Strippable coating film and coating method using same
Assignee: Mitsui Toatsu Chemicals Inc
•
Filing: 1985-10-26
•
Granted: 1989-12-12
•
Expires: 2005-10-26
Abstract
Abstract This invention relates to a strippable coating film for use as a masking material serving to create attractively finished boundaries, for example, in multi-color painting of automobiles and the like, as well as a coating method using such a coating film. A coating film containing 1 to 20 parts by weight of carbon black per 100 parts by weight of the resin component present therein is suitable. Especially preferred is a coating film formed of an acrylic emulsion paint and having an adhesion to the substrate of 20 to 1000 g/inch as expressed in terms of 180° peeling strength. It is disclosed that, by equipping a YAG laser with a Q-switching oscillator unit and operating the Q-switch at a pulse repetition frequency of 0.5 to 30 kHz, the coating film can be cleanly cut to achieve an attractive finish in multi-color painting. Alternatively, a two-layer coating film containing the above-defined amount of carbon black may be formed by applying a coating material having adhesive power to a substrate to form an undercoating layer in contact with the substrate and then applying a coating material having flexibility and exhibiting film-forming properties to the undercoating layer to form an overcoating surface layer. This two-layer coating film is more effective than the single-layer coating film in preventing the substrate from being damaged.
Inventors
- 👤 Keiichi Kamada
- 👤 Motoyuki Torikai
- 👤 Yasuo Ohkita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 13:03
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/20; B; B05; B05D; B05D1/00; B05D1/32; B05D1/322; B05D1/325; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/28; Y10T428/31504; Y10T428/31826; Y10T428/31833; Y10T428/31855; Y10T428/31909; Y10T428/31928; Y10T428/31935
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
77 words
A strippable coating film containing 1 to °parts by weight of carbon black per 100 parts by weight of a resin component comprising 25 to 40 parts by weight of acrylonitrile, 65 to 40 parts by weight of butyl acrylate, and 0.5 to 10 parts by weight of (meth)acrylic acid present therein, wherein the adhesion of the film to an object to be coated is 20 to 1000 g/inch as expressed in terms of 180° peeling strength.
Claim 2
Dependent Claim
77 words
A strippable coating film containing 1 to °parts by weight of carbon black per 100 parts by weight of a resin component comprising 25 to 40 parts by weight of acrylonitrile, 65 to 40 parts by weight of butyl acrylate, and 0.5 to 10 parts by weight of (meth)acrylic acid present therein, wherein the adhesion of the film to an object to be coated is 20 to 1000 g/inch as expressed in terms of 180° peeling strength.
Claim 3
Dependent Claim
26 words
A strippable coating film as claimed in claim 1 wherein the carbon black is furnace black, lamp black, thermal black, acetylene black or German furnace black.
Claim 4
Dependent Claim
147 words
A strippable coating film comprising two layers of resin coating materials, wherein the undercoating layer in contact with the object to be coated contains therein 1 to 20 parts by weight (based on the resin component) of carbon black and has adhesive power, wherein the resin component of the undercoating layer is an acrylic and its adhesion to the substrate is 20 to 1000 g/inch as expressed in terms of 180° peeling strength, wherein the overcoating layer located on the surface side contains therein 1 to 20 parts by weight (based on the resin component) of carbon black wherein said layer is flexible and does not exhibit surface tack and and wherein the resin component of the overcoating layer comprises 25 to 40 parts by weight of acrylonitrile, 64 to 40 parts by weight of butyl acrylate, and 0.5 to 10 parts by weight of (meth)acrylic acid.
Claim 5
Dependent Claim
147 words
A strippable coating film comprising two layers of resin coating materials, wherein the undercoating layer in contact with the object to be coated contains therein 1 to 20 parts by weight (based on the resin component) of carbon black and has adhesive power, wherein the resin component of the undercoating layer is an acrylic and its adhesion to the substrate is 20 to 1000 g/inch as expressed in terms of 180° peeling strength, wherein the overcoating layer located on the surface side contains therein 1 to 20 parts by weight (based on the resin component) of carbon black wherein said layer is flexible and does not exhibit surface tack and and wherein the resin component of the overcoating layer comprises 25 to 40 parts by weight of acrylonitrile, 64 to 40 parts by weight of butyl acrylate, and 0.5 to 10 parts by weight of (meth)acrylic acid.
Claim 6
Dependent Claim
51 words
A strippable coating film as claimed in claim 3 wherein either the undercoating layer or the overcoating layer contains an inorganic filler having an average particle diameter of 0.1 to 10 μ in an amount of 5 to 50 parts by weight per 100 parts by weight of the resin component.
Claim 7
Dependent Claim
35 words
A strippable coating film as claimed in claim 3 wherein the undercoating layer contains aluminum powder in an amount of 1 to 40 parts by weight per 100 parts by weight of the resin component.
Claim 8
Dependent Claim
231 words
A coating method for creating attractively finished boundaries which comprises applying a coating material containing 1 to 20% by weight (based on the resin component) of carbon black in the dry film and having adhesive power to an object to be coated wherein the adhesion of the object to be coated is 20-1000 g/inch as expressed in terms of 180° peeling strength, and thereby forming an undercoating layer, the resin component of which is an acrylic resin, in contact with the object to be coated; applying a coating material containing 1 to 20% by weight (based on the resin component) of carbon black in the dry film, having flexibility and exhibiting film-forming properties to the undercoating layer and thereby forming a surface layer, the resin component of which comprises 25 to 40 parts by weight of acrylonitrile, 65 to 40 parts by weight of butyl acrylate, and 0.5 to 10 parts by weight of (meth)acrylic acid, to produce a strippable coating film composed of two layers both containing carbon black; cutting only the surface layer of the coating film with a laser beam from a YAG laser; stripping off the unnecessary portions of the laser-cut surface layer together with the underlying adhesive layer; applying a final coat of paint to the parts from which the coating film has been removed; and stripping off the remaining portions of the strippable coating film.
Claim 9
Dependent Claim
231 words
A coating method for creating attractively finished boundaries which comprises applying a coating material containing 1 to 20% by weight (based on the resin component) of carbon black in the dry film and having adhesive power to an object to be coated wherein the adhesion of the object to be coated is 20-1000 g/inch as expressed in terms of 180° peeling strength, and thereby forming an undercoating layer, the resin component of which is an acrylic resin, in contact with the object to be coated; applying a coating material containing 1 to 20% by weight (based on the resin component) of carbon black in the dry film, having flexibility and exhibiting film-forming properties to the undercoating layer and thereby forming a surface layer, the resin component of which comprises 25 to 40 parts by weight of acrylonitrile, 65 to 40 parts by weight of butyl acrylate, and 0.5 to 10 parts by weight of (meth)acrylic acid, to produce a strippable coating film composed of two layers both containing carbon black; cutting only the surface layer of the coating film with a laser beam from a YAG laser; stripping off the unnecessary portions of the laser-cut surface layer together with the underlying adhesive layer; applying a final coat of paint to the parts from which the coating film has been removed; and stripping off the remaining portions of the strippable coating film.
Claim 10
Dependent Claim
27 words
A method as claimed in claim 6, wherein the YAG laser is equipped with a pulse repetition frequency in the range of 500 Hz to 10 kHz.
References Cited (Backward Citations)
BE688494A
Cited
US4217379A
Cited
US4201799A
Cited
US4245003A
Cited
US4358482A
Cited
US4578281A
Cited
US4598127A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-12-11 | 1993-06-12 | 1993-12-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-12-11 | 1997-06-12 | 1997-12-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-12-11 | 2001-06-12 | 2001-12-12 | $7700.00 | Window Closed / Lapsed |