claim 7
Independent Claim
112 words
A method of preparing an annealed amorphous metal core for use in a transformer comprising: (A) covering at least portions of the edges of said core with an insulating substrate of woven cloth or matted material selected from the group consisting of glass, polyesters, polyimides, polyamides and mixtures thereof that is impregnated with a curable adhesive comprising a thixotrope, said substrate extending beyond said edges; (B) bending the portions of said substrate that extend beyond said edges over said edges and into contact with said core; (C) placing a plate over the portion of said substrate that covers said edges and pressing said plate against said core; and (D) curing said adhesive.
Claim 8
Dependent Claim
25 words
A method according to claim 5 wherein a release sheet and a layer of a foamed sheet are placed between said plate and said substrate.
Claim 9
Dependent Claim
18 words
A method according to claim 6 wherein said release sheet and said foamed sheet are polyethylene or polypropylene.
Claim 10
Dependent Claim
29 words
A method according to claim 5 wherein said adhesive is UV curable, said plate is UV transparent, and said adhesive is cured by passing UV light through said plate.
Claim 11
Dependent Claim
26 words
A method according to claim 8 wherein said adhesive includes about 4 to about 6 percent by weight (based on total adhesive weight) of a thixotrope.
Claim 12
Dependent Claim
26 words
A method according to claim 9 wherein said thixotrope is selected from the group consisting of fumed silica, mica flakes, milled glass fibers, and mixtures thereof.
Claim 13
Dependent Claim
13 words
A method according to claim 5 wherein said substrate is woven glass cloth.
Claim 14
Dependent Claim
42 words
A method according to claim 5 wherein said core is placed in a horizontal position with an exposed edge of said amorphous metal core facing upward prior to said method and is inverted for application of said method to the opposite side.
Claim 15
Independent Claim
163 words
A method of preparing an annealed rectangular wound amorphous metal core having one unit leg for use in a transformer comprising: (A) placing said core in a horizontal position with one edge of said amorphous metal core facing upward; (B) covering uncut legs of said core with a woven glass cloth impregnated with a UV curable adhesive containing about 4 to about 6 percent by weight (based on total adhesive weight) of fumed silica, where said cloth extends beyond said edge of said core by about 0.25 to about 1 inch; (C) bending the portions of said cloth that extend beyond said edges of said core 90 degrees downward and pressing said portions against said core; (D) placing a release sheet over said cloth; (E) placing a UV transparent plate over said release sheet and pressing said plate against said core; and (F) passing UV light through said plate to cure said adhesive; (G) inverting said core and repeating steps (A) through (F).
Claim 16
Independent Claim
163 words
A method of preparing an annealed rectangular wound amorphous metal core having one unit leg for use in a transformer comprising: (A) placing said core in a horizontal position with one edge of said amorphous metal core facing upward; (B) covering uncut legs of said core with a woven glass cloth impregnated with a UV curable adhesive containing about 4 to about 6 percent by weight (based on total adhesive weight) of fumed silica, where said cloth extends beyond said edge of said core by about 0.25 to about 1 inch; (C) bending the portions of said cloth that extend beyond said edges of said core 90 degrees downward and pressing said portions against said core; (D) placing a release sheet over said cloth; (E) placing a UV transparent plate over said release sheet and pressing said plate against said core; and (F) passing UV light through said plate to cure said adhesive; (G) inverting said core and repeating steps (A) through (F).
Claim 17
Dependent Claim
15 words
A method according to claim 13 wherein said release sheet is a film of polyethylene.
References Cited (Backward Citations)
US4239572A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-01-08 | 1993-07-10 | 1994-01-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-01-08 | 1997-07-10 | 1998-01-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-01-08 | 2001-07-10 | 2002-01-09 | $7700.00 | Window Closed / Lapsed |