Resin composition of styrene resin and polyamide block copolymer
Assignee: Daicel Corp
•
Filing: 1987-09-04
•
Granted: 1989-10-03
•
Expires: 2007-09-04
Abstract
Abstract A resin composition suitable for injection molding, having excellent abrasion resistance, comprising (A) a thermoplastic injection moldable resin component containing a first thermoplastic injection moldable styrene-based resin and a second thermoplastic injection moldable resin different from said first resin and (B) a polyamide-based block copolymer.
Inventors
- 👤 Katuyoshi Murabayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 02:22
CPC Classifications
C; C08; C08L; C08L25/00; C08L25/02; C08L25/04; C08L25/08; C08L71/00; C08L71/08; C08L71/10; C08L71/12; C08L71/123; C08L25/06; C08L67/00; C08L75/00; C08L81/00; Y; Y10; Y10S; Y10S525/00; Y10S525/905
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
226 words
A resin composition suitable for injection molding, comprising: (1) 100 parts by weight of a thermoplastic injection moldable resin component consisting of (a) a first thermoplastic injection moldable resin selected from the group consisting of rubber-modified polystyrene, a copolymer consisting essentially of styrene and an unsaturated monomer copolymerizable with styrene, a copolymer consisting essentially of styrene, acrylonitrile and an unsaturated monomer copolymerizable with styrene, and a copolymer consisting essentially of acrylonitrile, butadiene, styrene and an unsaturated monomer copolymerizable with styrene, said unsaturated monomer copolymerizable with styrene being selected from the group consisting of α-methyl styrene, acrylate esters, methacrylate esters, unsaturated dicarboxylic acids and anhydrides thereof, and (b) up to 50 percent by weight of a second thermoplastic injection moldable resin different from said first resin, and (2) 0.01 to 50 parts by weight of a polyamide block copolymer consisting essentially of (a) 10 to 99 percent by weight of polyamide blocks prepared by polymerizing amino carboxylic acids having 6 to 12 carbon atoms, lactams having 6 to 12 carbon atoms, nylon salts prepared from diamines having from 6 to 12 carbon atoms and dicarboxylic acids having from 6 to 12 carbon atoms, and the balance is (b) (1) polyester blocks or (2) polyol blocks linked to said polyamide blocks by ester bonds, wherein said second thermoplastic injection moldable resin is different from said polyamide block copolymer.
Claim 2
Dependent Claim
226 words
A resin composition suitable for injection molding, comprising: (1) 100 parts by weight of a thermoplastic injection moldable resin component consisting of (a) a first thermoplastic injection moldable resin selected from the group consisting of rubber-modified polystyrene, a copolymer consisting essentially of styrene and an unsaturated monomer copolymerizable with styrene, a copolymer consisting essentially of styrene, acrylonitrile and an unsaturated monomer copolymerizable with styrene, and a copolymer consisting essentially of acrylonitrile, butadiene, styrene and an unsaturated monomer copolymerizable with styrene, said unsaturated monomer copolymerizable with styrene being selected from the group consisting of α-methyl styrene, acrylate esters, methacrylate esters, unsaturated dicarboxylic acids and anhydrides thereof, and (b) up to 50 percent by weight of a second thermoplastic injection moldable resin different from said first resin, and (2) 0.01 to 50 parts by weight of a polyamide block copolymer consisting essentially of (a) 10 to 99 percent by weight of polyamide blocks prepared by polymerizing amino carboxylic acids having 6 to 12 carbon atoms, lactams having 6 to 12 carbon atoms, nylon salts prepared from diamines having from 6 to 12 carbon atoms and dicarboxylic acids having from 6 to 12 carbon atoms, and the balance is (b) (1) polyester blocks or (2) polyol blocks linked to said polyamide blocks by ester bonds, wherein said second thermoplastic injection moldable resin is different from said polyamide block copolymer.
Claim 3
Dependent Claim
27 words
A resin composition as claimed in claim 1, wherein said second resin is selected from the group consisting of: polycarbonate resin, vinyl chloride resin and polyolefin resin.
Claim 4
Dependent Claim
68 words
A resin composition as claimed in claim 1, wherein said aminocarboxylic acids are selected from the group consisting of: ω-aminocaproic acid, ω-aminoenanthic acid, ω-aminocaprylic acid, ω-aminopelargonic acid, ω-aminocapric acid, 11-aminoundecanoic acid and 12-aminododecanoic acid, said lactams are selected from the group consisting of: caprolactam and laurolactam, and said nylon salts are selected from the group consisting of nylons 6/6, 6/10, 6/12, 11/6, 11/10, 11/12, 12/6, 12/10 and 12/12.
Claim 5
Dependent Claim
165 words
A resin composition as claimed in claim 1, wherein said polyester blocks are (a) polyesters prepared from diacids and diols, said diacids being selected from the group consisting of phthalic acid, isophthalic acid, terephthalic acid, naphthalene-2,6-dicarboxylic acid, naphthalene-2,7-dicarboxylic acid, diphenyl-4,4'-dicarboxylic acid, diphenoxyethanedicarboxylic acid, 1,4-cyclohexanedicarboxylic acid, 1,2-cyclohexanedicarboxylic acid, dicyclohexyl-4,4'-dicarboxylic acid, succinic acid, oxalic acid, adipic acid, sebacic acid, and dodecanedioic acid, and said diols being selected from the group consisting of: ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, propylene glycol, 1,4-butanediol, 1,3-butanediol, neopentyl glycol, 1,5-pentanediol, 1,6-hexanediol, polyethylene glycol, polypropylene glycol, and polytetramethylene glycol, or (b) polycaprolactone-polyesters being prepared from members of the group consisting of ε-caprolactone, ω-hydroxycaproic acid and C 1 -C 3 alkyl esters thereof, and said polyol blocks being selected from the group consisting of polyols of a number-average molecular weight of 500-3000, comprising polyethylene glycol, poly(1,2-propylene oxide)glycol, poly(1,3-propylene oxide)glycol, poly(tetramethylene oxide)glycol, poly(hexamethylene oxide)glycol, ethylene oxide/propylene oxide block copolymers, ethylene oxide/propylene oxide random copolymers, ethylene oxide/tetrahydrofuran block copolymers and ethylene oxide/tetrahydrofuran random copolymers.
Claim 6
Dependent Claim
25 words
A resin composition as claimed in claim 1 in which the amount of said polyamide block copolymer is from 0.1 to 30 parts by weight.
Claim 7
Dependent Claim
25 words
A resin composition as claimed in claim 1 in which the amount of said polyamide block copolymer is from 0.5 to 15 parts by weight.
Claim 8
Dependent Claim
25 words
A resin composition as claimed in claim 5 in which said polyamide block copolymer contains 20 to 90 percent by weight of said polyamide blocks.
Claim 9
Dependent Claim
25 words
A resin composition as claimed in claim 6 in which said polyamide block copolymer contains 30 to 80 percent by weight of said polyamide blocks.
Claim 10
Dependent Claim
16 words
A resin composition as claimed in claim 1, consisting of a mixture of (1) and (2).
Claim 11
Dependent Claim
16 words
A resin composition as claimed in claim 1 in which said first resin is rubber-modified polystyrene.
Claim 12
Dependent Claim
16 words
An article which has been obtained by injection-moulding the resin composition as defined in claim 1.
Claim 13
Dependent Claim
24 words
A resin composition as claimed in claim 1, in which said polyamide block copolymer comprises (a) a polyamide block and (b) a polyester block.
Claim 14
Dependent Claim
36 words
A resin composition as claimed in claim 1, in which said polyamide block copolymer comprises (a) a polyamide block and (c) a polyol block, both blocks having been linked with each other by an ester group.
References Cited (Backward Citations)
US4716198A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-10-02 | 1993-04-03 | 1993-10-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-10-02 | 1997-04-03 | 1997-10-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-10-02 | 2001-04-03 | 2001-10-03 | $7700.00 | Window Closed / Lapsed |