US4868149A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Palladium-containing catalyst for treatment of automotive exhaust and method of manufacturing the catalyst
Assignee: Umicore Autocat USA Inc
•
Filing: 1988-05-23
•
Granted: 1989-09-19
•
Expires: 2008-05-23
Abstract
Abstract This application relates to a catalyst for treating automotive exhaust. The catalyst comprises a honeycomb carrier having deposited thereon a layer of alumina which has dispersed thereof lanthanum oxide, cerium oxide, palladium oxide and rhodium metal. The lanthanum oxide is present as crystallites that are less than about 25 Angstroms in size. The cerium oxide contains 3% lanthanum in the cerium oxide crystal lattice and the palladium oxide is present as crystallites which are less than about 25 Angstroms in size. A method of manufacturing the catalyst and process for using the catalyst are also disclosed and claimed.
Inventors
- 👤 Maureen L. Bricker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 08:19
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/34; B01D53/92; B01D53/94; B01D53/9445; B01D53/945; B01J; B01J23/00; B01J23/38; B01J23/54; B01J23/56; B01J23/63; B01J35/00; B01J35/30; B01J35/391; B01J35/393; B01J35/40; B01J35/45; B01J35/70; B01J35/77; B01D2255/00; B01D2255/20; B01D2255/206; B01J2235/00; B01J2235/15; B01J2235/30; B01J35/60; B01J35/61; B01J35/613; B01J35/615; B01J35/63; B01J35/633; B01J35/635; Y; Y02; Y02T; Y02T10/00; Y02T10/10; Y02T10/12
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
79 words
A thermally durable catalyst for treating automotive exhaust comprising a metallic or ceramic honeycomb carrier having deposited thereon a layer of a high surface area alumina, the alumina having dispersed thereon lanthanum oxide present as crystallites of less than about 25 Angstroms, cerium oxide, characterized in that at least 3% of the cerium in the cerium oxide crystal lattice is replaced by lanthanum, palladium oxide in the form of crystallites less than 25 Angstroms in size and rhodium oxide.
Claim 2
Dependent Claim
79 words
A thermally durable catalyst for treating automotive exhaust comprising a metallic or ceramic honeycomb carrier having deposited thereon a layer of a high surface area alumina, the alumina having dispersed thereon lanthanum oxide present as crystallites of less than about 25 Angstroms, cerium oxide, characterized in that at least 3% of the cerium in the cerium oxide crystal lattice is replaced by lanthanum, palladium oxide in the form of crystallites less than 25 Angstroms in size and rhodium oxide.
Claim 3
Dependent Claim
34 words
The catalyst of claim 1 wherein the alumina has a surface area from about 75 to about 200 m 2 /g and a pore volume from about 0.25 to about 0.8 cm 3 /g.
Claim 4
Dependent Claim
28 words
The catalyst of claim 1 wherein the alumina is present in an amount from about 90 to about 170 g of alumina per liter of volume of carrier.
Claim 5
Dependent Claim
25 words
The catalyst of claim 1 where the cerium oxide is present in an amount from about 5 to about 50 weight percent of the alumina.
Claim 6
Dependent Claim
25 words
The catalyst of claim 1 where the lanthanum oxide is present in an amount from about 3 to about 22 weight percent of the alumina.
Claim 7
Dependent Claim
25 words
The catalyst of claim 1 where the palladium oxide is present in an amount from about 0.1 to about 9 weight percent of the alumina.
Claim 8
Dependent Claim
24 words
The catalyst of claim 1 wherein the rhodium is present in an amount from about 0.01 to about 4 weight percent of the alumina.
Claim 9
Independent Claim
129 words
A method of manufacturing a catalyst for treating an automotive exhaust comprising: (a) coating a metallic or ceramic honeycomb carrier with a slurry of a high surface area alumina having dispersed thereon cerium oxide and calcining to give a first coated honeycomb carrier; (b) impregnating the calcined first coated honeycomb carrier with a solution of a lanthanum salt, and calcining to give a calcined second coated honeycomb carrier; and (c) impregnating the calcined second coated honeycomb carrier with a solution containing a palladium and a rhodium compound, and calcining to give a finished catalyst, and recovering the finished catalyst having palladium and lanthanum in the form of crystallites less than about 25 Angstroms and at least 3% of the cerium in the crystal lattice is replaced by lanthanum oxide.
Claim 10
Independent Claim
129 words
A method of manufacturing a catalyst for treating an automotive exhaust comprising: (a) coating a metallic or ceramic honeycomb carrier with a slurry of a high surface area alumina having dispersed thereon cerium oxide and calcining to give a first coated honeycomb carrier; (b) impregnating the calcined first coated honeycomb carrier with a solution of a lanthanum salt, and calcining to give a calcined second coated honeycomb carrier; and (c) impregnating the calcined second coated honeycomb carrier with a solution containing a palladium and a rhodium compound, and calcining to give a finished catalyst, and recovering the finished catalyst having palladium and lanthanum in the form of crystallites less than about 25 Angstroms and at least 3% of the cerium in the crystal lattice is replaced by lanthanum oxide.
Claim 11
Dependent Claim
34 words
The method of claim 8 where the alumina has a surface area from about 75 to about 200 m 2 /g, and a pore volume from about 0.25 to about 0.8 cm 3 /g.
Claim 12
Dependent Claim
28 words
The method of claim 8 where the alumina is present in an amount from about 90 to about 170 g of alumina per liter of volume of carrier.
Claim 13
Dependent Claim
25 words
The method of claim 8 where the cerium oxide is present in an amount from about 5 to about 50 weight percent of the alumina.
Claim 14
Dependent Claim
25 words
The method of claim 8 where the lanthanum oxide is present in an amount from about 3 to about 22 weight percent of the alumina.
Claim 15
Dependent Claim
25 words
The method of claim 8 where the palladium oxide is present in an amount from about 0.1 to about 9 weight percent of the alumina.
Claim 16
Dependent Claim
24 words
The method of claim 8 where the rhodium is present in an amount from about 0.01 to about 4 weight percent of the alumina.
References Cited (Backward Citations)
US3767453A
Cited
US3785998A
Cited
US4170573A
Cited
US4528279A
Cited
US4619909A
Cited
US4727052A
Cited
US4791091A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-09-18 | 1993-03-20 | 1993-09-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-09-18 | 1997-03-20 | 1997-09-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-09-18 | 2001-03-20 | 2001-09-19 | $7700.00 | Window Closed / Lapsed |