Method for separation, recovery, and recycling of plastics from municipal solid waste
Assignee: WEME LLC
•
Filing: 1988-03-21
•
Granted: 1989-07-04
•
Expires: 2008-03-21
Abstract
Abstract A method for treatment of mixed wastes containing various plastics, such as municipal solid wastes, in which mechanical agitation and heat distortion of plastic films cause rupture and spilling of the contents of plastic film containers in the wastes. The wastes are introduced into a processing unit with means of heating and mechanical agitation of the contents. By the method in this invention, the plastics are separated and recovered as a mixture that may be recycled as a composite plastic used in the manufacture of various products or that may be further separated into identifiable types of plastics for recycling. The quantity of plastics recovered from MSW is greatly increased compared to previous processes using steam heat to achieve separation of the components of such mixed wastes.
Inventors
- 👤 Clifford C. Holloway
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 22:59
CPC Classifications
C; C22; C22B; C22B1/00; C22B1/005; B; B03; B03B; B03B9/00; B03B9/06; B29; B29B; B29B17/00; B29B17/02; B29B2017/0203; B29K; B29K2105/00; B29K2105/04; B29K2705/00; B29K2705/02; B29L; B29L2007/00; B29L2007/008; Y; Y02; Y02P; Y02P10/00; Y02P10/20; Y02W; Y02W30/00; Y02W30/50; Y02W30/62; Y10; Y10S; Y10S209/00; Y10S209/93; Y10S241/00; Y10S241/38
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
110 words
A method for treatment of mixed wastes containing various plastics in plastic film containers to enhance the recoverability of said plastics comprising: (a) introducing a predetermined quantity of mixed wastes into a pressure chamber; heating said mixed waste to about 195° F. to 215° F. at a pressure of about 10.0 to 15.0 psia for a processing period of between about 15 minutes to one hour by introducing saturated steam into said pressure chamber to rupture said plastic film containers; (c) agitating said mixed waste during said processing period; and (d) removing said mixed waste from said pressure chamber for classification for recycling; and (e) separating and recovering said plastics.
Claim 2
Independent Claim
110 words
A method for treatment of mixed wastes containing various plastics in plastic film containers to enhance the recoverability of said plastics comprising: (a) introducing a predetermined quantity of mixed wastes into a pressure chamber; heating said mixed waste to about 195° F. to 215° F. at a pressure of about 10.0 to 15.0 psia for a processing period of between about 15 minutes to one hour by introducing saturated steam into said pressure chamber to rupture said plastic film containers; (c) agitating said mixed waste during said processing period; and (d) removing said mixed waste from said pressure chamber for classification for recycling; and (e) separating and recovering said plastics.
Claim 3
Dependent Claim
39 words
method as defined in claim 1 wherein said pressure chamber is essentially cylindrical and is inclined at a predetermined angle from horizontal wherein said agitating step comprises continuously rotating said chamber about its longitudinal axis while injecting steam thereinto.
Claim 4
Dependent Claim
35 words
A method as defined in claim 1 further comprising partially classifying said mixed waste removed from said pressure chamber by magnetically separating ferrous metals in said mixed waste from the remainder of said mixed waste.
Claim 5
Dependent Claim
34 words
A method as defined in claim 3 further comprising further classifying said mixed waste by eddy current detection of aluminum products and subsequent removal of aluminum products from the remainder of said mixed waste.
Claim 6
Independent Claim
128 words
A method for treatment of mixed wastes containing various plastics in plastic film containers to enhance the recoverability of said plastics comprising: (a) heating said mixed wastes in mass to a temperature of about 195° F. to about 215° F. at a pressure of about 10.0 to 15.0 psia by introducing saturated steam into a pressure chamber for a processing period of between 15 minutes to one hour, to reduce the tensile strength of plastics therein without melting said plastics; (b) continuously agitating said mixed wastes while heating said wastes; (c) maintaining said pressure on said mixed wastes while heating and agitating said mixed wastes to rupture said plastic film containes sufficiently to permit classification of said mixed wastes for recycling, and (d) separating and recovering said plastics.
Claim 7
Independent Claim
128 words
A method for treatment of mixed wastes containing various plastics in plastic film containers to enhance the recoverability of said plastics comprising: (a) heating said mixed wastes in mass to a temperature of about 195° F. to about 215° F. at a pressure of about 10.0 to 15.0 psia by introducing saturated steam into a pressure chamber for a processing period of between 15 minutes to one hour, to reduce the tensile strength of plastics therein without melting said plastics; (b) continuously agitating said mixed wastes while heating said wastes; (c) maintaining said pressure on said mixed wastes while heating and agitating said mixed wastes to rupture said plastic film containes sufficiently to permit classification of said mixed wastes for recycling, and (d) separating and recovering said plastics.
Claim 8
Dependent Claim
89 words
The method as defined in claim 5 further comprising the steps subsequent to said heating and agitating steps of: (a) magnetically removing ferrous metals from said mixed wastes; (b) removing aluminum from said mixed wastes subsequent to eddy current detection of said aluminum; (c) mechanically separating glass and plastic containers, as well as bulk paper, from the remainder of said mixed wastes; (d) mechanically removing cloth from said mixed wastes using a ragger; and (e) pneumatically separating low density plastics from said mixed wastes in a hot air stream.
Claim 9
Dependent Claim
49 words
The method as defined in claim 5 wherein said heating and agitating of said mixed wastes are carried out in a cylindrical pressure vessel inclined at a predetermined angle with respect to the horizontal and wherein said agitating is performed by rotating said pressure vessel about its longitudinal axis.
Claim 10
Dependent Claim
87 words
The method as defined in claim 5 further comprising the steps subsequent to said heating and agitating of: (a) magnetically removing ferrous metals from said mixed waste; (b) removing aluminum from said mixed wastes using eddy current detection; (c) mechanically separating glass and plastic containers, as well as bulk paper, from the remainder of said mixed wastes; (d) mechanically removing cloth from said mixed waste using a ragger; and (e) pneumatically separating low density plastics from the remainder of said mixed waste in a hot air stream.
References Cited (Backward Citations)
US3587851A
Cited
DE2520598A1
Cited
US4106627A
Cited
US4033907A
Cited
US4264352A
Cited
US4342830A
Cited
US4570861A
Cited
US4511091A
Cited
US4607797A
Cited
US4540495A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-07-03 | 1993-01-02 | 1993-07-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-07-03 | 1997-01-02 | 1997-07-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-07-03 | 2001-01-02 | 2001-07-04 | $7700.00 | Window Closed / Lapsed |