Ceramic composite and methods of making the same
Assignee: Lanxide Technology Co LP
•
Filing: 1987-01-12
•
Granted: 1989-10-17
•
Expires: 2007-01-12
Abstract
Abstract There is provided a method for producing a self-supporting ceramic composite comprising (1) a ceramic matrix obtained by oxidation of an aluminum zinc alloy to form a polycrystalline oxidation reaction product of the metal with an oxidant, and (2) one or more fillers embedded by the matrix. The metal alloy and permeable mass of filler having at least one defined surface boundary are oriented relative to each other so that formation of the oxidation reaction product will occur into said mass of filler and in a direction towards said defined surface boundary. On heating the metal to a first temperature above its melting point but below the melting point of said oxidation reaction product to form a body of molten parent metal, the molten metal reacts with said oxidant to form said oxidation reaction product which infiltrates said mass of filler to said defined surface boundary. The resulting infiltrated mass is heated to a second temperature in order to remove or oxidize at least a substantial portion of any residual non-oxidized metallic constituents from or in said infiltrated mass without substantial formation of said oxidation reaction product beyond said defined surface boundary, thereby producing a self-supporting ceramic composite.
Inventors
- 👤 Jack A. Kuszyk
- 👤 Christopher R. Kennedy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 21:27
CPC Classifications
C; C04; C04B; C04B35/00; B; B22; B22D; B22D41/00; B22D41/14; B22D41/22; B22D41/28; B22D41/30; B22D41/32; C04B35/622; C04B35/64; C04B35/65; C04B35/652
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
379 words
A method for producing a self-supporting ceramic composite comprising (1) a ceramic matrix obtained by oxidation of a parent metal comprising an aluminum alloy to form a polycrystalline material comprising an oxidation reaction product of the parent metal with at least one oxidant; and (2) at least one filler embedded by the matrix, which method comprises: (a) positioning a parent metal, comprising an aluminum alloy having at least about 1% by weight zinc, adjacent to a permeable mass of filler having at least one defined surface boundary and orienting said parent metal and said filler relative to each other so that formation of an oxidation reaction product of the parent metal with an oxidant will occur into said mass of filler and in a direction towards said defined surface boundary; (b) heating said parent metal to a first temperature above its melting point but below the melting point of said oxidation reaction product to form a body of molten parent metal and reacting the molten parent metal with said oxidant at said first temperature to form said oxidation reaction product, and at said first temperature maintaining at least a portion of said oxidation reaction product in contact with and extending between said body of molten metal and said oxidant, to draw molten metal through the oxidation reaction product towards the oxidant and towards and into the adjacent mass of filler so that fresh oxidation reaction product continues to form within the mass of filler at an interface between the oxidant and previously formed oxidation reaction product, and continuing said reaction for a time sufficient to infiltrate said mass of filler to said defined surface boundary, with said ceramic matrix, said ceramic matrix containing at least some residual non-oxidized metallic constituents of said parent metal; and (c) heating the resulting infiltrated mass of step (b) in at least one environment selected from the group consisting of an oxygen-containing atmosphere, an inert atmosphere and a vacuum to a second temperature above the first temperature but below the melting point of the oxidation reaction product to remove or oxidize at least a substantial portion of said residual non-oxidized metallic constituents of said parent metal without substantial formation of oxidation reaction product beyond said defined surface boundary, thereby producing a self-supporting ceramic composite.
Claim 2
Independent Claim
379 words
A method for producing a self-supporting ceramic composite comprising (1) a ceramic matrix obtained by oxidation of a parent metal comprising an aluminum alloy to form a polycrystalline material comprising an oxidation reaction product of the parent metal with at least one oxidant; and (2) at least one filler embedded by the matrix, which method comprises: (a) positioning a parent metal, comprising an aluminum alloy having at least about 1% by weight zinc, adjacent to a permeable mass of filler having at least one defined surface boundary and orienting said parent metal and said filler relative to each other so that formation of an oxidation reaction product of the parent metal with an oxidant will occur into said mass of filler and in a direction towards said defined surface boundary; (b) heating said parent metal to a first temperature above its melting point but below the melting point of said oxidation reaction product to form a body of molten parent metal and reacting the molten parent metal with said oxidant at said first temperature to form said oxidation reaction product, and at said first temperature maintaining at least a portion of said oxidation reaction product in contact with and extending between said body of molten metal and said oxidant, to draw molten metal through the oxidation reaction product towards the oxidant and towards and into the adjacent mass of filler so that fresh oxidation reaction product continues to form within the mass of filler at an interface between the oxidant and previously formed oxidation reaction product, and continuing said reaction for a time sufficient to infiltrate said mass of filler to said defined surface boundary, with said ceramic matrix, said ceramic matrix containing at least some residual non-oxidized metallic constituents of said parent metal; and (c) heating the resulting infiltrated mass of step (b) in at least one environment selected from the group consisting of an oxygen-containing atmosphere, an inert atmosphere and a vacuum to a second temperature above the first temperature but below the melting point of the oxidation reaction product to remove or oxidize at least a substantial portion of said residual non-oxidized metallic constituents of said parent metal without substantial formation of oxidation reaction product beyond said defined surface boundary, thereby producing a self-supporting ceramic composite.
Claim 3
Dependent Claim
22 words
The method of claim 1, wherein at least one dopant in addition to zinc is used in conjunction with the parent metal.
Claim 4
Dependent Claim
23 words
The method of claim 1 or claim 2, wherein said filler comprises from about 3% by weight to about 10% by weight silica.
Claim 5
Dependent Claim
25 words
The method of claim 1 or claim 2, wherein said oxidant comprises an oxygen-containing gas and said oxidation reaction product comprises an oxide of aluminum.
Claim 6
Dependent Claim
13 words
The method of claim 4, wherein said oxidant comprises air at atmospheric pressure.
Claim 7
Dependent Claim
21 words
The method of claim 1 or claim 2, wherein said first temperature is from about 850° C. to about 1450° C.
Claim 8
Dependent Claim
18 words
The method of claim 1, wherein said first temperature is from about 950° C. to about 1100° C.
Claim 9
Dependent Claim
15 words
The method of claim 1, wherein said second temperature is greater than about 1250° C.
Claim 10
Dependent Claim
15 words
The method of claim 1, wherein said second temperature is at least about 1400° C.
Claim 11
Dependent Claim
20 words
The method of claim 1, wherein heating step (c) to said second temperature is effected in air at atmospheric pressure.
Claim 12
Dependent Claim
45 words
The method of claim 1 or claim 2, wherein said filler comprises at least one metal oxide, boride, nitride, or carbide of a metal selected from the group consisting of aluminum, cerium, hafnium, lanthanum, silicon, neodymium, praseodymium, samarium, scandium, thorium, uranium, titanium, yttrium, and zirconium.
Claim 13
Dependent Claim
29 words
The method of claim 1 or claim 2, wherein said filler comprises a material selected from the group consisting of granules, fibers, tubes, refractory fiber cloth, and mixtures thereof.
Claim 14
Dependent Claim
20 words
The method of claim 1 or claim 2, wherein said filler comprises at least one of alumina and silicon carbide.
Claim 15
Dependent Claim
37 words
The method of claim 1 or claim 2, wherein said ceramic matrix resulting from said heating step (c) comprises interconnected porosity having at least a portion being accessible from at least one surface of said ceramic composite.
Claim 16
Dependent Claim
21 words
The method of claim 14, wherein said interconnected porosity comprises openings having a mean diameter of less than about 6 microns.
Claim 17
Independent Claim
377 words
A method for producing a self-supporting ceramic composite comprising (1) a ceramic matrix obtained by oxidation of a parent metal comprising an aluminum alloy to form a polycrystalline material comprising an oxidation reaction product of the parent metal with at least one oxidant; and (2) at least one filler embedded by the matrix, which method comprises: (a) positioning a parent metal, comprising an aluminum alloy having about 4-7% by weight zinc, adjacent to a permeable mass of filler having at least one defined surface boundary and orienting said parent metal and said filler relative to each other so that formation of an oxidation reaction product of the parent metal with an oxidant will occur into said mass of filler and in a direction towards said defined surface boundary; (b) heating said parent metal to a first temperature above its melting point but below the melting point of said oxidation reaction product to form a body of molten parent metal and reacting the molten parent metal with said oxidant at said first temperature to form said oxidation reaction product, and at said first temperature maintaining at least a portion of said oxidation reaction product in contact with and extending between said body of molten metal and said oxidant, to draw molten metal through the oxidation reaction product towards the oxidant and towards and into the adjacent mass of filler so that fresh oxidation reaction product continues to form within the mass of filler at an interface between the oxidant and previously formed oxidation reaction product, and continuing said reaction for a time sufficient to infiltrate said mass of filler to said defined surface boundary, with said ceramic matrix, said ceramic matrix containing at least some residual non-oxidized metallic constituents of said parent metal; and (c) heating the resulting infiltrated mass of step (b) in at least one environment selected from the group consisting of an oxygen-containing atmosphere, an inert atmosphere and a vacuum to a second temperature above the first temperature but below the melting point of the oxidation reaction product to remove or oxidize at least a substantial portion of said residual non-oxidized metallic constituents of said parent metal without substantial formation of oxidation reaction product beyond said defined surface boundary, thereby producing a self-supporting ceramic composite.
Claim 18
Independent Claim
377 words
A method for producing a self-supporting ceramic composite comprising (1) a ceramic matrix obtained by oxidation of a parent metal comprising an aluminum alloy to form a polycrystalline material comprising an oxidation reaction product of the parent metal with at least one oxidant; and (2) at least one filler embedded by the matrix, which method comprises: (a) positioning a parent metal, comprising an aluminum alloy having about 4-7% by weight zinc, adjacent to a permeable mass of filler having at least one defined surface boundary and orienting said parent metal and said filler relative to each other so that formation of an oxidation reaction product of the parent metal with an oxidant will occur into said mass of filler and in a direction towards said defined surface boundary; (b) heating said parent metal to a first temperature above its melting point but below the melting point of said oxidation reaction product to form a body of molten parent metal and reacting the molten parent metal with said oxidant at said first temperature to form said oxidation reaction product, and at said first temperature maintaining at least a portion of said oxidation reaction product in contact with and extending between said body of molten metal and said oxidant, to draw molten metal through the oxidation reaction product towards the oxidant and towards and into the adjacent mass of filler so that fresh oxidation reaction product continues to form within the mass of filler at an interface between the oxidant and previously formed oxidation reaction product, and continuing said reaction for a time sufficient to infiltrate said mass of filler to said defined surface boundary, with said ceramic matrix, said ceramic matrix containing at least some residual non-oxidized metallic constituents of said parent metal; and (c) heating the resulting infiltrated mass of step (b) in at least one environment selected from the group consisting of an oxygen-containing atmosphere, an inert atmosphere and a vacuum to a second temperature above the first temperature but below the melting point of the oxidation reaction product to remove or oxidize at least a substantial portion of said residual non-oxidized metallic constituents of said parent metal without substantial formation of oxidation reaction product beyond said defined surface boundary, thereby producing a self-supporting ceramic composite.
Claim 19
Dependent Claim
18 words
The method of claim 16, wherein said first temperature is from about 850° C. to about 1450° C.
Claim 20
Dependent Claim
18 words
The method of claim 16, wherein said first temperature is from about 950° C. to about 1100° C.
Claim 21
Dependent Claim
15 words
The method of claim 16, wherein said second temperature is greater than about 1250° C.
Claim 22
Dependent Claim
15 words
The method of claim 16, wherein said second temperature is at least about 1400° C.
Claim 23
Dependent Claim
34 words
The method of claim 16, wherein said ceramic matrix resulting from said heating step (c) comprises interconnected porosity having at least a portion being accessible from at least one surface of said ceramic composite.
Claim 24
Dependent Claim
21 words
The method of claim 21, wherein said interconnected porosity comprises openings having a mean diameter of less than about 6 microns.
Claim 25
Dependent Claim
16 words
The method of claim 1 or claim 2 wherein said filler comprises at least one whisker.
References Cited (Backward Citations)
US2741822A
Cited
US3255027A
Cited
US3298842A
Cited
US3296002A
Cited
US3419404A
Cited
US3473987A
Cited
US3421863A
Cited
US3437468A
Cited
US3789096A
Cited
US3473938A
Cited
US3864154A
Cited
US3973977A
Cited
EP0116809A1
Cited
EP0155831A2
Cited
EP0169067A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-10-16 | 1993-04-17 | 1993-10-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-10-16 | 1997-04-17 | 1997-10-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-10-16 | 2001-04-17 | 2001-10-17 | $7700.00 | Window Closed / Lapsed |