Glassfiber reinforced fluorocarbon polymer coating composition for metal surfaces, process of preparing the same, and metal sheets coated with such coating composition
Assignee: DAINPPON INK & CHEMICALS Inc 3-35-58 SAKASHITA ITABASHI-KU TOKYO JAPAN
•
Filing: 1987-10-20
•
Granted: 1989-09-05
•
Expires: 2007-10-20
Abstract
Abstract A novel fluorocarbon polymer coating composition in which glass fibers are successfully dispersed to add enhanced scratch and wear resistances to the superior properties inherent to the fluorocarbon polymer. The glass fibers are firstly sized with a solution of a titanate coupling agent and subsequently sized with a solution of a silane coupling agent. With this composite sizing treatment, the glass fibers can have greatly improved wettability or compatibility with the fluorocarbon polymer coating composition so that they can be substantially randomly dispersed in the coating composition, whereby the fluorocarbon polymer coating can have the combined superior properties resulting from the use of the fluorocarbon polymer and the incorporation of the glass fibers.
Inventors
- 👤 Haruki Fujii
- 👤 Isao Miyawaki
- 👤 Motoomi Sakai
- 👤 Fumio Kanazawa
- 👤 Tadahiko Watanabe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:51
CPC Classifications
B; B05; B05D; B05D5/00; B05D5/08; B05D5/083; C; C03; C03C; C03C25/00; C03C25/10; C03C25/24; C03C25/40; C08; C08J; C08J5/00; C08J5/04; C08J5/06; C08J5/08; C09; C09D; C09D127/00; C09D127/02; C09D127/12; C23; C23C; C23C28/00; B05D2202/00; B05D2504/00; B05D2601/00; B05D2601/20; B05D7/00; B05D7/50; B05D7/52; B05D7/54; C08J2327/00; C08J2327/02; C08J2327/12; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/252; Y10T428/31504; Y10T428/3154; Y10T428/31678; Y10T428/31692; Y10T428/31699
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
101 words
Metal sheet coated with fluorocarbon polymer coating comprising: a metal sheet formed with a prime coat of an epoxy resin; and an outer coat on said prime coat, said outer coat being formed from a fluorocarbon polymer coating composition in which glass fibers are dispersed substantially randomly therein, said coating composition consisting essentially of a solution of a fluorocarbon polymer, and said glass fibers being prepared through the process of firstly treating said glass fiber with a first sizing solution of a titanate coupling agent and subsequently treating thus-sized glass fibers with a second sizing solution of a silane coupling agent.
Claim 2
Dependent Claim
101 words
Metal sheet coated with fluorocarbon polymer coating comprising: a metal sheet formed with a prime coat of an epoxy resin; and an outer coat on said prime coat, said outer coat being formed from a fluorocarbon polymer coating composition in which glass fibers are dispersed substantially randomly therein, said coating composition consisting essentially of a solution of a fluorocarbon polymer, and said glass fibers being prepared through the process of firstly treating said glass fiber with a first sizing solution of a titanate coupling agent and subsequently treating thus-sized glass fibers with a second sizing solution of a silane coupling agent.
Claim 3
Dependent Claim
24 words
Metal sheet coated with fluorocarbon polymer coating composition as set forth in claim 1, wherein said metal plate is a zinc plated steel sheet.
Claim 4
Dependent Claim
22 words
Metal sheet coated with fluorocarbon polymer coating compound as set forth in claim 1, wherein said metal sheet is an aluminum sheet.
Claim 5
Dependent Claim
23 words
Metal sheet coated with fluorocarbon polymer coating compound as set forth in claim 1, wherein said metal sheet is a stainless steel sheet.
Claim 6
Dependent Claim
33 words
Metal sheet coated with fluorocarbon polymer coating compound as set forth in claim 1, wherein said glass fiber has a diameter of 1 to 30 μ and a length of 1 to 200μ.
Claim 7
Dependent Claim
38 words
Metal sheet coated with fluorocarbon polymer coating compound as set forth in claim 5, wherein 1 to 60 parts by weight of said glass fibers are incorporated into 100 parts of said coating composition forming said outer coat.
Claim 8
Dependent Claim
25 words
Metal sheet coated with fluorocarbon polymer coating composition as set forth in claim 1, wherein said metal plate is an aluminum-zinc alloy plated sheet steel.
Claim 9
Dependent Claim
48 words
A metal sheet coated with the fluorocarbon polymer coating compound as set forth in claim 7, wherein the metal sheet is treated with a primer solution containing 15 to 60% by weight of a chromate compound prior to coating the metal sheet with said fluorocarbon polymer coating compound.
Claim 10
Dependent Claim
65 words
Fluorocarbon polymer coating composition for metal surfaces comprising: a coating solution consisting essentially of a fluorocarbon polymer and glass fibers dispersed in said coating composition, said glass fibers being prepared through the process of firstly treating said glass fiber with a first sizing solution of a titanate coupling agent and subsequently treating thus-sized glass fibers with a second sizing solution of a silane coupling agent.
Claim 11
Dependent Claim
65 words
Fluorocarbon polymer coating composition for metal surfaces comprising: a coating solution consisting essentially of a fluorocarbon polymer and glass fibers dispersed in said coating composition, said glass fibers being prepared through the process of firstly treating said glass fiber with a first sizing solution of a titanate coupling agent and subsequently treating thus-sized glass fibers with a second sizing solution of a silane coupling agent.
Claim 12
Dependent Claim
29 words
Fluorocarbon polymer coating composition as set forth in claim 9, wherein said glass fiber has a diameter of 1 to 30 μ and a length of 1 to 200μ.
Claim 13
Dependent Claim
32 words
Fluorocarbon polymer coating compound as set forth in claim 1, wherein 1 to 60 parts by weight of said glass fibers are blended with 100 parts by weight of said coating composition.
Claim 14
Dependent Claim
17 words
Fluorocarbon polymer coating composition as set forth in claim 9, wherein said fluorocarbon polymer is polyvinylidene fluoride.
Claim 15
Dependent Claim
128 words
Process of preparing a glass fiber reinforced fluorocarbon polymer coating composition for metal surfaces comprising the steps of: immersing glass fibers in a first sizing solution of a titanate coupling agent and a solvent thereof and evaporating the solution in order to obtain the glass fibers of which surface are treated by the titanate-coupling agent; subsequently immersing thus sized glass fibers in a second sizing solution of a silane coupling agent and a solvent thereof and evaporating the solution in order to obtain the glass fibers of which surface are sized with the titanate and silane coupling agents; and dispersing the resulting glass fibers into a coating composition consisting essentially of a fluorocarbon polymer and a solvent thereof to obtain said glass fiber contained fluorocarbon polymer coating composition.
Claim 16
Dependent Claim
128 words
Process of preparing a glass fiber reinforced fluorocarbon polymer coating composition for metal surfaces comprising the steps of: immersing glass fibers in a first sizing solution of a titanate coupling agent and a solvent thereof and evaporating the solution in order to obtain the glass fibers of which surface are treated by the titanate-coupling agent; subsequently immersing thus sized glass fibers in a second sizing solution of a silane coupling agent and a solvent thereof and evaporating the solution in order to obtain the glass fibers of which surface are sized with the titanate and silane coupling agents; and dispersing the resulting glass fibers into a coating composition consisting essentially of a fluorocarbon polymer and a solvent thereof to obtain said glass fiber contained fluorocarbon polymer coating composition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-09-04 | 1993-03-06 | 1993-09-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-09-04 | 1997-03-06 | 1997-09-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-09-04 | 2001-03-06 | 2001-09-05 | $7700.00 | Window Closed / Lapsed |