Silicon nitride-ceramic and a manufacturing method therof
Assignee: Toshiba Corp
•
Filing: 1988-02-05
•
Granted: 1989-12-12
•
Expires: 2008-02-05
Abstract
Abstract A silicon nitride-ceramic is composed of a sintered body including silicon nitride and an additive, and has a columnar crystal of β type silicon nitride substantially parallel to one plane. A method for manufacturing a silicon nitride-ceramic comprises the steps of forming first powder including a needle-shaped crystal of β type silicon nitride by mixing the needle-shaped crystal of the β type silicon nitride with second silicon nitride powder mainly of α type including an additive, or by heating the second silicon nitride powder at temperature 1500° to 1750 ° C. in advance; and sintering the first powder at a predetermined temperature under non-oxidation atmosphere.
Inventors
- 👤 Yasuhiro Goto
- 👤 Takeyuki Yonezawa
- 👤 Yoshiyuki Ohnuma
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 16:19
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/593
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
100 words
A silicon nitride-ceramic composed of a sintered body including silicon nitride and 0.1 to 15 weight % of at least one additive, said ceramic having columnar crystals of β type silicon nitride oriented substantially in parallel to one plane, the ratio (I 101 /I 210 ) of intensity (I 101 ) of plane (101) of the β type silicon nitride to intensity (I 210 ) of plane (210), determined by x-ray diffraction, being less than 0.4 with respect to the plane in which the columnar crystals are oriented, to improve mechanical properties of the ceramic with respect to said plane.
Claim 2
Dependent Claim
100 words
A silicon nitride-ceramic composed of a sintered body including silicon nitride and 0.1 to 15 weight % of at least one additive, said ceramic having columnar crystals of β type silicon nitride oriented substantially in parallel to one plane, the ratio (I 101 /I 210 ) of intensity (I 101 ) of plane (101) of the β type silicon nitride to intensity (I 210 ) of plane (210), determined by x-ray diffraction, being less than 0.4 with respect to the plane in which the columnar crystals are oriented, to improve mechanical properties of the ceramic with respect to said plane.
Claim 3
Dependent Claim
38 words
A silicon nitride-ceramic as claimed in claim 1, wherein said additive is at least one material selected from the group consisting of rare earth oxides, alumina, magnesia, aluminum nitride, iron oxide, titanium oxide, zirconium oxide and molybdenum carbide.
Claim 4
Independent Claim
141 words
A method for manufacturing a silicon nitride-ceramic, comprising the steps of: forming a raw material of mainly α type silicon nitride including 0.1 to 15 weight % of at least one additive and 5-50 weight % of needle-shaped crystals of β type silicon nitride; and sintering the raw material at a temperature of approximately 1650° to 1850° C. to orient the β type silicon nitride approximately in parallel to one plane so that the ratio (I 101 /I 210 ) of intensity (I 101 ) of plane (101) of the β type silicon nitride to intensity (I 210 ) of plane (210) thereof, determined by x-ray diffraction, is less than 0.4 with respect to the plane in which the needle-shaped crystals of the β type silicon nitride are oriented, thereby improving mechanical properties of the ceramic with respect to said plane.
Claim 5
Independent Claim
141 words
A method for manufacturing a silicon nitride-ceramic, comprising the steps of: forming a raw material of mainly α type silicon nitride including 0.1 to 15 weight % of at least one additive and 5-50 weight % of needle-shaped crystals of β type silicon nitride; and sintering the raw material at a temperature of approximately 1650° to 1850° C. to orient the β type silicon nitride approximately in parallel to one plane so that the ratio (I 101 /I 210 ) of intensity (I 101 ) of plane (101) of the β type silicon nitride to intensity (I 210 ) of plane (210) thereof, determined by x-ray diffraction, is less than 0.4 with respect to the plane in which the needle-shaped crystals of the β type silicon nitride are oriented, thereby improving mechanical properties of the ceramic with respect to said plane.
Claim 6
Dependent Claim
20 words
A manufacturing method as claimed in claim 3, wherein the orienting and sintering steps are simultaneously performed by hot pressing.
Claim 7
Dependent Claim
24 words
A manufacturing method as claimed in claim 3, wherein the orienting step is performed by one of injection molding, extrusion molding and slip casting.
Claim 8
Dependent Claim
33 words
A manufacturing method as claimed in claim 3, wherein said additive selected from the group consisting of rare earth oxides, alumina, magnesia, aluminum nitride, iron oxide, titanium oxide, zirconium oxide and molybdenum carbide.
Claim 9
Dependent Claim
32 words
A manufacturing method according to claim 3, wherein said raw material is obtained by heating the α type silicon nitride powder including said additive at a temperature from 1500° to 1750° C.
References Cited (Backward Citations)
US3442997A
Cited
US3432295A
Cited
SU380615A1
Cited
JPS55116671A
Cited
JPS5888171A
Cited
US4563433A
Cited
US4696710A
Cited
JPS6191065A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-12-11 | 1993-06-12 | 1993-12-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-12-11 | 1997-06-12 | 1997-12-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-12-11 | 2001-06-12 | 2001-12-12 | $7700.00 | Window Closed / Lapsed |