US4882402A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Side chain liquid crystalline polymeric media exhibiting third order nonlinear optical response
Assignee: Corning Inc
•
Filing: 1987-10-15
•
Granted: 1989-11-21
•
Expires: 2007-10-15
Abstract
Abstract This invention provides a process for producing a transparent optical medium consisting of a liquid crystalline polymer which exhibits third order nonlinear optical response. Illustrative of an invention optical medium is a transparent film of a side chain liquid crystalline polymer corresponding to the formula: ##STR1## The transparent film has an isotropic molecular configuration with macroscopic centrosymmetry, and exhibits essentially no scattering of a transmitted incident light beam.
Inventors
- 👤 Thomas M. Leslie
- 👤 Hyun N. Yoon
- 👤 Ronald N. DeMartino
- 👤 James B. Stamatoff
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 21:45
CPC Classifications
C; C09; C09K; C09K19/00; C09K19/04; C09K19/38; C09K19/3833; C09K19/3842; C09K19/3852; G; G02; G02F; G02F1/00; G02F1/35; G02F1/355; G02F1/361; G02F1/3615; G02F1/3617
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
171 words
A transparent nonlinear optical medium produced in accordance with a process which comprises heating a thermotropic liquid crystalline polymer above the mesophase temperature range to form an isotropic melt phase, and cooling the isotropic melt phase rapidly to below the glass transition temperature of the polymer to form a transparent solid medium; wherein the transparent nonlinear optical medium exhibits a third order nonlinear optical susceptibility χ.sup.(3) of at least about 1×10 -11 esu as measured at 1.91 μm excitation wavelength, and wherein the polymer is characterized by a recurring monomeric unit corresponding to the formula: ##STR20## where n is an integer between about 4-20; X 1 is --NR 1 --, --O--, or --S--; R 1 is hydrogen or methyl; Z 1 is --NO 2 , --CN or --CF 3 ; and where the polymer has a weight average molecular weight in the range between about 5000-200,000, and a glass transition temperature above about 40° C.; and wherein the optical medium exhibits less than about 5 percent scattering of transmitted incident light.
Claim 2
Dependent Claim
171 words
A transparent nonlinear optical medium produced in accordance with a process which comprises heating a thermotropic liquid crystalline polymer above the mesophase temperature range to form an isotropic melt phase, and cooling the isotropic melt phase rapidly to below the glass transition temperature of the polymer to form a transparent solid medium; wherein the transparent nonlinear optical medium exhibits a third order nonlinear optical susceptibility χ.sup.(3) of at least about 1×10 -11 esu as measured at 1.91 μm excitation wavelength, and wherein the polymer is characterized by a recurring monomeric unit corresponding to the formula: ##STR20## where n is an integer between about 4-20; X 1 is --NR 1 --, --O--, or --S--; R 1 is hydrogen or methyl; Z 1 is --NO 2 , --CN or --CF 3 ; and where the polymer has a weight average molecular weight in the range between about 5000-200,000, and a glass transition temperature above about 40° C.; and wherein the optical medium exhibits less than about 5 percent scattering of transmitted incident light.
Claim 3
Dependent Claim
171 words
A transparent nonlinear optical medium produced in accordance with a process which comprises heating a thermotropic liquid crystalline polymer above the mesophase temperature range to form an isotropic melt phase, and cooling the isotropic melt phase rapidly to below the glass transition temperature of the polymer to form a transparent solid medium; wherein the transparent nonlinear optical medium exhibits a third order nonlinear optical susceptibility χ.sup.(3) of at least about 1×10 -11 esu as measured at 1.91 μm excitation wavelength, and wherein the polymer is characterized by a recurring monomeric unit corresponding to the formula: ##STR21## where n is an integer between about 4-20; X 1 is --NR 1 --, --O--, or --S--; R 1 is hydrogen or methyl; Z 1 is --NO 2 , --CN or --CF 3 ; and where the polymer has a weight average molecular weight in the range between about 5000-200,000, and a glass transition temperature above about 40° C.; and wherein the optical medium exhibits less than about 5 percent scattering of transmitted incident light.
Claim 4
Dependent Claim
171 words
A transparent nonlinear optical medium produced in accordance with a process which comprises heating a thermotropic liquid crystalline polymer above the mesophase temperature range to form an isotropic melt phase, and cooling the isotropic melt phase rapidly to below the glass transition temperature of the polymer to form a transparent solid medium; wherein the transparent nonlinear optical medium exhibits a third order nonlinear optical susceptibility χ.sup.(3) of at least about 1×10 -11 esu as measured at 1.91 μm excitation wavelength, and wherein the polymer is characterized by a recurring monomeric unit corresponding to the formula: ##STR21## where n is an integer between about 4-20; X 1 is --NR 1 --, --O--, or --S--; R 1 is hydrogen or methyl; Z 1 is --NO 2 , --CN or --CF 3 ; and where the polymer has a weight average molecular weight in the range between about 5000-200,000, and a glass transition temperature above about 40° C.; and wherein the optical medium exhibits less than about 5 percent scattering of transmitted incident light.
Claim 5
Dependent Claim
138 words
A transparent nonlinear optical medium comprising a liquid crystalline polymer which is characterized by a recurring monomeric unit corresponding to the formula: ##STR22## where n is an integer between about 4-20; X 1 is --NR 1 --, --O--, or --S--; R 1 is hydrogen or methyl; Z 1 is --NO 2 , --CN or --CF 3 ; and where the polymer has a weight average molecular weight in the range between about 5000-200,000, and a glass transition temperature above about 40° C.; wherein the transparent nonlinear optical medium exhibits a third order nonlinear optical susceptibility χ.sup.(13) of at least about 1×10 -11 esu as measured at 1.91 μm excitation wavelength, and the optical medium has an isotropic molecular configuration with macroscopic centrosymmetry; and wherein the optical medium exhibits less than about 5 percent scattering of transmitted incident light.
Claim 6
Dependent Claim
138 words
A transparent nonlinear optical medium comprising a liquid crystalline polymer which is characterized by a recurring monomeric unit corresponding to the formula: ##STR22## where n is an integer between about 4-20; X 1 is --NR 1 --, --O--, or --S--; R 1 is hydrogen or methyl; Z 1 is --NO 2 , --CN or --CF 3 ; and where the polymer has a weight average molecular weight in the range between about 5000-200,000, and a glass transition temperature above about 40° C.; wherein the transparent nonlinear optical medium exhibits a third order nonlinear optical susceptibility χ.sup.(13) of at least about 1×10 -11 esu as measured at 1.91 μm excitation wavelength, and the optical medium has an isotropic molecular configuration with macroscopic centrosymmetry; and wherein the optical medium exhibits less than about 5 percent scattering of transmitted incident light.
References Cited (Backward Citations)
US4631328A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-11-20 | 1993-05-22 | 1993-11-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-11-20 | 1997-05-22 | 1997-11-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-11-20 | 2001-05-22 | 2001-11-21 | $7700.00 | Window Closed / Lapsed |