US4884476A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for the preparation of a diamond-clad machining tool
Assignee: Asahi Diamond Industrial Co Ltd
•
Filing: 1988-06-13
•
Granted: 1989-12-05
•
Expires: 2008-06-13
Abstract
Abstract A diamond-clad machining tool is prepared by the steps of (a) forming a film of diamond of 10 to 1000 μm thickness by the method of vapor-phase deposition on the surface of a temporary substrate of, e.g., silicon, (b) bonding the diamond film as borne by the temporary substrate to the surface of a base body of the tool by brazing and (c) removing the temporary substrate, e.g., by grinding to leave the diamond film bonded to the base body of the tool by brazing. The method is advantageous in the versatility in respect of the material of substrate on which a diamond film is deposited from the vapor phase as well as in the firmness of bonding between the cladding layer and the base body of the tool in comparison with the conventional vapor-phase deposition method of diamond directly to the surface of the base body of a tool.
Inventors
- 👤 Fuminori Okuzumi
- 👤 Junichi Matsuda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 12:02
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/26; C23C16/27; C23C16/272; B; B23; B23B; B23B27/00; B23B27/14; B23B27/141; B23B27/145; B23P; B23P5/00; C23C16/01; B23B2226/00; B23B2226/31; B23B2228/00; B23B2228/08; B23B2240/00; B23B2240/08; Y; Y10; Y10S; Y10S76/00; Y10S76/12; Y10T; Y10T407/00; Y10T407/26
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
115 words
A method for the preparation of a machine tool having a cladding layer of diamond formed by the method of vapor-phase deposition which comprises the steps of: (a) forming a film of diamond having a thickness of from 10 to 1000 μm by vapor-phase deposition on the surface of a temporary substrate; (b) bonding the film of diamond as borne by the temporary substrate by brazing the surface of the diamond film with a brazing material to the surface of a base body of a machine tool; and (c) removing the temporary substrate from the film of diamond bonded to the surface of the base body of the machine tool with a brazing layer therebetween.
Claim 2
Independent Claim
115 words
A method for the preparation of a machine tool having a cladding layer of diamond formed by the method of vapor-phase deposition which comprises the steps of: (a) forming a film of diamond having a thickness of from 10 to 1000 μm by vapor-phase deposition on the surface of a temporary substrate; (b) bonding the film of diamond as borne by the temporary substrate by brazing the surface of the diamond film with a brazing material to the surface of a base body of a machine tool; and (c) removing the temporary substrate from the film of diamond bonded to the surface of the base body of the machine tool with a brazing layer therebetween.
Claim 3
Dependent Claim
37 words
The method for the preparation of a machine tool having a cladding layer of diamond as claimed in claim 1 wherein said temporary substrate comprises a material selected from the group consisting of silicon, molybdenum and tungsten.
Claim 4
Dependent Claim
41 words
The method for the preparation of a machine tool having a cladding layer of diamond as claimed in claim 1 wherein said brazing material is selected from the group consisting of titanium-copper-silver base alloys, coppernickel-titanium base alloys and silver-copper-palladium base alloys.
Claim 5
Dependent Claim
47 words
The method for the preparation of a machine tool having a cladding layer of diamond as claimed in claim 1 wherein said cladding layer of diamond is formed by the method of plasma-induced chemical vapor-phase deposition in an atmosphere of a gaseous mixture of methane and hydrogen.
Claim 6
Dependent Claim
49 words
The method for the preparation of a machine tool having a cladding layer of diamond as claimed in claim 3 wherein said base body comprises a metallic base body or a cemented carbide base body and said film of diamond has a thickness of from 30 to 150 μm.
Claim 7
Dependent Claim
47 words
The method for the preparation of a machine tool having a cladding layer of diamond as claimed in claim 5 wherein said cladding layer of diamond is formed by the method of plasma-induced chemical vapor-phase deposition in an atmosphere of a gaseous mixture of methane and hydrogen.
Claim 8
Dependent Claim
54 words
The method for the preparation of a machine tool having a cladding layer of diamond as claimed in claim 6 wherein said temporary substrate consists essentially of a material selected from the group consisting of silicon, molybdenum and tungsten and said cladding layer of diamond has a thickness of from 30 to 150 μm.
Claim 9
Dependent Claim
27 words
The method for the preparation of a machine tool having a cladding layer of diamond as claimed in claim 7 wherein said temporary substrate consists of silicon.
Claim 10
Dependent Claim
59 words
The method for the preparation of a machine tool having a cladding layer of diamond as claimed in claim 1 wherein said base body of a machine tool is a ceramic material; said brazing material is a titanium-copper-silver base alloy and said temporary substrate consists essentially of a material selected from the group consisting of silicon, molybdenum and tungsten.
Claim 11
Dependent Claim
42 words
The method for the preparation of a machine tool having a cladding layer of diamond as claimed in claim 9 wherein said temporary substrate consists of silicon and said cladding layer of diamond has a thickness of from 30 to 150 μm.
Claim 12
Dependent Claim
119 words
A machine tool having a cladding layer of diamond which integrally comprises: (a) a base body of a machine tool; (b) a cladding layer consisting of diamond having a thickness of from 10 to 1000 μm which was formed by vapor deposition; (c) a layer of brazing material positioned between the surface of the base body of the machine tool and said cladding layer of diamond and bonding the base body surface and the diamond cladding layer together, said cladding layer consisting of diamond which was formed by vapor deposition on a temporary substrate which was removed from said diamond cladding layer after said diamond cladding layer was bonded to said base body by said layer of brazing material.
Claim 13
Dependent Claim
119 words
A machine tool having a cladding layer of diamond which integrally comprises: (a) a base body of a machine tool; (b) a cladding layer consisting of diamond having a thickness of from 10 to 1000 μm which was formed by vapor deposition; (c) a layer of brazing material positioned between the surface of the base body of the machine tool and said cladding layer of diamond and bonding the base body surface and the diamond cladding layer together, said cladding layer consisting of diamond which was formed by vapor deposition on a temporary substrate which was removed from said diamond cladding layer after said diamond cladding layer was bonded to said base body by said layer of brazing material.
Claim 14
Dependent Claim
35 words
The machine tool having a cladding layer of diamond as claimed in claim 11 wherein the brazing material is selected from the group consisting of titanium-copper-silver base alloys, copper-nickel-titanium base alloys and silver-copper-palladium base alloys.
Claim 15
Dependent Claim
29 words
The machine tool having a cladding layer of diamond as claimed in claim 11 wherein said cladding layer of diamond has a thickness of from 30 to 150 μm.
Claim 16
Dependent Claim
37 words
The machine tool having a cladding layer of diamond as claimed in claim 12 wherein said base body comprises a metal or cemented carbide and wherein said cladding layer has thickness of from 30 to 150 μm.
Claim 17
Dependent Claim
42 words
The machine tool having a cladding layer of diamond as claimed in claim 11 wherein said base body is a ceramic, said brazing material is a titanium-copper-silver base alloy and said cladding layer has a thickness of from 30 to 150 μm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-12-04 | 1993-06-05 | 1993-12-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-12-04 | 1997-06-05 | 1997-12-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-12-04 | 2001-06-05 | 2001-12-05 | $7700.00 | Window Closed / Lapsed |