Moisture-resistant, coated thermoplastic film having enhanced adhesion to inks and metallic layers
Assignee: Mitsubishi Chemical America Inc
•
Filing: 1987-11-03
•
Granted: 1989-11-14
•
Expires: 2007-11-03
Abstract
Abstract A two-step, sequential coating method is disclosed which permits the use of aqueous precursor solutions to coat water-insoluble compounds onto thermoplastic film. In a preferred embodiment, an aqueous oleic acid/ammonium oleate solution is coated onto amorphous polyester sheet which is subsequently monoaxially oriented by stretching in the machine direction, and coated with an aqueous solution of calcium hydroxide, thereby forming a layer of calcium oleate in situ. The coated film is subsequently biaxially oriented by stretching in the transverse direction, and heat-set.
Inventors
- 👤 David Rudd
- 👤 R. Scott Caines
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 21:48
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/04; C08J7/06; C08J7/065; B; B05; B05D; B05D5/00; B05D5/04; B05D7/00; B05D7/02; B05D7/04; B29; B29C; B29C55/00; B29C55/02; B29C55/023; B29C55/026; C08J7/043; B29K; B29K2067/00; Y; Y10; Y10T; Y10T428/00; Y10T428/27; Y10T428/273; Y10T428/31504; Y10T428/31536; Y10T428/31786
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
93 words
A moisture-resistant, coated thermoplastic film comprising: (i) an oriented thermoplastic film; and (ii) a moisture-resistant coating on at least one side of said film, said coating having been applied to said film by sequentially coating said film with at least two aqueous solutions, one of which contains a precursor A and the other solution containing precursor B, such that A and B react to form at least one alkaline earth salt of a fatty acid having 10 to 18 carbon atoms upon said film which is less water-soluble than either A or B.
Claim 2
Dependent Claim
93 words
A moisture-resistant, coated thermoplastic film comprising: (i) an oriented thermoplastic film; and (ii) a moisture-resistant coating on at least one side of said film, said coating having been applied to said film by sequentially coating said film with at least two aqueous solutions, one of which contains a precursor A and the other solution containing precursor B, such that A and B react to form at least one alkaline earth salt of a fatty acid having 10 to 18 carbon atoms upon said film which is less water-soluble than either A or B.
Claim 3
Dependent Claim
32 words
The film of claim 1, wherein said film is an oriented polyester film and said coating is present in an amount effective to improve the adhesion of printing inks to said film.
Claim 4
Dependent Claim
15 words
The film of claim 2 wherein said oriented polyester film is biaxially oriented polyethylene terephthalate.
Claim 5
Dependent Claim
29 words
The film of claim 2 wherein said coating has a dry coating weight of from about 1×10 -8 to about 2×10 -5 lbs per square foot of film surface.
Claim 6
Dependent Claim
25 words
The film of claim 4 wherein said dry coating weight is from about 2×10 -7 to 7×10 -6 lbs per square foot of film surface.
Claim 7
Dependent Claim
16 words
The film of claim 4 wherein said coating comprises an alkaline earth salt of oleic acid.
Claim 8
Dependent Claim
11 words
The film of claim 6 wherein said coating comprises calcium oleate.
Claim 9
Dependent Claim
15 words
The film of claim 7 having a printing ink composition applied directly to said coating.
Claim 10
Dependent Claim
39 words
The film of claim 7 having a metallic layer directly applied to said coating, said metallic layer comprising a metal selected from the group consisting of aluminum, chromium, copper, gold, indium, nickel, silver, stainless steel, tin, titanium, and zinc.
Claim 11
Dependent Claim
11 words
The film of claim 9 wherein said metallic layer comprises aluminum.
Claim 12
Dependent Claim
19 words
The film of claim 9 wherein said metallic layer is applied to said coating by a vacuum deposition technique.
Claim 13
Dependent Claim
111 words
A moisture-resistant, coated polyester film produced by the process comprising (i) extruding a substantially amorphous polyester resin in sheet-like form and subsequently cooling said resin to form cast polyester sheet, (ii) coating said sheet with a first aqueous solution containing a fatty acid having from 10 to 18 carbon atoms; (iii) subsequently orienting said polyester sheet in the longitudinal direction, thereby forming monoaxially oriented polyester film, p1 (iv) coating said monoaxially oriented polyester film with a second aqueous solution containing an alkaline earth hydroxide, p1 (v) subsequently orienting said monoaxially oriented polyester film in the transverse direction, thereby forming biaxially oriented polyester film, (vi) heatsetting said biaxially oriented coated polyester film.
Claim 14
Dependent Claim
111 words
A moisture-resistant, coated polyester film produced by the process comprising (i) extruding a substantially amorphous polyester resin in sheet-like form and subsequently cooling said resin to form cast polyester sheet, (ii) coating said sheet with a first aqueous solution containing a fatty acid having from 10 to 18 carbon atoms; (iii) subsequently orienting said polyester sheet in the longitudinal direction, thereby forming monoaxially oriented polyester film, p1 (iv) coating said monoaxially oriented polyester film with a second aqueous solution containing an alkaline earth hydroxide, p1 (v) subsequently orienting said monoaxially oriented polyester film in the transverse direction, thereby forming biaxially oriented polyester film, (vi) heatsetting said biaxially oriented coated polyester film.
Claim 15
Dependent Claim
21 words
The film of claim 12 wherein said first aqueous solution comprises oleic acid and said second aqueous solution comprises calcium hydroxide.
Claim 16
Dependent Claim
17 words
The film of claim 13 having a printing ink composition applied directly to said coated polyester film.
Claim 17
Dependent Claim
45 words
The film of claim 13 having a metallic layer directly applied to the coated side of said film, said metallic layer comprising at least one metal selected from the group consisting of aluminum, chromium, copper, gold, indium, nickel, silver, stainless steel, tin, titanium, and zinc.
Claim 18
Dependent Claim
26 words
The film of claim 12 wherein said first aqueous solution is substantially dried on the surface of said polyester sheet prior to orienting said polyester sheet.
Claim 19
Dependent Claim
30 words
The film of claim 16 wherein said second aqueous solution is substantially dried on the surface of said monoaxially oriented polyester film prior to orienting said monoaxially oriented polyester film.
Claim 20
Dependent Claim
32 words
The film of claim 13 wherein said first aqueous solution additionally contains from 3 to 7 weight percent ammonium hydroxide, based upon the weight of oleic acid present in said aqueous solution.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-11-13 | 1993-05-15 | 1993-11-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-11-13 | 1997-05-15 | 1997-11-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-11-13 | 2001-05-15 | 2001-11-14 | $7700.00 | Window Closed / Lapsed |