US4868230A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Cationic, advanced epoxy resins from (1) diglycidyl ethers of phenols (2) diglycidyl ethers of alkane diols and (3) a dihydric phenol
Assignee: Dow Chemical Co
•
Filing: 1987-07-02
•
Granted: 1989-09-19
•
Expires: 2007-07-02
Abstract
Abstract A method for preparing an advanced epoxy cationic resin from an epoxy-based resin containing oxirane groups by converting at least some of the oxirane groups to cationic groups, wherein the improvement is using as the epoxy-based resin an advanced epoxy resin obtained by reacting in the presence of a suitable catalyst (1) a diglycidylether of an aliphatic diol which is essentially free of ether oxygen atoms, such as a diglycidyl ether of 1,4-butanediol, (2) a diglycidylether of a dihydric phenol, for example a diglycidyl ether of bisphenol A and (3) a dihydric phenol such as bisphenol A and optionally a capping agent such as p-nonylphenol. Coating compositions suitable for electrodeposition are prepared from the product obtained by the process.
Inventors
- 👤 Nancy A. Rao
- 👤 Richard A. Hickner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 18:31
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/02; C08G59/04; C08G59/06; C08G59/066; C09; C09D; C09D5/00; C09D5/44; C09D5/4419; C09D5/443
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
221 words
The product resulting from a process for the preparation of an advanced epoxy cationic resin from an epoxy resin composition having terminal oxirane groups which includes the step of converting oxirane groups to cationic groups by reacting a nucleophile with at least some of the oxirane groups of the epoxy resin composition wherein an organic acid and water are added during some part of this conversion; wherein the advanced epoxy resin is obtained by reacting in the presence of a suitable catalyst (A) a composition comprising (1) at least one diglycidyl ether of an aliphatic diol which diol is essentially free of ether oxygen atoms; and (2) a diglycidyl ether of a dihydric phenol; with (B) at least one dihydric phenol wherein components (A-1) and (A-2) are employed in such quantities that about 10 to about 75 weight percent of the glycidyl ethers contained in component (A) are contributed by (A-1) and from about 25 weight percent to about 90 weight percent of the glycidyl ethers are contributed by (A-2) and wherein components (A) and (B) are employed in such quantities that the resultant epoxide equivalent weight is from about 350 to about 10,000; whereby there is obtained a cationic, advanced epoxy resin having a charge density of from about 0.2 to about 0.6 milliequivalent of charge per gram of resin.
Claim 2
Dependent Claim
221 words
The product resulting from a process for the preparation of an advanced epoxy cationic resin from an epoxy resin composition having terminal oxirane groups which includes the step of converting oxirane groups to cationic groups by reacting a nucleophile with at least some of the oxirane groups of the epoxy resin composition wherein an organic acid and water are added during some part of this conversion; wherein the advanced epoxy resin is obtained by reacting in the presence of a suitable catalyst (A) a composition comprising (1) at least one diglycidyl ether of an aliphatic diol which diol is essentially free of ether oxygen atoms; and (2) a diglycidyl ether of a dihydric phenol; with (B) at least one dihydric phenol wherein components (A-1) and (A-2) are employed in such quantities that about 10 to about 75 weight percent of the glycidyl ethers contained in component (A) are contributed by (A-1) and from about 25 weight percent to about 90 weight percent of the glycidyl ethers are contributed by (A-2) and wherein components (A) and (B) are employed in such quantities that the resultant epoxide equivalent weight is from about 350 to about 10,000; whereby there is obtained a cationic, advanced epoxy resin having a charge density of from about 0.2 to about 0.6 milliequivalent of charge per gram of resin.
Claim 3
Dependent Claim
35 words
The product of claim 1 in which the amount of diglycidyl ether of an aliphatic diol which is essentially free of ether oxygen atoms is from about 10 weight percent to about 50 weight percent.
Claim 4
Dependent Claim
35 words
The product of claim 2 in which the amount of diglycidyl ether of an aliphatic diol which is essentially free of ether oxygen atoms is from about 15 weight percent to about 35 weight percent.
Claim 5
Dependent Claim
126 words
The product of claim 3 in which the diglycidyl ether of an aliphatic diol which is essentially free of ether oxygen atoms has the approximate formula ##STR8## wherein each R is independently hydrogen or a hydrocarbyl group having from 1 to 3 carbon atoms; Z is a divalent aliphatic or cycloaliphatic group having from 2 to about 20 carbon atoms, or one of the groups represented by the formulas ##STR9## wherein A' is a divalent hydrocarbon group having from 1 to about 6 carbon atoms; each R' is independently hydrogen, or a hydrocarbyl or hydrocarbyloxy group having from 1 to 4 carbon atoms; each R" is an aliphatic group having from 1 to about 6 carbon atoms; and n has a value of zero or 1.
Claim 6
Dependent Claim
23 words
The product of claim 4 in which the epoxide equivalent weight of the advanced epoxy resin is from about 600 to about 3,000.
Claim 7
Dependent Claim
67 words
The product of claim 5 in which the diglycidyl ether of dihydric phenol has the formula ##STR10## wherein each R independently is hydrogen or a hydrocarbyl group having from 1 to 3 carbon atoms, each R' independently is hydrogen, or a hydrocarbyl or a hydrocarbyloxy group having from 1 to about 4 carbon atoms or a halogen and n' has a value from zero to about 10.
Claim 8
Dependent Claim
95 words
The product of claim 5 in which the diglycidyl ether of a dihydric phenol has the formula ##STR11## wherein A is a divalent hydrocarbon group having from 1 to 12 carbon atoms; --S--, --S--S--, --SO--, --SO 2 --, --CO--, --O--CO--O--, or --O--; each R' is independently hydrogen, or a hydrocarbyl or hydrocarbyloxy group having from 1 to 4 carbon atoms, or a halogen; R is independently hydrogen or a hydrocarbyl group having from 1 to 3 carbon atoms; n has a value from zero to 1; and n' has a value from zero to 10.
Claim 9
Dependent Claim
16 words
The product of claim 6 in which n' has a value from 0.1 to about 5.
Claim 10
Dependent Claim
16 words
The product of claim 7 in which n' has a value from 0.1 to about 5.
Claim 11
Dependent Claim
49 words
The product of claim 8 in which the amount of component (A) is from about 60 percent to about 90 percent and the amount of component (B) is from about 40 percent to about 10 percent, the percentage being based on the total weight of components (A) and (B).
Claim 12
Dependent Claim
49 words
The product of claim 9 in which the amount of component (A) is from about 60 percent to about 90 percent and the amount of component (B) is from about 40 percent to about 10 percent, the percentage being based on the total weight of components (A) and (B).
Claim 13
Dependent Claim
36 words
The product of claim 10 wherein the advanced epoxy resin, before conversion to a cationic resin, has an oxirane content of from about 1 to about 5 percent based on the total weight of the resin.
Claim 14
Dependent Claim
36 words
The product of claim 12 wherein the advanced epoxy resin, before conversion to a cationic resin, has an oxirane content of from about 2 percent to about 4 percent, based on the total weight of resin.
Claim 15
Dependent Claim
36 words
The product of claim 9 wherein the advanced epoxy resin, before conversion to a cationic resin, has an oxirane content of from about 1 to about 5 percent based on the total weight of the resin.
Claim 16
Dependent Claim
36 words
The product of claim 14 wherein the advanced epoxy resin, before conversion to a cationic resin, has an oxirane content of from about 2 percent to about 4 percent, based on the total weight of resin.
Claim 17
Dependent Claim
19 words
The product of claim 12 in which a capping agent, component (C), is combined with components (A) and (B).
Claim 18
Dependent Claim
29 words
The product of claim 16 in which the amount of capping agent is from about 1 percent to about 15 percent based on the total weight of diglycidyl ethers.
Claim 19
Dependent Claim
14 words
The product of claim 17 in which the capping agent is a monofunctional phenol.
Claim 20
Dependent Claim
19 words
The product of claim 14 in which a capping agent, component (C), is combined with components (A) and (B).
Claim 21
Dependent Claim
29 words
The product of claim 17 in which the amount of capping agent is from about 1 percent to about 15 percent based on the total weight of diglycidyl ethers.
Claim 22
Dependent Claim
14 words
The product of claim 20 in which the capping agent is a monofunctional phenol.
Claim 23
Dependent Claim
57 words
A coating composition suitable for electrodeposition comprising an aqueous dispersion of the product of claim 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20 or 21 in combination with a curing agent selected from a blocked polyisocyanate, an amine aldehyde resin, and a phenol aldehyde resin.
Claim 24
Dependent Claim
15 words
The coating composition of claim 22 in which the curing agent is a blocked polyisocyanate.
Claim 25
Dependent Claim
15 words
The coating composition of claim 23 in which the blocked polyisocyanate is a ketoxime-blocked polyisocyanate.
Claim 26
Dependent Claim
11 words
The coating composition of claim 22 which also contains a pigment.
Claim 27
Dependent Claim
11 words
The coating composition of claim 23 which also contains a pigment.
Claim 28
Dependent Claim
11 words
The coating composition of claim 24 which also contains a pigment.
References Cited (Backward Citations)
US3839252A
Cited
US3984299A
Cited
US3947339A
Cited
US3936405A
Cited
US4101486A
Cited
US4432850A
Cited
US4419467A
Cited
US4515911A
Cited
US4575523A
Cited
US4612338A
Cited
EP0199663A1
Cited
US4698141A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-09-18 | 1993-03-20 | 1993-09-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-09-18 | 1997-03-20 | 1997-09-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-09-18 | 2001-03-20 | 2001-09-19 | $7700.00 | Window Closed / Lapsed |