US4849486A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Polyphenylene ether resin composition
Assignee: Eneos Corp
•
Filing: 1986-07-09
•
Granted: 1989-07-18
•
Expires: 2006-07-09
Abstract
Abstract This invention relates to a new and improved resin composition containing polyphenylene ether and, more particularly, to a molding resin composition including polyphenylene ether and cyclopentadiene resin containing a polar group. The new and improved resin composition has good melting flowability and retains good mechanical and thermal characteristics inherent to polyphenylene ether and can be suitably used as a molding material.
Inventors
- 👤 Shozo Tsuchiya
- 👤 Makoto Sasaki
- 👤 Yukio Kobayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 16:14
CPC Classifications
C; C08; C08L; C08L25/00; C08L45/00; C08L71/00; C08L71/08; C08L71/10; C08L71/12; C08L71/123; C08L65/00; Y; Y10; Y10S; Y10S525/00; Y10S525/905
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
186 words
A molding polyphenylene ether resin composition comprising: (a) 30 to 100 parts by weight of polyphenylene ether resin; (b) 0 to 70 parts by weight of styrene resin; (c) 3 to 100 parts by weight of polar-group containing cyclopentadiene resin having a ring and a ball softening point of not less than 100° C. with respect to 100 parts by weight of (a)+ (b); the polar-group cyclopentadiene resin (c) being a resin selected from the group consisting of: a polargroup cyclopentadiene resin prepared by copolymerizing 100 parts by weight of component A consisting essentially of a five-membered ring compound having conjugated double bonds and represented by the formula: ##STR5## (wherein H is a hydrogen atom, R is an alkyl group having 1 to 3 carbon atoms, each of m and n is independently 0 or an integer of not less than 1, and m+n=6) a Diels-Alder adduct thereof or mixture thereof and 1 to 50 parts by weight of component B, which is a compound containing carbon-carbon double bonds with a polar group selected from the group consisting of a hydroxy group and an ester group.
Claim 2
Dependent Claim
186 words
A molding polyphenylene ether resin composition comprising: (a) 30 to 100 parts by weight of polyphenylene ether resin; (b) 0 to 70 parts by weight of styrene resin; (c) 3 to 100 parts by weight of polar-group containing cyclopentadiene resin having a ring and a ball softening point of not less than 100° C. with respect to 100 parts by weight of (a)+ (b); the polar-group cyclopentadiene resin (c) being a resin selected from the group consisting of: a polargroup cyclopentadiene resin prepared by copolymerizing 100 parts by weight of component A consisting essentially of a five-membered ring compound having conjugated double bonds and represented by the formula: ##STR5## (wherein H is a hydrogen atom, R is an alkyl group having 1 to 3 carbon atoms, each of m and n is independently 0 or an integer of not less than 1, and m+n=6) a Diels-Alder adduct thereof or mixture thereof and 1 to 50 parts by weight of component B, which is a compound containing carbon-carbon double bonds with a polar group selected from the group consisting of a hydroxy group and an ester group.
Claim 3
Dependent Claim
46 words
A molding polyphenylene ether resin composition according to claim 1 comprising 40-80 parts of polyphenylene ether resin, 0-60 parts of styrene resin, 5-60 parts of the polargroup cyclopentadiene resin with respect to 100 parts by weight of the combination of polyphenylene ether resin and styrene resin.
Claim 4
Dependent Claim
52 words
A molding polyphenylene ether resin composition according to claim 1 in which the styrene resin contains at least 70° by weight copolymerized monomer of the formula ##STR6## in which R is hydrogen, lower alkyl or halogen, Z is lower alkyl, hydrogen or halogen and p is an integer of 1 to 5.
Claim 5
Dependent Claim
22 words
A molding polyphenylene ether resin composition according to claim 3 in which the copolymerized monomer is not less than 90° by weight.
Claim 6
Dependent Claim
17 words
A molding polyphenylene ether resin composition according to claim 1 in which the styrene resin is polystyrene.
Claim 7
Dependent Claim
24 words
A molding polyphenylene ether resin composition according to claim 1 in which the amount of component B is 2 to 40 parts by weight.
Claim 8
Dependent Claim
28 words
A molding polyphenylene ether resin composition according to claim 1 in which the polar-group cyclopentadiene resin has a ring and ball softening point of 120° to 200° C.
Claim 9
Dependent Claim
28 words
A molding polyphenylene ether resin composition according to claim 1 in which the polar-group cyclopentadiene resin has a ring and ball softening point of 130° to 180° C.
Claim 10
Dependent Claim
22 words
A molding polyphenylene ether resin composition according to claim 1 in which component A is dicyclopentadiene and component B is methyl methacrylate.
Claim 11
Dependent Claim
46 words
A molding polyphenylene ether resin composition according to claim 9 in which the styrene resin is polystyrene, the polar-group cyclopentadiene resin has a ring and ball softening point of 120° to 200° C. and the amount of component B is 2 to 40 parts by weight.
Claim 12
Dependent Claim
19 words
A molding polyphenylene ether resin composition according to claim 1 in which the polyphenylene ether resin is poly(dimethylphenylene) ether.
Claim 13
Dependent Claim
18 words
The molding polyphenylene ether resin composition according to claim 1, wherein said component B is an unsaturated alcohol.
Claim 14
Dependent Claim
28 words
The molding polyphenylene ether resin composition according to claim 12, wherein said unsaturated alcohol is selected from the group consisting of allyl alcohol, butenediol, crotyl alcohol and hexenediol.
Claim 15
Dependent Claim
18 words
The molding polyphenylene ether resin composition according to claim 1, wherein said component B is an unsaturated ester.
Claim 16
Dependent Claim
32 words
The molding polyphenylene ether resin composition according to claim 14 wherein said unsaturated ester is selected from the group consisting of vinyl acetate, vinyl propionate, methyl methacrylate, ethyl acrylate and butyl acrylate.
Claim 17
Dependent Claim
17 words
A molding polyphenylene ether resin composition according to claim 1, in which said component A is dicyclopentadiene.
Claim 18
Dependent Claim
18 words
A molding polyphenylene ether resin composition according to claim 1, in which said component B is methyl methacrylate.
Claim 19
Dependent Claim
43 words
A molding polyphenylene ether resin composition consisting essentially of; (a) 40-80 parts of poly(dimethylphenylene) ether; (b) 0-60 parts of polystyrene; and (c) 5-60 parts the resin copolymerization product of dicyclopentadiene and methyl methacrylate having a ring and ball softening point of 130°-180° C.
Claim 20
Dependent Claim
43 words
A molding polyphenylene ether resin composition consisting essentially of; (a) 40-80 parts of poly(dimethylphenylene) ether; (b) 0-60 parts of polystyrene; and (c) 5-60 parts the resin copolymerization product of dicyclopentadiene and methyl methacrylate having a ring and ball softening point of 130°-180° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-07-17 | 1993-01-16 | 1993-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-07-17 | 1997-01-16 | 1997-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-07-17 | 2001-01-16 | 2001-07-18 | $7700.00 | Window Closed / Lapsed |