Monolithic compound-ceramic capacitor
Assignee: MRA Laboratories Inc
•
Filing: 1988-12-05
•
Granted: 1989-11-21
•
Expires: 2008-12-05
Abstract
Abstract A green ceramic cake is formed comprised of a center layer of fine-ceramic particles sandwiched between two outer layers of relatively coarse-ceramic particles. However, the chemical compositions of the center and outer layers are all essentially the same. The center layer contains a stack of spaced-apart film-patterns of electroding ink. This cake is separated into many individual green monolithic-ceramic capacitors each with electrodes extending conventionally to opposite ends thereof. These capacitors are sintered to mature the ceramic, and conductive terminations are formed at the opposite ends contacting the buried electrodes. The finer start powder of the center layer is relatively expensive, but the resulting fine grain homogenous grain structure there in the finished capacitor permits closely spaced buried electrodes and generally a higher quality dielectric due to greater density and more homogenous composition than is achieved in the cheaper outer layer material.
Inventors
- 👤 Galeb H. Maher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 13:29
CPC Classifications
H; H01; H01G; H01G4/00; H01G4/30; Y; Y10; Y10T; Y10T29/00; Y10T29/43; Y10T29/435
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
90 words
A monolithic ceramic capacitor comprising: (a) one layer comprising a mature polycrystalline ceramic having a narrow and homogenous distribution of grain sizes; (b) a stack of at least two spaced-apart conductive film electrodes buried in said one layer; and (c) two outer layers comprising a mature polycrystalline ceramic, each of said two layers located on opposite surfaces of said one layer and being co-reacted and bonded thereto, said ceramic of said two layers having a distinctly broader and less homogenous distribution of grain sizes than that of said one-layer ceramic.
Claim 2
Dependent Claim
90 words
A monolithic ceramic capacitor comprising: (a) one layer comprising a mature polycrystalline ceramic having a narrow and homogenous distribution of grain sizes; (b) a stack of at least two spaced-apart conductive film electrodes buried in said one layer; and (c) two outer layers comprising a mature polycrystalline ceramic, each of said two layers located on opposite surfaces of said one layer and being co-reacted and bonded thereto, said ceramic of said two layers having a distinctly broader and less homogenous distribution of grain sizes than that of said one-layer ceramic.
Claim 3
Dependent Claim
21 words
The capacitor of claim 1 wherein the chemical composition and grain structure are essentially the same in said two outer layers.
Claim 4
Dependent Claim
17 words
The capacitor of claim 2 wherein the thicknesses of said two outer layers are essentially the same.
Claim 5
Dependent Claim
32 words
The capacitor of claim 1 wherein said electrodes are spaced apart by less than 0.75 mil (19 microns) and the grains of said one-layer ceramic are smaller than 0.5 mil (12.7 microns).
Claim 6
Dependent Claim
32 words
The capacitor of claim 1 wherein said electrodes are spaced apart by less than 0.5 mil (12.7 microns) and the grains of said one-layer ceramic are smaller than 0.33 mil (8.5 microns).
Claim 7
Dependent Claim
24 words
The capacitor of claim 1 wherein the average grain size of said one layer is substantially less than that of said two outer layers.
Claim 8
Dependent Claim
32 words
The capacitor of claim 1 wherein the composition of said two outer layers is essentially the same as the composition of said one-layer and have essentially the same temperature coefficient of expansion.
Claim 9
Dependent Claim
20 words
The capacitor of claim 7 wherein said composition of said one layer and said two layers is a barium titanate.
Claim 10
Dependent Claim
20 words
The capacitor of claim 7 wherein said composition of said one layer and said two layers is a rare-earth titanate.
Claim 11
Dependent Claim
35 words
The capacitor of claim 1 wherein said one-and two-layers are additionally comprised of a sintering flux, selected from silicates, borates and combinations thereof, said flux being located at the grain boundaries of said polycrystalline ceramics.
Claim 12
Independent Claim
113 words
A method for making a monolithic ceramic capacitor comprising: (a) forming one green ceramic layer comprising submicron particles of one ceramic composition and an organic binder binding said submicron particles together, and a stack of at least two spaced apart conductive film electrodes buried in said one green layer; (b) forming on opposite surfaces of said one green layer, respectively, two green ceramic layers each comprising large particles of essentially the same ceramic composition and an organic binder binding said large particles together, said large particles having an average particle size greater than one micron; and (c) co-sintering said green layers to simultaneously densify and mature said one and said two ceramic layers.
Claim 13
Independent Claim
113 words
A method for making a monolithic ceramic capacitor comprising: (a) forming one green ceramic layer comprising submicron particles of one ceramic composition and an organic binder binding said submicron particles together, and a stack of at least two spaced apart conductive film electrodes buried in said one green layer; (b) forming on opposite surfaces of said one green layer, respectively, two green ceramic layers each comprising large particles of essentially the same ceramic composition and an organic binder binding said large particles together, said large particles having an average particle size greater than one micron; and (c) co-sintering said green layers to simultaneously densify and mature said one and said two ceramic layers.
Claim 14
Dependent Claim
13 words
The method of claim 11 wherein said ceramic composition is a barium titanate.
References Cited (Backward Citations)
US4284521A
Cited
US4424615A
Cited
US4302625A
Cited
US4556929A
Cited
US4620264A
Cited
US4533974A
Cited
US4650648A
Cited
US4764357A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-11-20 | 1993-05-22 | 1993-11-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-11-20 | 1997-05-22 | 1997-11-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-11-20 | 2001-05-22 | 2001-11-21 | $7700.00 | Window Closed / Lapsed |