Method for welding galvanized material
Assignee: Raycon Corp
•
Filing: 1988-02-02
•
Granted: 1989-10-10
•
Expires: 2008-02-02
Abstract
Abstract A method for welding galvanized material including a low vapor pressure mild steel core and a high vapor pressure rich zinc coating includes the steps of arranging components of such galvanized material in juxtaposed relationship at a lapped joint; and applying a high density laser energy beam along the lapped joint as a weave pattern in which the weave pattern has a width great enough to bridge the lapped joint and a weave pattern frequency which forms a predetermined weld pool between the components and wherein the lapped joint and weave pattern combine to define a vapor pressure relief path so that the weld pool will not be disrupted during the application of the high density laser energy beam to the galvanized components.
Inventors
- 👤 Trevor A. Johnson
- 👤 Sharon L. Gorscak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 14:27
CPC Classifications
B; B23; B23K; B23K26/00; B23K26/20; B23K26/21; B23K26/24; B23K26/244; B23K26/32; B23K2101/00; B23K2101/34; B23K2103/00; B23K2103/02; B23K2103/04; B23K2103/08; B23K2103/50
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
126 words
A method for welding galvanized steel comprising the steps of: electroplating mild steel with a gum coating of zinc; spraying the gum coated steel with a zinc rich coating having a thickness in the range of 0.001 to 0.3 millimeters; providing a plurality of sheets with the aforesaid first and second coatings and with an edge on each of the sheets; juxtaposing the plurality of sheets with one another to form a lapped joint at edges of at least two of said plurality of sheets; and laser welding the juxtaposed sheets at the lapped joint along a pattern which will bond the juxtaposed sheets to one another while providing for the escape of vapor generated at the weld pool through a path at the lapped joint.
Claim 2
Independent Claim
126 words
A method for welding galvanized steel comprising the steps of: electroplating mild steel with a gum coating of zinc; spraying the gum coated steel with a zinc rich coating having a thickness in the range of 0.001 to 0.3 millimeters; providing a plurality of sheets with the aforesaid first and second coatings and with an edge on each of the sheets; juxtaposing the plurality of sheets with one another to form a lapped joint at edges of at least two of said plurality of sheets; and laser welding the juxtaposed sheets at the lapped joint along a pattern which will bond the juxtaposed sheets to one another while providing for the escape of vapor generated at the weld pool through a path at the lapped joint.
Claim 3
Dependent Claim
88 words
In a method for joining a plurality of galvanized steel components by use of a high density energy beam the improvement comprising: providing a edge on each of the galvanized steel components; juxtaposing the galvanized steel components to provide a lap joint between the edges thereon; impinging the high density energy beam against one of the components and advancing it along a curvilinear path which overlaps the lap joint to provide a weld zone between the galvanized steel components having a vapor escape path at the lap joint.
Claim 4
Dependent Claim
88 words
In a method for joining a plurality of galvanized steel components by use of a high density energy beam the improvement comprising: providing a edge on each of the galvanized steel components; juxtaposing the galvanized steel components to provide a lap joint between the edges thereon; impinging the high density energy beam against one of the components and advancing it along a curvilinear path which overlaps the lap joint to provide a weld zone between the galvanized steel components having a vapor escape path at the lap joint.
Claim 5
Dependent Claim
115 words
In a method for welding first and second components having a coating of material with a vapor pressure greater than that of the coated material by use of a high density energy beam the improvement comprising: providing each of the first and second components with a edge portion arranged in a juxtaposed lapped relationship; advancing the high density energy beam along a path which intercepts the exposed surface of one of the components and penetrates to the other of the components to form a molten weld pool therebetween and which periodically intercepts only the other of the components to provide a vapor escape path from the molten weld pool through the juxtaposed lapped edge portions.
Claim 6
Dependent Claim
115 words
In a method for welding first and second components having a coating of material with a vapor pressure greater than that of the coated material by use of a high density energy beam the improvement comprising: providing each of the first and second components with a edge portion arranged in a juxtaposed lapped relationship; advancing the high density energy beam along a path which intercepts the exposed surface of one of the components and penetrates to the other of the components to form a molten weld pool therebetween and which periodically intercepts only the other of the components to provide a vapor escape path from the molten weld pool through the juxtaposed lapped edge portions.
Claim 7
Dependent Claim
36 words
In the method of claim 3, providing each of said components in sheet form; and coating each of said sheets with a zinc rich coating to a thickness in the range of 0.001 to 0.3 millimeters.
Claim 8
Dependent Claim
30 words
In the method of claim 3, providing each of said components in sheet form; clinching one end of one of said sheets to form the lapped joint between the components.
Claim 9
Dependent Claim
30 words
In the method of claim 3, advancing the high density energy beam in a weave pattern having a width which overlaps an edge of at least one of the components.
Claim 10
Dependent Claim
43 words
In the method of claim 3, advancing the high density energy beam in a weave pattern having a width which overlaps the lapped joint and which has a weave to weave distance which is less than that of the width of the pattern.
Claim 11
Dependent Claim
26 words
In the method of claim 6, selecting a weave pattern having a weave to weave distance which is less than the width of the weave pattern.
Claim 12
Dependent Claim
26 words
In the method of claim 7, selecting a weave pattern having a weave to weave distance of one mm and a pattern width of 4 mm.
Claim 13
Dependent Claim
128 words
In a method for joining galvanized components having a coating with a vapor pressure greater than the vapor pressure of the coated material by use of energy which forms a molten pool between the components cooled to join the components the improvements comprising: positioning the galvanized components in a preselected relationship to define a vapor pressure relief path; applying a high density energy beam of non-contact weld energy to the positioned galvanized components to progressively melt each of the components to form a melt pool; progressively cooling the melt pool to bond the galvanized components together as the non-contact weld energy is applied thereto; and advancing the density energy beam in a weave pattern having a width which overlaps an edge of at least one of the components.
Claim 14
Dependent Claim
128 words
In a method for joining galvanized components having a coating with a vapor pressure greater than the vapor pressure of the coated material by use of energy which forms a molten pool between the components cooled to join the components the improvements comprising: positioning the galvanized components in a preselected relationship to define a vapor pressure relief path; applying a high density energy beam of non-contact weld energy to the positioned galvanized components to progressively melt each of the components to form a melt pool; progressively cooling the melt pool to bond the galvanized components together as the non-contact weld energy is applied thereto; and advancing the density energy beam in a weave pattern having a width which overlaps an edge of at least one of the components.
Claim 15
Dependent Claim
145 words
In a method for joining galvanized components having a coating with a vapor pressure greater than the vapor pressure of the coated material by use of energy which forms a molten pool between the components cooled to join the components the improvement comprising; positioning the galvanized components in a preselected lapped joint relationship to define a vapor pressure relief path; applying a high density energy beam of non-contact weld energy to the positioned galvanized components to progressively melt each of the components to form a melt pool; progressively cooling the melt pool to bond the galvanized components together as the non-contact weld energy is applied thereto; and advancing the high density energy beam in a weave pattern having a width which overlaps the lapped joint and which has a weave to weave distance which is less than that of the width of the weave pattern.
Claim 16
Dependent Claim
145 words
In a method for joining galvanized components having a coating with a vapor pressure greater than the vapor pressure of the coated material by use of energy which forms a molten pool between the components cooled to join the components the improvement comprising; positioning the galvanized components in a preselected lapped joint relationship to define a vapor pressure relief path; applying a high density energy beam of non-contact weld energy to the positioned galvanized components to progressively melt each of the components to form a melt pool; progressively cooling the melt pool to bond the galvanized components together as the non-contact weld energy is applied thereto; and advancing the high density energy beam in a weave pattern having a width which overlaps the lapped joint and which has a weave to weave distance which is less than that of the width of the weave pattern.
Claim 17
Dependent Claim
139 words
In a method for joining galvanized components having a coating with a vapor pressure greater than the vapor pressure of the coated material by use of energy which forms a molten pool between the components cooled to join the components the improvement comprising: positioning the galvanized components in a preselected lapped joint relationship to define a vapor pressure relief path; applying a high density energy beam of non-contact weld energy to the positioned galvanized components to progressively melt each of the components to form a melt pool; progressively cooling the melt pool to bond the galvanized components together as the non-contact weld energy is applied thereto; and advancing the high density energy beam in a weave pattern and selecting the weave pattern to have a weave to weave distance which is less than the width of the weave pattern.
Claim 18
Dependent Claim
139 words
In a method for joining galvanized components having a coating with a vapor pressure greater than the vapor pressure of the coated material by use of energy which forms a molten pool between the components cooled to join the components the improvement comprising: positioning the galvanized components in a preselected lapped joint relationship to define a vapor pressure relief path; applying a high density energy beam of non-contact weld energy to the positioned galvanized components to progressively melt each of the components to form a melt pool; progressively cooling the melt pool to bond the galvanized components together as the non-contact weld energy is applied thereto; and advancing the high density energy beam in a weave pattern and selecting the weave pattern to have a weave to weave distance which is less than the width of the weave pattern.
Claim 19
Dependent Claim
25 words
In the method of claim 10, selecting a weave pattern having a weave to weave distance of one mm and a width of 4 mm.
Claim 20
Dependent Claim
25 words
In the method of claim 12, selecting a weave pattern having a weave to weave distance of one mm and a width of 4 mm.
Claim 21
Dependent Claim
97 words
In a method for joining a plurality of components having a protective metallic coating which produces a high vapor pressure when melted by use of a high density energy beam, the improvement comprising: providing an edge on each of the coated components: juxtaposing the coated components to provide a lap joint between the edges thereon; impinging the high density energy beam against one of the components and advancing it along a curvilinear path which overlaps the lap joint to provide a weld zone between the coated components each having a vapor escape path at the lap joint.
Claim 22
Dependent Claim
97 words
In a method for joining a plurality of components having a protective metallic coating which produces a high vapor pressure when melted by use of a high density energy beam, the improvement comprising: providing an edge on each of the coated components: juxtaposing the coated components to provide a lap joint between the edges thereon; impinging the high density energy beam against one of the components and advancing it along a curvilinear path which overlaps the lap joint to provide a weld zone between the coated components each having a vapor escape path at the lap joint.
Claim 23
Dependent Claim
133 words
In a method for joining galvanized components having a coating which a vapor pressure greater than the vapor pressure of the coated material by use of energy which forms a molten pool between the components cooled to join the components the improvement comprising; providing each of the components in sheet form and coating each of said sheets with a zinc rich coating to a thickness in the range of 0.001 to 0.3 millimeters; positioning the galvanized components in a preselected relationship to define a vapor pressure relief path; applying a continuous stream of non-contact weld energy to the positioned galvanized components to progressively melt each of the components to form a melt pool; and progressively cooling the melt pool to bond the galvanized components together as the non-contact weld energy is applied thereto.
Claim 24
Dependent Claim
133 words
In a method for joining galvanized components having a coating which a vapor pressure greater than the vapor pressure of the coated material by use of energy which forms a molten pool between the components cooled to join the components the improvement comprising; providing each of the components in sheet form and coating each of said sheets with a zinc rich coating to a thickness in the range of 0.001 to 0.3 millimeters; positioning the galvanized components in a preselected relationship to define a vapor pressure relief path; applying a continuous stream of non-contact weld energy to the positioned galvanized components to progressively melt each of the components to form a melt pool; and progressively cooling the melt pool to bond the galvanized components together as the non-contact weld energy is applied thereto.
References Cited (Backward Citations)
EP0157913A1
Cited
US4745257A
Cited
JPS60255294A
Cited
JPS6127189A
Cited
US4682002A
Cited
FR2600923A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-10-09 | 1993-04-10 | 1993-10-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-10-09 | 1997-04-10 | 1997-10-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-10-09 | 2001-04-10 | 2001-10-10 | $7700.00 | Window Closed / Lapsed |