US4851150A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Drying control chemical additives for rapid production of large sol-gel derived silicon, boron and sodium containing monoliths
Assignee: GRYPHON VENTURES II LP
•
Filing: 1984-02-27
•
Granted: 1989-07-25
•
Expires: 2004-02-27
Abstract
Abstract Large sol-gel derived silicon-containing monoliths are prepared with the use of drying control chemical additives selected from the group consisting of glycerol, formamide, oxalic acid and acids of the formula CnH2(n-1)O2N to control the ultrastructure of the gel solid and pore phases. Gelation, aging, drying, and densification of the sol-gel derived monoliths may be performed rapidly in tens of hours instead of tens of days without cracking, final densification at temperature of 800 DEG C. to 1200 DEG C. or less being possible. The silicon-containing monolith comprises a ternary SiO2-B2O3-Na2O system.
Inventors
- 👤 Larry L. Hench
- 👤 Gerard F. Orcel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 13:32
CPC Classifications
C; C03; C03C; C03C1/00; C03C1/006; C03B; C03B19/00; C03B19/12; C03B2201/00; C03B2201/06; C03B2201/08; C03B2201/10; C03B2201/30; C03B2201/50
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
113 words
A method for producing a crack-free sol-gel derived silicon-containing gel monolith comprising (1) forming a silicon-containing sol comprising SiO 2 --B 2 O 3 --Na 2 O in a proportion of 42 mole % SiO 2 , 30 mole % B 2 O 3 and 28 mole % Na 2 O and a drying control chemical additive, said drying control agent enabling the formation of a crack-free gel monolith under drying conditions of elevated temperatures of between 70° and 150° C. for a period of between 18 hours and 96 hours; (2) casting said sol; (3) gelling said cast sol; and (4) drying said gelled cast sol to form a crack-free gelled monolith.
Claim 2
Independent Claim
113 words
A method for producing a crack-free sol-gel derived silicon-containing gel monolith comprising (1) forming a silicon-containing sol comprising SiO 2 --B 2 O 3 --Na 2 O in a proportion of 42 mole % SiO 2 , 30 mole % B 2 O 3 and 28 mole % Na 2 O and a drying control chemical additive, said drying control agent enabling the formation of a crack-free gel monolith under drying conditions of elevated temperatures of between 70° and 150° C. for a period of between 18 hours and 96 hours; (2) casting said sol; (3) gelling said cast sol; and (4) drying said gelled cast sol to form a crack-free gelled monolith.
Claim 3
Dependent Claim
37 words
The method of claim 1 wherein the drying control chemical additive is selected from the group consisting of glycerol, formamide, oxalic acid and acids of the formula C n H 2 (n-1) O 2n and mixtures thereof.
Claim 4
Dependent Claim
19 words
The method of claim 2 wherein said sol is formed from tetramethoxysilane, a trimethoxy boron and a sodium methoxide.
Claim 5
Dependent Claim
30 words
The method of claim 3 wherein oxalic acid is added in an amount of from about 0.1 to about 10 weight percent of the tetramethoxysilane, trimethoxy boron and sodium methoxide.
Claim 6
Dependent Claim
14 words
The method of claim 2 wherein the drying control chemical additive is oxalic acid.
Claim 7
Dependent Claim
18 words
The method of claim 5 wherein said silicon-containing sol is formed from tetraethoxysilane, trimethoxy boron and sodium methoxide.
Claim 8
Dependent Claim
29 words
The method of claim 6 wherein oxalic acid is added in an amount from about 0.1 to about 10 weight percent of the tetraethoxysilane, trimethoxy boron and sodium methoxide.
Claim 9
Dependent Claim
14 words
A crack-free sol-gel derived silicon-containing gel monolith made by the process of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-07-24 | 1993-01-23 | 1993-07-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-07-24 | 1997-01-23 | 1997-07-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-07-24 | 2001-01-23 | 2001-07-25 | $7700.00 | Window Closed / Lapsed |