Abstract A novel basic refractory composition is disclosed. This composition has high resistance to calcium silicates such as cement clinkers and slag formed in steelmaking operations. It also has superior resistance to thermal shock and stresses such as load in high temperature. A refractory brick produced from this composition can be used in the firing zone of a rotary kiln and successfully withstands cement firing operations for a significantly longer period than conventional refractory bricks. The basic refractory composition consists of a synthetic calcium zirconate based clinker in combination with raw materials for magnesia; the molar ratio of CaO to ZrO 2 in said clinker is in the range of 0.5-1.1, at least part of said clinker being in the form of particles having a size not smaller than 0.5 mm, ZrO 2 being present in an amount of 4-49 wt % of said composition, the sum of CaO and MgO being 50-95 wt %, and the sum of ZrO 2 , CaO and MgO being at least 80 wt %.
A basic refractory composition comprising a synthetic calcium zirconate based clinker having therein respective quantities of calcium oxide (CaO) and zirconium oxide (ZrO 2 ), in combination with magnesia (MgO), the molar ratio of CaO to ZrO 2 in said clinker being in the range of 0.5-1.1, at least 10 wt.% of said composition being in the form of clinker particles having a size not smaller than 0.5 mm prior to forming, the total combined weight percentage of the quantities of ZrO 2 , CaO and MgO in the composition being at least 80 wt.%, ZrO 2 being present in an amount of 4-49 wt.% of said composition, and the sum of CaO and MgO being 50-95 wt.%.
Claim 2
Dependent Claim
118 words
A basic refractory composition comprising a synthetic calcium zirconate based clinker having therein respective quantities of calcium oxide (CaO) and zirconium oxide (ZrO 2 ), in combination with magnesia (MgO), the molar ratio of CaO to ZrO 2 in said clinker being in the range of 0.5-1.1, at least 10 wt.% of said composition being in the form of clinker particles having a size not smaller than 0.5 mm prior to forming, the total combined weight percentage of the quantities of ZrO 2 , CaO and MgO in the composition being at least 80 wt.%, ZrO 2 being present in an amount of 4-49 wt.% of said composition, and the sum of CaO and MgO being 50-95 wt.%.
Claim 3
Dependent Claim
26 words
A basic refractory composition according to claim 1 wherein the molar ratio of CaO to ZrO 2 in said clinker is in the range of 0.8-1.1.
Claim 4
Dependent Claim
29 words
A basic refractory composition according to claim 1 wherein the content of ZrO 2 is present in an amount in the range of 6-40 wt % of said composition.
Claim 5
Dependent Claim
26 words
A basic refractory composition according to claim 1 wherein the sum of CaO and MgO in said composition is in the range of 59-88 wt %.
Claim 6
Dependent Claim
26 words
A basic refractory composition according to claim 1 wherein the sum of CaO, MgO and ZrO 2 in said composition is at least 90 wt %.