US4857624A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Phenolic-modified rosin ester printing inks
Assignee: Flint Ink Corp
•
Filing: 1988-05-27
•
Granted: 1989-08-15
•
Expires: 2008-05-27
Abstract
Abstract Improved phenolic-modified rosin ester resins are disclosed. The phenolic-modified rosin ester resins comprise the reaction product of substantially unsaturated rosins with a dienophile, a phenolic compound and a formaldehyde-containing compound, which product is then esterified. The resulting composition is useful in vehicles for publication gravure printing inks, as well as in the printing inks themselves. Printing inks fabricated in accordance with the invention employing these improved phenolic-modified rosin ester resins provide prints of superior quality.
Inventors
- 👤 Douglas S. DeBlasi
- 👤 John P. Walsh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 13:22
CPC Classifications
C; C08; C08G; C08G16/00; C08G16/02; C09; C09D; C09D11/00; C09D11/02; C09D11/10
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
124 words
A method for the production of compositions particularly suitable for use in gravure printing comprising the steps of: reacting a rosin with a sufficient amount of dienophile to produce a modified rosin, cooling the modified rosin to about 120°-140° C., adding sufficient amounts of a formaldehyde source and a phenolic compound in a ratio of about 0.25 to about 1.0 equivalents of formaldehyde per equivalent of phenol, to produce from about 0.05 to about 0.30 moles of an in situ phenolic per mole of rosin, refluxing the reaction mixture to form a phenolic resin, heating the phenolic resin for a sufficient time to cause self-condensation of the phenolic resin, and esterifying the phenolic resin with a polyfunctional hydroxy compound to produce a resin product.
Claim 2
Independent Claim
124 words
A method for the production of compositions particularly suitable for use in gravure printing comprising the steps of: reacting a rosin with a sufficient amount of dienophile to produce a modified rosin, cooling the modified rosin to about 120°-140° C., adding sufficient amounts of a formaldehyde source and a phenolic compound in a ratio of about 0.25 to about 1.0 equivalents of formaldehyde per equivalent of phenol, to produce from about 0.05 to about 0.30 moles of an in situ phenolic per mole of rosin, refluxing the reaction mixture to form a phenolic resin, heating the phenolic resin for a sufficient time to cause self-condensation of the phenolic resin, and esterifying the phenolic resin with a polyfunctional hydroxy compound to produce a resin product.
Claim 3
Dependent Claim
27 words
A method in accordance with claim 1 wherein said adding step further comprises adding a sufficient amount of an alkaline catalyst to enhance the phenolic resin-forming reaction.
Claim 4
Dependent Claim
43 words
A method in accordance with claim 1 wherein said refluxing step comprises heating to about 127° C.-133° C. for from about 1 hour 45 minutes to about 2 hours 15 minutes to maximize the reaction of the formaldehyde source and the phenolic compound.
Claim 5
Dependent Claim
22 words
A method in accordance with claim 1 wherein the equivalent ratio of formaldehyde to phenol is from about 0.6 to about 0.75.
Claim 6
Dependent Claim
26 words
A method in accordance with claim 4 wherein said reacting step comprises reacting 1 equivalent of rosin with about 0.3 to about 0.6 equivalents of dienophile.
Claim 7
Dependent Claim
30 words
A method in accordance with claim 1 wherein the dienophile is selected from the group consisting of fumaric acid, maleic acid, maleic anhydride, acrylic acid, methacrylic acid and itaconic acid.
Claim 8
Dependent Claim
38 words
A method in accordance with claim 1 wherein said reacting step further comprises heating the rosin and the dienophile uniformly for about 15 minutes to about 1 hour 45 minutes at about 217° C. to about 223° C.
Claim 9
Dependent Claim
68 words
A method in accordance with claim 7 wherein said esterifying step comprises adding the polyfunctional hydroxy compound gradually over a period of approximately one hour at 177° C.-183° C., heating uniformly to 257°-263° C., and holding the reaction mixture at 257° C.-263° C., for a sufficient time to produce an esterified phenolic resin having a Gardner viscosity greater than, or equal to M-N at 50% TNV in toluene.
Claim 10
Dependent Claim
50 words
A method in accordance with claim 8 wherein said esterifying step further comprises the step of heating the esterified phenolic resin of Gardner viscosity M-N at from about 248° C. to about 252° C. until the Gardner viscosity of the resin is at least W-X at 50% TNV in toluene.
Claim 11
Dependent Claim
27 words
A method in accordance with claim 9 wherein said esterifying step further comprises addition of a sufficient amount of an alkaline catalyst to enhance the esterification reaction.
Claim 12
Dependent Claim
36 words
A method in accordance with claim 1 wherein the amounts of formaldehyde source and phenolic compound are sufficient to produce from about 0.10 to about 0.20 moles of in situ phenolic per mole of rosin acid.
Claim 13
Dependent Claim
22 words
A method in accordance with claim 1 wherein the total hydroxyl to total carboxyl equivalent ratio is from about 1.05 to 1.15.
Claim 14
Dependent Claim
28 words
A method in accordance with claim 6 wherein the phenolic compound is selected from the group consisting of bisphenols, para-tertiary-alkyl phenols, phenol, cresol, para-octyl phenol and para-nonyl phenol.
Claim 15
Dependent Claim
25 words
A method in accordance with claim 13 wherein the dienophile comprises fumaric acid, the phenolic comprises bisphenol A and the polyfunctional hydroxyl compound comprises pentaerythritol.
Claim 16
Dependent Claim
40 words
A method in accordance with claim 1 further comprising the step of dissolving the esterified phenolic resin having a Gardner viscosity of W-X in at least one organic solvent to produce a resin solution useful as a printing ink vehicle.
Claim 17
Dependent Claim
28 words
A method in accordance with claim 1 further comprising the step of adding a sufficient amount of a pigment to produce a composition useful as a printing ink.
Claim 18
Dependent Claim
9 words
A product produced by the process of claim 1.
Claim 19
Dependent Claim
11 words
A printing ink vehicle produced by the process of claim 15.
Claim 20
Dependent Claim
10 words
A printing ink produced by the process of claim 16.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-08-14 | 1993-02-13 | 1993-08-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-08-14 | 1997-02-13 | 1997-08-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-08-14 | 2001-02-13 | 2001-08-15 | $7700.00 | Window Closed / Lapsed |