Flame-retardant composition and flame-retardant cable using same
Assignee: Fujikura Ltd
•
Filing: 1987-03-11
•
Granted: 1989-09-26
•
Expires: 2007-03-11
Abstract
Abstract A flame-retardant composition is prepared by mixing 100 parts by weight of a rubber or plastics free from any halogen with about 50 to about 200 parts by weight of magnesium hydroxide having an average particle diameter of about 0.3 to about 2 μm and about 5 to about 50 parts by weight of carbon black powder having an oil absorption of about 0.5 to about 2.0 ml/g, and then cross-linking the mixture with an organic peroxide, sulfur, or a sulfur compound as a vulcanizing agent. By forming an electrical insulation and/or a sheath of the flame-retardant composition, there is provided a flame-retardant cable of the type including a cable core composed of an electric conductor coated with the electrical insulation or a plurality of such cores twisted together and covered, together with a filler, with the sheath. The flame-retardant composition and the flame-retardant cable using this composition possess high flame resistance while possessing acceptable mechanical properties and will not evolve any hydrogen halide or other noxious gas if burnt. With less smoke emission than conventional cables on fire, the composition and the cable are less hazardous.
Inventors
- 👤 Masatake Hasegawa
- 👤 Hirotada Kobayashi
- 👤 Hideo Sunazuka
- 👤 Akira Yoshino
- 👤 Takao Matsuda
- 👤 Yoshioki Shingo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 19:03
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/18; H01B3/20; H01B3/24; H01B3/30; H01B3/44; C; C08; C08K; C08K3/00; C08K3/02; C08K3/04; C08K3/18; C08K3/20; C08K3/22; H01B7/00; H01B7/17; H01B7/29; H01B7/295; Y; Y10; Y10S; Y10S260/00; Y10S260/24; Y10S428/00; Y10S428/92; Y10S428/921; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/294; Y10T428/2942; Y10T428/2949; Y10T428/296; Y10T428/2962
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
148 words
In a flame-retarding cable of the type which includes a cable core composed of an electric conductor coated with electrical insulation or a plurality of such cores twisted together and covered, together with a filler, with a sheath, wherein the improvement comprises in that said insulation or said sheath, or both, are made of a flame-retardant composition obtained by preparing a mixture by mixing (i) 100 parts by weight of a halogen-free rubber or a halogen-free plastic with (ii) about 50 to about 200 parts by weight of magnesium hydroxide having an average particle diameter of about 0.3 to about 2 μm and (iii) about 5 to about 50 parts by weight of carbon black powder having an oil absorption of about 0.5 to about 2.0 ml g -1 , and then cross-linking said mixture with an organic peroxide, sulfur, or a sulfur compound as a vulcanizing agent.
Claim 2
Dependent Claim
148 words
In a flame-retarding cable of the type which includes a cable core composed of an electric conductor coated with electrical insulation or a plurality of such cores twisted together and covered, together with a filler, with a sheath, wherein the improvement comprises in that said insulation or said sheath, or both, are made of a flame-retardant composition obtained by preparing a mixture by mixing (i) 100 parts by weight of a halogen-free rubber or a halogen-free plastic with (ii) about 50 to about 200 parts by weight of magnesium hydroxide having an average particle diameter of about 0.3 to about 2 μm and (iii) about 5 to about 50 parts by weight of carbon black powder having an oil absorption of about 0.5 to about 2.0 ml g -1 , and then cross-linking said mixture with an organic peroxide, sulfur, or a sulfur compound as a vulcanizing agent.
Claim 3
Dependent Claim
38 words
A flame-retardant cable as recited in claim 1, wherein the filler interposed between the core or twisted cores and the sheath comprises a flame-retardant composition free from any halogen and having an oxygen index of at least 30.
Claim 4
Dependent Claim
45 words
A flame-retardant cable as recited in claim 1, which further comprises a flame retardant containing red phosphorus in an amount such that the red phosphorus makes up about 2 to about 15 parts by weight per 100 parts by weight of the rubber or plastics.
Claim 5
Dependent Claim
38 words
A flame-retardant cable as recited in claim 3, wherein the filler interposed between the core or twisted cores and the sheath comprises a flame-retardant composition free from any halogen and having an oxygen index of at least 30.
Claim 6
Dependent Claim
87 words
A flame-retardant cable as recited in claim 1 or 7, wherein the mixture contains about 3 to about 10 parts by weight each of an organopolysiloxane and a basic lead compound of the formula xPbO.Pb(R).yH 2 O, in which 0≦x≦3, R is a higher fatty acid group, an aromatic carboxylic acid group or a sulfuric acid group, the higher fatty acid group and the aromatic carboxylic acid group each having 6 or more carbon atoms, and 0≦y≦10, per 100 parts by weight of the rubber or plastics.
Claim 7
Dependent Claim
38 words
A flame-retardant cable as recited in claim 5, wherein the filler interposed between the core or twisted cores and the sheath comprises a flame-retardant composition free from any halogen and having an oxygen index of at least 30.
Claim 8
Dependent Claim
21 words
A flame-retardant cable as recited in claim 1 or 6, wherein the magnesium hydroxide is surface-treated with stearic or oleic acid.
Claim 9
Dependent Claim
38 words
A flame-retardant cable as recited in claim 7, wherein the filler interposed between the core or twisted cores and the sheath comprises a flame-retardant composition free from any halogen and having an oxygen index of at least 30.
References Cited (Backward Citations)
GB1479083A
Cited
US4209566A
Cited
US4396730A
Cited
US4430470A
Cited
US4505850A
Cited
JPS59170176A
Cited
US4549041A
Cited
US4722959A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-09-25 | 1993-03-27 | 1993-09-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-09-25 | 1997-03-27 | 1997-09-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-09-25 | 2001-03-27 | 2001-09-26 | $7700.00 | Window Closed / Lapsed |