Method for preparation of high temperature superconductors using trichloroacetates
Assignee: WR Grace and Co Conn
•
Filing: 1987-11-16
•
Granted: 1989-08-22
•
Expires: 2007-11-16
Abstract
Abstract Superior homogeneity in ceramic materials is achieved by forming an aqueous solution of trichloroacetates of certain metals, heating the solution to decompose the trichloroacetates to form carbonate precipitates, and recovering the carbonate precipitates. The latter can be calcined to form superconductors. For example, oxides, or carbonates of Y, Ba, and Cu are dissolved in aqueous trichloroacetic acid and the solution is heated to decompose trichloroacetate ions and to form mixed carbonates, which precipitate. The precipitate is recovered and calcined to form a superconducting material.
Inventors
- 👤 Jacob Block
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 04:35
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/80; H10N60/85; H10N60/855; H10N60/857; C; C01; C01G; C01G3/00; C01G3/006; C04; C04B; C04B35/00; C04B35/01; C04B35/45; C04B35/4504; C04B35/4508; H10N60/01; H10N60/0268; C01P; C01P2002/00; C01P2002/02; Y; Y10; Y10S; Y10S505/00; Y10S505/80; Y10S505/801; Y10S505/809; Y10S505/81
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
71 words
A composition consisting essentially of aqueous solution of L,M,A trichloracetates, substantially free from ions other than L,M,A, where L is at least one metal of the rare earth group, including scandium and yttrium; M is at least one metal of the group Ba, Ca, and Sr; and A is the proportions of L:M:A being such that the carbonate precipitate resulting on heating the solution is calcinable to yield a superconducting product.
Claim 2
Dependent Claim
71 words
A composition consisting essentially of aqueous solution of L,M,A trichloracetates, substantially free from ions other than L,M,A, where L is at least one metal of the rare earth group, including scandium and yttrium; M is at least one metal of the group Ba, Ca, and Sr; and A is the proportions of L:M:A being such that the carbonate precipitate resulting on heating the solution is calcinable to yield a superconducting product.
Claim 3
Dependent Claim
14 words
A composition according to claim 1 where L is Y, and M is Ba.
Claim 4
Dependent Claim
124 words
Method of preparing a slurry of L,M,A mixed carbonates substantially free of ions other than L.M.A carbonate, chloride, and water-generated ions comprising: (i) forming an aqueous solution of L,M,A tirchloroacetates by adding to an aqueous solution of trichloroacetic acid L,M and A as oxide, hydroxide, carbonate, or bicarbonate where L is at least one metal of the rate earth group, including scandium and yttrium; M is at least one metal of the group Ba, Ca, and Sr; and A is Cu, (ii) heating the said solution to form mixed L,M,A carbonate precipitate with evolution of carbon dioxide and chloroform; and (iii) recovering and drying the said precipitate, the proportions of L:M:A being such that the said precipitate is calcinable to yield a superconducting product.
Claim 5
Dependent Claim
124 words
Method of preparing a slurry of L,M,A mixed carbonates substantially free of ions other than L.M.A carbonate, chloride, and water-generated ions comprising: (i) forming an aqueous solution of L,M,A tirchloroacetates by adding to an aqueous solution of trichloroacetic acid L,M and A as oxide, hydroxide, carbonate, or bicarbonate where L is at least one metal of the rate earth group, including scandium and yttrium; M is at least one metal of the group Ba, Ca, and Sr; and A is Cu, (ii) heating the said solution to form mixed L,M,A carbonate precipitate with evolution of carbon dioxide and chloroform; and (iii) recovering and drying the said precipitate, the proportions of L:M:A being such that the said precipitate is calcinable to yield a superconducting product.
Claim 6
Dependent Claim
21 words
A method according to claim 3 wherein, following drying the precipitate, the precipitate is calcined to convert the carbonate to oxide.
Claim 7
Dependent Claim
54 words
A method according to claim 4 wherein the precipitate is calcined by heating it in a first step to about 850°-1,050° C. for about 1-10 hours and in a second step at about 400°-500° C. in a stream of air or oxygen for about 1-3 hours, followed by cooling, thereby forming a superconducting material.
Claim 8
Dependent Claim
40 words
A method according to claim 5 wherein the precipitate is calcined by heating in a first step to about 950° C. for about 1 hour; and in a second step at about 450° C. in oxygen for about 1 hour.
Claim 9
Dependent Claim
18 words
A method according to claim 3, 4, 5 or 6, wherein L is Y and M is Ba.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-08-21 | 1993-02-20 | 1993-08-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-08-21 | 1997-02-20 | 1997-08-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-08-21 | 2001-02-20 | 2001-08-22 | $7700.00 | Window Closed / Lapsed |