US4849266A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Compliant layer
Assignee: Lanxide Technology Co LP
•
Filing: 1987-11-03
•
Granted: 1989-07-18
•
Expires: 2007-11-03
Abstract
Abstract This invention relates to a new ceramic-metal composite body and a method for producing the same. Particularly, a compliant layer composition is utilized for preventing the rupture of a ceramic article (1) and/or the yielding or failure of a metal during the pouring, solidification and cooling of a molten metal which has been cast around the ceramic. A slurry composition for the compliant layer (2) includes plaster of paris, a liquid vehicle and a filler material. The slurry composition is coated on the ceramic article (1) and thereafter is heat-treated to form a compliant layer (2). Ceramic-metal composite bodies comprising low strength hollow articles and high expansion coefficient metals may be manufactured according to the method of this invention.
Inventors
- 👤 Ratnesh K. Dwivedi
- 👤 Virgil Irick, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 12:59
CPC Classifications
C; C04; C04B; C04B37/00; B; B22; B22D; B22D19/00; F; F05; F05C; F05C2251/00; F05C2251/04; F05C2251/042; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/4998; Y10T29/49982; Y10T29/49984; Y10T428/00; Y10T428/13; Y10T428/131; Y10T428/249921; Y10T428/249953; Y10T428/249987; Y10T428/31504; Y10T428/31678
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
75 words
A ceramic-metal composite body, comprising: a ceramic article having an outer surface; a metal casting encasing at least a portion of said outer surface; and an intermediate compliant layer disposed on at least a portion of said outer surface and intimately engaged by said metal, said compliant layer reducing stresses generated by the metal when the metal, as molten, is cast and cooled thereabout, said compliant layer comprising calcium sulfate as a major component thereof.
Claim 2
Dependent Claim
75 words
A ceramic-metal composite body, comprising: a ceramic article having an outer surface; a metal casting encasing at least a portion of said outer surface; and an intermediate compliant layer disposed on at least a portion of said outer surface and intimately engaged by said metal, said compliant layer reducing stresses generated by the metal when the metal, as molten, is cast and cooled thereabout, said compliant layer comprising calcium sulfate as a major component thereof.
Claim 3
Dependent Claim
46 words
The ceramic-metal composite body of claim 1, wherein said ceramic article comprises a material selected from the group of materials consisting of alumina, cordierite and an oxidation reaction product of an aluminum particulate parent metal with an oxidant to form alumina with aluminum metal included therein.
Claim 4
Dependent Claim
37 words
The ceramic-metal composite body of claim 2, wherein said ceramic article is hollow and has a four-point flexural strength of not greater than about 5000 psi and a Young's Modulus of not greater than about 70 GPa.
Claim 5
Dependent Claim
19 words
The ceramic-metal composite body of claim 3, wherein said oxidation reaction product comprises a porous core, dense skin material.
Claim 6
Dependent Claim
46 words
The ceramic-metal composite body of claim 4, wherein said porous core, dense skin material comprises a material having 5-10 volume percent of aluminum in the aluminum matrix and a ration between the thickness of the skin relative to the porous core is between 1/5 and 1/50.
Claim 7
Dependent Claim
47 words
The ceramic-metal composite body of claim 5, wherein said porous core, dense skin material is hollow and has a four-point flexural strength for the porous core of about 4000 psi, a Young's Modulus of about 160 GPa and a thermal expansion coefficient of about 9-10×10 -6 in/in/°C.
Claim 8
Dependent Claim
40 words
The ceramic-metal composite body of claim 1, wherein said metal comprises a metal selected from the group consisting of aluminum, copper, zinc, magnesium and alloys thereof, said metal being a thermal expansion coefficient of less than about 20×10 -6 in/in/°C.
Claim 9
Dependent Claim
17 words
The ceramic-metal composite body of claim 1, wherein said intermediate compliant layer further comprises a filler material.
Claim 10
Dependent Claim
29 words
The ceramic-metal composite body of claim 8, wherein said filler material comprises at least one material selected from the group consisting of cristobalite, quartz, kaolin clays, alumina and cordierite.
Claim 11
Dependent Claim
136 words
A ceramic-metal composite body, comprising: a hollow ceramic article comprising a material selected from the group of materials consisting of alumina, cordierite and an oxidation reaction product of an aluminum particulate parent metal with an oxidant to form alumina with aluminum metal included therein, said hollow ceramic article having an inner surface and an outer surface; an intermediate compliant layer comprising calcium sulfate as a major component thereof, said compliant layer having a porosity of at least about 30 volume percent; and an outer layer of metal intimately engaging said intermediate compliant layer, said outer layer of metal comprising a metal selected from the group of metals consisting of aluminum, cooper, zinc, magnesium and alloys thereof, wherein said compliant layer reduces stresses generated by the metal when the metal, as molten, is cast and cooled thereabout.
Claim 12
Dependent Claim
136 words
A ceramic-metal composite body, comprising: a hollow ceramic article comprising a material selected from the group of materials consisting of alumina, cordierite and an oxidation reaction product of an aluminum particulate parent metal with an oxidant to form alumina with aluminum metal included therein, said hollow ceramic article having an inner surface and an outer surface; an intermediate compliant layer comprising calcium sulfate as a major component thereof, said compliant layer having a porosity of at least about 30 volume percent; and an outer layer of metal intimately engaging said intermediate compliant layer, said outer layer of metal comprising a metal selected from the group of metals consisting of aluminum, cooper, zinc, magnesium and alloys thereof, wherein said compliant layer reduces stresses generated by the metal when the metal, as molten, is cast and cooled thereabout.
Claim 13
Dependent Claim
19 words
The ceramic-metal composite body of claim 10, wherein said compliant layer has a porosity of about 40-70 volume percent.
Claim 14
Dependent Claim
19 words
The ceramic-metal composite body of claim 10, wherein said oxidation reaction product comprises a porous core, dense skin article.
Claim 15
Dependent Claim
47 words
The ceramic-metal composite body of claim 12, wherein said porous core, dense skin article comprises a material having 5-10 volume percent of aluminum in the aluminum matrix and a ratio between thickness of the skin relative to thickness of the porous core is between 1/5 and 1/50.
Claim 16
Dependent Claim
44 words
The ceramic-metal composite body of claim 13, wherein said porous core, dense skin article has a four-point flexural strength for the porous core of about 4000 psi, A Young's Modulus of about 160 GPa and a thermal expansion coefficient of about 9-10×10 -6 in/in°C.
Claim 17
Dependent Claim
17 words
The ceramic-metal composite body of claim 10, wherein said intermediate compliant layer further comprises a filler material.
Claim 18
Dependent Claim
29 words
The ceramic-metal composite body of claim 15, wherein said filler material comprises at least one material selected from the group consisting of cristobalite, quartz, kaolin clays, alumina and cordierite.
Claim 19
Dependent Claim
75 words
A ceramic-metal composite body, comprising: a ceramic article having an outer surface; a metal casting encasing at least a portion of said outer surface; and an intermediate compliant layer disposed on at least a portion of said outer surface and intimately engaged by said metal, said compliant layer reducing stresses generated by the metal when the metal, as molten, is cast and cooled thereabout, said compliant layer comprising calcium silicate as a major component thereof.
Claim 20
Dependent Claim
75 words
A ceramic-metal composite body, comprising: a ceramic article having an outer surface; a metal casting encasing at least a portion of said outer surface; and an intermediate compliant layer disposed on at least a portion of said outer surface and intimately engaged by said metal, said compliant layer reducing stresses generated by the metal when the metal, as molten, is cast and cooled thereabout, said compliant layer comprising calcium silicate as a major component thereof.
References Cited (Backward Citations)
US3568723A
Cited
US3919755A
Cited
US4055451A
Cited
US4291741A
Cited
US4676064A
Cited
JPS61115662A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-07-17 | 1993-01-16 | 1993-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-07-17 | 1997-01-16 | 1997-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-07-17 | 2001-01-16 | 2001-07-18 | $7700.00 | Window Closed / Lapsed |