Process for manufacturing architectural glass
Assignee: ML BURKE COMPANY A PROPRIETORSHIP OF CALIFORNIA
•
Filing: 1988-04-18
•
Granted: 1989-09-05
•
Expires: 2008-04-18
Abstract
Abstract A polyurethane filmed glass material for use as monolithic insulated glass or laminated glass in spandrel applications is provided. Polyurethane sheet which has been ultraviolet light stabilized is pigmented, coated or otherwise colored to produce a coloring which is predictable and reproducible. A coupling agent is employed and the polyurethane adheres directly to a glass sheet without glues or adhesives. The manufacture of the glass material includes laying a sheet of colored polyurethane sheet material on a sheet of glass which has been prepared with a coupling agent. Outside surfaces of the polyurethane are coated with a release material. The glass sheet and the prepared polyurethane sheet are then loaded into a vacuum bag which in turn is then loaded into an autoclave. The bag is subjected to a vacuum while the autoclave vessel is pressurized. The autoclave vessel is simultaneously run through a temperature curve to heat and cool the polyurethane and glass whereby the polyurethane is temporarily softened and thereby adheres to the glass. The lamininated product is thereafter tempered.
Inventors
- 👤 Gennaro J. Catalano
- 👤 Larry D. George
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 07:32
CPC Classifications
B; B32; B32B; B32B17/00; B32B17/06; B32B17/10; B32B17/10005; B32B17/10807; B32B17/10981; B29; B29C; B29C35/00; B29C35/02; B29C35/0227; B29C43/00; B29C43/02; B29C43/10; B29C43/12; B29C70/00; B29C70/68; B29C70/681; B29C70/683; B32B17/10009; B32B17/10018; B32B17/10036; B32B17/10165; B32B17/10174; B32B17/10339; B32B17/1055; B32B17/1077; B32B17/10816; B32B17/10825; B32B17/10834; B32B17/10844; B32B17/10853
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
301 words
A process for manufacturing opacified monolith and spandrel architectural glass comprising the steps of: a. obtaining a quantity of polyurethane opacified film, said film being in preformed condition at ambient temperature; b. obtaining a sheet of architectural plate glass, said plate glass being in preformed condition at ambient temperature; c. coating one surface of said plate glass with a coupling agent mixture containing a member of the organoester silane group; d. cutting said polyurethane film to a size to cover said coated surface of said plate glass; e. applying said cut polyurethane film piece to said coated surface of said plate glass to form a laminate; f. wrapping said laminate in a mold release perforated material; g. wrapping a resin absorbing breather material about the outside of said perforated release material and said laminate; h. wrapping said breather and release material wrapped laminate in a flexible blanket of non-gas permeable material; i. sealing the edges of said non-gas permeable material, to form a flexible vacuum bag; j. placing said laminate sealed vacuum bag in an autoclave; k. pressurizing said autoclave interior while evacuating said vacuum bag interior while heating said autoclave interior to a temperature to melt said polyurethane into a plastic state; and l. cooling down said autoclave with its interior pressurized to anneal said laminate; m. wherein said pressurizing while heating step includes heating from ambient to 260 degrees F. while increasing pressure to 180 psig, then holding at that temperature and pressure for about 25 minutes; n. wherein said cooling down step includes allowing said autoclave to cool to 120 degrees F. while maintaining said 180 psig pressure, then releasing said pressure when said 120 degrees F. temperature is reached, then allowing said autoclave to cool to 108 degrees F. and thereafter opening said autoclave to ambient conditions.
Claim 2
Dependent Claim
301 words
A process for manufacturing opacified monolith and spandrel architectural glass comprising the steps of: a. obtaining a quantity of polyurethane opacified film, said film being in preformed condition at ambient temperature; b. obtaining a sheet of architectural plate glass, said plate glass being in preformed condition at ambient temperature; c. coating one surface of said plate glass with a coupling agent mixture containing a member of the organoester silane group; d. cutting said polyurethane film to a size to cover said coated surface of said plate glass; e. applying said cut polyurethane film piece to said coated surface of said plate glass to form a laminate; f. wrapping said laminate in a mold release perforated material; g. wrapping a resin absorbing breather material about the outside of said perforated release material and said laminate; h. wrapping said breather and release material wrapped laminate in a flexible blanket of non-gas permeable material; i. sealing the edges of said non-gas permeable material, to form a flexible vacuum bag; j. placing said laminate sealed vacuum bag in an autoclave; k. pressurizing said autoclave interior while evacuating said vacuum bag interior while heating said autoclave interior to a temperature to melt said polyurethane into a plastic state; and l. cooling down said autoclave with its interior pressurized to anneal said laminate; m. wherein said pressurizing while heating step includes heating from ambient to 260 degrees F. while increasing pressure to 180 psig, then holding at that temperature and pressure for about 25 minutes; n. wherein said cooling down step includes allowing said autoclave to cool to 120 degrees F. while maintaining said 180 psig pressure, then releasing said pressure when said 120 degrees F. temperature is reached, then allowing said autoclave to cool to 108 degrees F. and thereafter opening said autoclave to ambient conditions.
Claim 3
Dependent Claim
41 words
The process of claim 1 wherein the step of obtaining polyurethane opacified film includes the step of: forming a polyurethane melt mix; coloring the polyurethane mix; and forming a sheet of said tinted polyurethane and curing said sheet into sheet film.
Claim 4
Dependent Claim
20 words
The process of claim 2 wherein the step of coloring the polyurethane mix includes tinting the polyurethane mix with dye.
Claim 5
Dependent Claim
20 words
The process of claim 2 wherein the step of coloring the polyurethane mix includes adding metallic aggregate to the polyurethane.
Claim 6
Dependent Claim
43 words
The process of claim 1 wherein the step of obtaining polyurethane opacified film includes the steps of: forming a sheet of said polyurethane and curing said sheet into sheet film; and depositing a layer of metal on one side of said sheet film.
Claim 7
Dependent Claim
22 words
The process of claim 14 wherein said metal deposited is from the following group: copper, stainless steel, silver, gold and tin oxide.
Claim 8
Dependent Claim
23 words
The process of claim 11 wherein said color provides light transmission from the following group: 8% transmission, 28% transmission, 44% transmission, and non-visionary.
Claim 9
Dependent Claim
24 words
The process of claim 14 wherein said metal deposit provides light transmission from the following group: 8% transmission, 14% transmission, 20% transmission, and non-visionary.
Claim 10
Dependent Claim
34 words
The process of claim 5 wherein the step of obtaining a sheet of architectural plate glass includes the steps of: cutting said plate glass to size; and washing and drying said cut plate glass.
Claim 11
Dependent Claim
26 words
The process of claim 1 wherein the coupling agent mixture contains 2% of said member of the organoester silane group and 98% isopropyl alcohol by volume.
Claim 12
Dependent Claim
31 words
The process of claim 10 wherein said autoclave pressurizing, evacuating, and heating step includes the step of simultaneously applying a vacuum of approximately 281/2 inches of water to said vacuum bag.
Claim 13
Dependent Claim
282 words
A process for manufacturing monolith and spandrel architectural glass laminate from preformed polyurethane sheet film and plate glass comprising the steps of: a. preparing one side of said plate glass by treating it with a coupling agent mixture containing a member of the organoester silane group; b. applying a sheet of said polyurethane film to said prepared plate glass side at ambient conditions to form a layer assembly; c. wrapping said layer assembly in a mold release material; d. wrapping a resin absorbing breather material about said mold release material to forma wrapped assembly; e. placing said wrapped assembly into a vacuum bag; f. placing said vacuum bag and contents into an autoclave wherein the following is conducted; and then g. first, heating said autoclave interior to about 260 degrees F.; h. second, applying a vacuum of about 281/2 inches of water to said vacuum bag while simultaneously pressurizing said autoclave to about 125 psig; i. third, maintaining those conditions of vacuum, pressure and temperature for about 15 minutes; j. fourth, reducing said autoclave temperature at a rate of one degree F. per minute for about the next 10 minutes following said 15 minute step to adjust to said autoclave temperature to about 250 degrees F.; k. fifth, reducing said autoclave temperature at a rate of four degrees F. per minute for about the next 7.5 minutes to adjust said autoclave temperature to about 220 degrees F. following said 10 minute step; l. sixth, allowing said autoclave to cool naturally to about 129 degrees F. following said 7.5 minute step; and m. seventh, removing said vacuum and said autoclave pressure and opening said autoclave following the reaching of 129 degrees F. temperature.
Claim 14
Dependent Claim
282 words
A process for manufacturing monolith and spandrel architectural glass laminate from preformed polyurethane sheet film and plate glass comprising the steps of: a. preparing one side of said plate glass by treating it with a coupling agent mixture containing a member of the organoester silane group; b. applying a sheet of said polyurethane film to said prepared plate glass side at ambient conditions to form a layer assembly; c. wrapping said layer assembly in a mold release material; d. wrapping a resin absorbing breather material about said mold release material to forma wrapped assembly; e. placing said wrapped assembly into a vacuum bag; f. placing said vacuum bag and contents into an autoclave wherein the following is conducted; and then g. first, heating said autoclave interior to about 260 degrees F.; h. second, applying a vacuum of about 281/2 inches of water to said vacuum bag while simultaneously pressurizing said autoclave to about 125 psig; i. third, maintaining those conditions of vacuum, pressure and temperature for about 15 minutes; j. fourth, reducing said autoclave temperature at a rate of one degree F. per minute for about the next 10 minutes following said 15 minute step to adjust to said autoclave temperature to about 250 degrees F.; k. fifth, reducing said autoclave temperature at a rate of four degrees F. per minute for about the next 7.5 minutes to adjust said autoclave temperature to about 220 degrees F. following said 10 minute step; l. sixth, allowing said autoclave to cool naturally to about 129 degrees F. following said 7.5 minute step; and m. seventh, removing said vacuum and said autoclave pressure and opening said autoclave following the reaching of 129 degrees F. temperature.
References Cited (Backward Citations)
US3547766A
Cited
US4232065A
Cited
US4362587A
Cited
JPS57199649A
Cited
US4622091A
Cited
US4642255A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-09-04 | 1993-03-06 | 1993-09-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-09-04 | 1997-03-06 | 1997-09-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-09-04 | 2001-03-06 | 2001-09-05 | $7700.00 | Window Closed / Lapsed |