Soluble acrylate copolymer containing carboxyl groups, processes for its preparation and coating agents based on the acrylate copolymer
Assignee: BASF Farben und Fasern AG
•
Filing: 1989-03-02
•
Granted: 1989-11-28
•
Expires: 2009-03-02
Abstract
Abstract The invention relates to a soluble acrylate copolymer which can be obtained by copolymerization of more than 3 to 30% by weight, based on the total weight of all the monomers, of a monomer with at least 2 polymerizable, olefinically unsaturated double bonds, monomers which carry functional groups and other monomers with a polymerizable double bond, the acid number of the acrylate resin being 15 to 200. The invention furthermore relates to processes for the preparation of the acrylate copolymers and coatings based thereon and based on polyepoxides.
Inventors
- 👤 Werner Jung
- 👤 Axel Sievers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 05:18
CPC Classifications
C; C08; C08F; C08F2/00; C08F2/04; C08F2/06; C09; C09D; C09D133/00; C09D133/04; C09D133/06; C09D133/062; C09D133/064; C08L; C08L63/00
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
141 words
A coating agent containing as an essential binder, (A) an acrylate copolymer prepared by copolymerizing monomers having at least two polymerizable, olefinically unsaturated double bonds, monomers which carry functional groups and other polymerizable monomers with an olefinically unsaturated double bond, the acrylate copolymer containing carboxyl groups, wherein more than 3 to 30% by weight, based on the total weight of the monomers, of a monomer with at least 2 polymerizable, olefinically unsaturated double bonds is copolymerized into the acrylate copolymer and the acid number of the acrylate copolymer is 15 to 200, and (B) a compound containing at least two epoxide groups per molecule, the ratio of (A) to (B) being such that the ratio of the acid groups of (A) to the epoxide groups of (B) is in the range of 0.5:3 to 2:0.5, and a crosslinking catalyst if appropriate.
Claim 2
Dependent Claim
141 words
A coating agent containing as an essential binder, (A) an acrylate copolymer prepared by copolymerizing monomers having at least two polymerizable, olefinically unsaturated double bonds, monomers which carry functional groups and other polymerizable monomers with an olefinically unsaturated double bond, the acrylate copolymer containing carboxyl groups, wherein more than 3 to 30% by weight, based on the total weight of the monomers, of a monomer with at least 2 polymerizable, olefinically unsaturated double bonds is copolymerized into the acrylate copolymer and the acid number of the acrylate copolymer is 15 to 200, and (B) a compound containing at least two epoxide groups per molecule, the ratio of (A) to (B) being such that the ratio of the acid groups of (A) to the epoxide groups of (B) is in the range of 0.5:3 to 2:0.5, and a crosslinking catalyst if appropriate.
Claim 3
Dependent Claim
89 words
A coating agent as described in claim 37 wherein the acrylate copolymer (A) comprises: (a 1 ) more than 3 to 30 percent by weight of a monomer with at least two polymerizable, olefinically unsaturated double bonds; (a 2 ) 3 to 30 percent by weight of a monomer containing carboxyl groups; (a 3 ) 40 to 93 percent by weight of other monomers with a polymerizable, olefinically unsaturated double bond; the sum of (a 1 ), (a 2 ), and (a 3 ) being 100 percent by weight.
Claim 4
Dependent Claim
45 words
A coating agent as described in claim 38 wherein 0.1 to 5% by weight of acrylate copolymer, based on the total weight of all monomers, comprises monomers with phosphoric acid groups, which are employed as the other monomers with a polymerizable, olefinically unsaturated double bond.
Claim 5
Dependent Claim
142 words
A coating agent as described in claim 38 wherein the acrylate copolymer can be obtained from: (a 1 ) more than 3 to 30 percent by weight of a monomer with at least two polymerizable, olefinically unsaturated double bonds, di-and polyesters of di- and polyols, with acrylic acid being excluded; (a 2 ) 3 to 30 percent by weight of a monomer containing carboxyl groups; (a 3 ) 0.1 to 20% by weight of a tertiary amine with a polymerizable, olefinically unsaturated double bond; (a 4 ) 0 to 40% by weight of a monomer containing hydroxyl groups, and (a 5 ) 0 to 80% by weight of other monomers with a polymerizable, olefinically unsaturated double bond, the sum of components (a 1 ), (a 2 ), (a 3 ), (a 4 ) and (a 5 ) being 100 percent by weight.
Claim 6
Dependent Claim
44 words
A coating agent as defined in claim 40 wherein the acrylate copolymer contains 0.1 to 5% by weight, based on the total weight of the monomers, of monomers with phosphoric acid groups, employed as the other monomers with a polymerizable, olefinically unsaturated double bond.
Claim 7
Dependent Claim
132 words
A coating agent as defined in claim 37 wherein the soluble acrylate copolymer is obtained from: (a 1 ) more than 3 to 30 percent by weight of a monomers with at least two polymerizable, olefinically unsaturated double bonds, di-and polyesters of di- and polyols with acrylic acid being excluded; (a 2 ) 0.1 to 20% by weight of a tertiary amine with a polymerizable, olefinically unsaturated double bond; (a 3 ) 5 to 40% by weight of monomers containing hydroxyl groups; (a 4 ) 0 to 80% by weight of other polymerizable monomers with an olefinically unsaturated double bond, and (a 5 ) cyclic carboxylic acid anhydrides, the sum of (a 1 ), (a 2 ), (a 3 ), (a 4 ) and (a 5 ) being 100 percent by weight.
Claim 8
Dependent Claim
65 words
The coating agent of claim 42 wherein the acrylate copolymer is further obtained by copolymerizing the monomers in an organic solvent at 70° C. to 130° C. using at least 0.5% by weight based on the total weight of the monomers, of a polymerization regulator, and using polymerization initiators, to give a pre-crosslinked, non-gelled product and reacting the copolymers with the cyclic carboxylic acid anhydrides.
Claim 9
Dependent Claim
137 words
A coating agent as described in claim 37 wherein the soluble acrylate polymer is obtained from: (a 1 ) more than 3 to 30 percent by weight of monomers with at least two polymerizable, olefinically unsaturated double bonds; (a 2 ) 1 to 25 percent by weight of monomers with cyclic carboxylic acid anhydride groups; (a 3 ) 45 to 80% by weight of other polymerizable monomers with an olefinically saturated double bond, the sum of (a 1 ), (a 2 ), and (a 3 ), being 100 percent by weight, and (a 4 ) compounds which contain at least one hydrogen which can react with an acid anhydride group and at least one tertiary amino group, it also being possible for the carboxylic acid anhydride groups to be reacted with a monofunctional compound with active hydrogen.
Claim 10
Dependent Claim
17 words
The coating agent of claim 44 wherein the (a 4 ) component contains a tertiary amino group.
Claim 11
Dependent Claim
23 words
The coating agent of claim 45 wherein the (a 4 ) component comprises a primary or secondary amine with a tertiary amino group.
Claim 12
Dependent Claim
136 words
A coating agent as defined in claim 37 wherein the acrylate copolymer can be obtained from: (a 1 ) more than 3 to 30 percent by weight of monomers with at least two polymerizable, olefinically unsaturated double bonds; (a 2 ) 1 to 30 percent by weight of glycidyl esters of ethylenically unsaturated carboxylic acids or glycidyl ethers of olefinically unsaturated compounds; (a 3 ) 40 to 95% by weight of other polymerizable monomers with an olefinically unsaturated double bond, the sum of all the monomers being 100% by weight; and (a 4 ) amines with a secondary amino group or di-or polyamines with at least one tertiary amino group and one primary or secondary amino group; (a 5 ) carboxylic acid which contains a tertiary nitrogen atom, or (a 6 ) cyclic carboxylic acid anhydrides.
Claim 13
Dependent Claim
74 words
A coating agent as defined in claim 47 wherein the acrylate copolymer is further obtained by first copolymerizing in an organic solvent at 70° C. to 130° C. using at least 0.5% by weight based on the total weight of the monomers, of a polymerization regulator, and using polymerization initiators to give a pre-crosslinked, non-gelled product, and then reacting the di- or polyamines with the carboxylic acids and with the cyclic carboxylic acid anhydrides.
Claim 14
Dependent Claim
39 words
A coating agent as defined in any one of claims 37 to 48 wherein the crosslinking catalyst is used in an amount ranging from 0.5 to 10% by weight based on the weight of the di- or polyepoxide component.
Claim 15
Dependent Claim
45 words
A process for preparing the coating agent as described in claim 37 comprising blending components (A) and (B) in a proportion such that the ratio of the acid groups of (A) to the epoxide groups of (B) is in the range of 0.5:3 to 2:0.5.
Claim 16
Dependent Claim
31 words
A process for coating a substrate comprising applying a coating agent as defined in any of claims 37 to 49 to the substrate, and hardening the composition to form a coating.
Claim 17
Dependent Claim
21 words
A coated substrate comprising a substrate and the coating agent of any of claims 37 to 49 applied to the substrate.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-11-27 | 1993-05-29 | 1993-11-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-11-27 | 1997-05-29 | 1997-11-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-11-27 | 2001-05-29 | 2001-11-28 | $7700.00 | Window Closed / Lapsed |