Preparation of foundry molds or cores
Assignee: Hepworth Minerals and Chemicals Ltd
•
Filing: 1987-07-27
•
Granted: 1989-07-18
•
Expires: 2007-07-27
Abstract
Abstract Foundry molds and cores are prepared by using as a binder a phenolic resin in solution in aqueous sodium hydroxide and using an ester to cure the binder. The ester may be incorporated in the mixture prior to shaping, or the ester in gaseous form may be passed through the shaped mixture.
Inventors
- 👤 Geoffrey W. Westwood
- 👤 Raymond A. Higgins
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 13:43
CPC Classifications
B; B22; B22C; B22C1/00; B22C1/16; B22C1/20; B22C1/22; B22C1/2233; B22C1/2246; B22C1/2253; C; C08; C08K; C08K5/00; C08K5/04; C08K5/10; C08K5/101
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
179 words
A method of preparing a foundry mould or core wherein an aldehyde is reacted with a phenol at an elevated temperature in the presence of aqueous alkali to produce a resin composition having a weight average molecular weight determined by gel permeation chromatography for the unprecipitated solution not exceeding 1500, the molar ratio of aldehyde to phenol being within the range 1:1 to 3:1 and the alkali being sodium alkali, the resin composition is mixed with a foundry aggregate and an organic ester, the weight of resin composition being up to 1.5% of the weight of the aggregate and the solids content of the resin composition being from about 40% to about 65%, by weight, the weight of ester being within the range 15% to 95% of the weight of the resin composition, the ester being an ester of an alcohol and a C 1 to C 12 carboxylic acid, the mixture is formed to the required shape and is permitted to cure and wherein the compressive strength after twenty four hours is at least 4000 kN/m 2 .
Claim 2
Independent Claim
179 words
A method of preparing a foundry mould or core wherein an aldehyde is reacted with a phenol at an elevated temperature in the presence of aqueous alkali to produce a resin composition having a weight average molecular weight determined by gel permeation chromatography for the unprecipitated solution not exceeding 1500, the molar ratio of aldehyde to phenol being within the range 1:1 to 3:1 and the alkali being sodium alkali, the resin composition is mixed with a foundry aggregate and an organic ester, the weight of resin composition being up to 1.5% of the weight of the aggregate and the solids content of the resin composition being from about 40% to about 65%, by weight, the weight of ester being within the range 15% to 95% of the weight of the resin composition, the ester being an ester of an alcohol and a C 1 to C 12 carboxylic acid, the mixture is formed to the required shape and is permitted to cure and wherein the compressive strength after twenty four hours is at least 4000 kN/m 2 .
Claim 3
Dependent Claim
36 words
A method according to claim 1 wherein the aldehyde is added gradually to an alkaline solution of the phenol and wherein the compressive strength after twenty four hours is in excess of 5500 kN/m 2 .
References Cited (Backward Citations)
GB1257181A
Cited
JPS50130627A
Cited
US4166799A
Cited
US4426467A
Cited
US4474904A
Cited
US4468359A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-07-17 | 1993-01-16 | 1993-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-07-17 | 1997-01-16 | 1997-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-07-17 | 2001-01-16 | 2001-07-18 | $7700.00 | Window Closed / Lapsed |