Method of manufacturing shadow mask and apparatus
Assignee: Toshiba Corp
•
Filing: 1988-05-18
•
Granted: 1989-08-29
•
Expires: 2008-05-18
Abstract
Abstract A method of manufacturing a shadow mask, comprising the steps of forming a first resist pattern having a large number of openings on one major surface of a thin metal plate and a second resist pattern on the other major surface, the second resist pattern having a large number of openings with an opening size larger than that of the first resist pattern, etching the thin metal plate surface having the first resist pattern to form first recesses, removing the first resist pattern, forming an etching-resistive layer on the thin metal plate surface having the first recesses to fill the first recesses, etching the thin metal plate surface having the second resist pattern to form second recesses which have a size larger than that of the first recesses and communicate with the first recesses, treating and swelling the etching-resistive layer with an alkali solution, spraying warm water to the etching-resistive layer to remove the etching-resistive layer, and removing the second resist pattern.
Inventors
- 👤 Makoto Kudou
- 👤 Katsumi Ichikawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 03:39
CPC Classifications
H; H01; H01J; H01J9/00; H01J9/02; H01J9/14; G; G03; G03F; G03F7/00; G03F7/12; H01J9/142
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
157 words
A method of manufacturing a shadow mask, comprising the steps of: forming a first resist pattern having a large number of openings on one major surface of a thin metal plate and a second resist pattern on the other major surface, the second resist pattern having a large number of openings with an opening size different from that of the first resist pattern; etching the thin metal plate surface having the first resist pattern to form first recesses; removing the first resist pattern; forming an etching-resistive layer on the thin metal plate surface having the first recesses; etching the thin metal plate surface having the second resist pattern to form second recesses which have a size different from that of the first recesses and communicate with the first recesses; treating and swelling the etching-resistive layer with an alkali solution; spraying warm water to the etching-resistive layer to remove the etching-resistive layer; and removing the second resist pattern.
Claim 2
Independent Claim
157 words
A method of manufacturing a shadow mask, comprising the steps of: forming a first resist pattern having a large number of openings on one major surface of a thin metal plate and a second resist pattern on the other major surface, the second resist pattern having a large number of openings with an opening size different from that of the first resist pattern; etching the thin metal plate surface having the first resist pattern to form first recesses; removing the first resist pattern; forming an etching-resistive layer on the thin metal plate surface having the first recesses; etching the thin metal plate surface having the second resist pattern to form second recesses which have a size different from that of the first recesses and communicate with the first recesses; treating and swelling the etching-resistive layer with an alkali solution; spraying warm water to the etching-resistive layer to remove the etching-resistive layer; and removing the second resist pattern.
Claim 3
Dependent Claim
28 words
A method according to claim 1, wherein the etching-resistive layer is made of a material selected from the group consisting of epoxy resin, acrylic resin and a photoresist.
Claim 4
Dependent Claim
38 words
A method according to claim 1, wherein the alkali solution for swelling the etching-resistive layer is a solution selected from the group consisting of an NaOH solution, NaOH solution containing a surfactant, and NaOH solution containing an inhibitor.
Claim 5
Dependent Claim
22 words
A method according to claim 1, wherein a temperature of the alkali solution falls within a range of 80° to 110° C.
Claim 6
Dependent Claim
22 words
A method according to claim 1, wherein a temperature of the alkali solution falls within a range of 88° to 98° C.
Claim 7
Dependent Claim
26 words
A method according to claim 1, wherein a pressure of the alkali solution applied to the etching-resistive layer is not more than 1.5 kg/cm 2 .
Claim 8
Dependent Claim
29 words
A method according to claim 1 wherein a pressure of the alkali solution applied to the etching-resistive layer falls within a range of 0.5 to 1.0 kg/cm 2 .
Claim 9
Dependent Claim
27 words
A method according to claim 1, wherein a temperature of warm water for removing the etching resistive layer falls within a range of 20° to 70° C.
Claim 10
Dependent Claim
26 words
A method according to claim 1, wherein a temperature of warm water for removing the etching-resistive layer falls within a range of 30° to 50° C.
Claim 11
Dependent Claim
28 words
A method according to claim 1, wherein a pressure of warm water sprayed to the etching-resistive layer falls within a range of 0.5 to 3 kg/cm 2 .
Claim 12
Dependent Claim
28 words
A method according to claim 1, wherein a pressure of warm water sprayed to the etching-resistive layer falls within a range of 1.0 to 2.0 kg/cm 2 .
Claim 13
Dependent Claim
16 words
A method according to claim 1, wherein the first recess is smaller than the second recess.
Claim 14
Dependent Claim
29 words
A method according to claim 1, wherein swelling and removal of the etching-resistive layer are performed in a chamber independent of a chamber for removing the second resist pattern.
Claim 15
Dependent Claim
21 words
A method according to claim 1, wherein warm water is obliquely sprayed with respect to a surface of the etching-resistive layer.
Claim 16
Independent Claim
140 words
An apparatus for manufacturing a shadow mask, comprising: means for etching one major surface of a thin metal plate, the thin metal plate being prepared such that a first resist pattern having a large number of openings is formed on said one major surface and that a second resist pattern having a large number of openings with an opening size different from that of the first resist pattern is formed on the other major surface of the thin metal plate; means for etching said one major surface of the thin metal plate with the etched surface on which an etching-resistive layer is formed; means for treating the etching-resistive layer with an alkali solution to swell the etching-resistive layer; means for spraying warm water to the etching-resistive layer to remove the etching-resistive layer; and means for removing the second resist pattern.
Claim 17
Independent Claim
140 words
An apparatus for manufacturing a shadow mask, comprising: means for etching one major surface of a thin metal plate, the thin metal plate being prepared such that a first resist pattern having a large number of openings is formed on said one major surface and that a second resist pattern having a large number of openings with an opening size different from that of the first resist pattern is formed on the other major surface of the thin metal plate; means for etching said one major surface of the thin metal plate with the etched surface on which an etching-resistive layer is formed; means for treating the etching-resistive layer with an alkali solution to swell the etching-resistive layer; means for spraying warm water to the etching-resistive layer to remove the etching-resistive layer; and means for removing the second resist pattern.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-08-28 | 1993-02-27 | 1993-08-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-08-28 | 1997-02-27 | 1997-08-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-08-28 | 2001-02-27 | 2001-08-29 | $7700.00 | Window Closed / Lapsed |