Process for improving resistance of metal bodies to stress corrosion cracking
Assignee: O'DONNELL & ASSOCIATES Inc A CORP OF PA
•
Filing: 1988-02-16
•
Granted: 1989-06-27
•
Expires: 2008-02-16
Abstract
Abstract A process for improving resistance of pressure vessel shells, tubesheets, tubes, pipes, pipe fittings and machine parts to stress corrosion cracking comprising heating at least those portions of such bodies subject to danger by stress corrosion cracking to a critical elevated themperature level, cooling at least the surface portions of the metal body subject to stress corrosion cracking and then permitting such treated portions of the metal body to come to ambient temperature.
Inventors
- 👤 Jan S. Porowski
- 👤 Manu L. Badlani
- 👤 William J. O'Donnell
- 👤 Edward J. Hampton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 16:39
CPC Classifications
C; C21; C21D; C21D9/00; C21D9/0068; C21D1/00; C21D9/08; Y; Y10; Y10S; Y10S376/00; Y10S376/90
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
153 words
A process for improving resistance of a metal body selected from the group consisting of pressure vessel shells, tubesheets, pipes and pipe fittings to stress corrosion cracking which comprises heating at least those portions of said metal body endangered by stress corrosion cracking to an elevated temperature level, cooling at least the surfaces of those heated portions of said metal body endangered by stress corrosion cracking to a temperature below said elevated temperature, and then permitting said portions of said metal body to come to ambient temperature, said elevated temperature level being below the characteristic temperature resulting in metallurgical change in the material of said metal body but at least an elevated temperature level such that the difference between said elevated temperature level and the temperature to which said surfaces are cooled is sufficient to result in plastic flow of said cooled surfaces to a depth equivalent to at least one grain size.
Claim 2
Dependent Claim
153 words
A process for improving resistance of a metal body selected from the group consisting of pressure vessel shells, tubesheets, pipes and pipe fittings to stress corrosion cracking which comprises heating at least those portions of said metal body endangered by stress corrosion cracking to an elevated temperature level, cooling at least the surfaces of those heated portions of said metal body endangered by stress corrosion cracking to a temperature below said elevated temperature, and then permitting said portions of said metal body to come to ambient temperature, said elevated temperature level being below the characteristic temperature resulting in metallurgical change in the material of said metal body but at least an elevated temperature level such that the difference between said elevated temperature level and the temperature to which said surfaces are cooled is sufficient to result in plastic flow of said cooled surfaces to a depth equivalent to at least one grain size.
Claim 3
Dependent Claim
14 words
The process of claim 1 wherein said metal body is a pressure vessel shell.
Claim 4
Dependent Claim
12 words
The process of claim 1 wherein said metal body is a tubesheet.
Claim 5
Dependent Claim
13 words
The process of claim 1 wherein said metal body is a pipe fitting.
Claim 6
Dependent Claim
21 words
The process of claim 1 wherein said elevated temperature is in the range of about 400° F. to about 1300° F.
Claim 7
Dependent Claim
33 words
The process of claim 1 wherein said portions of said metal body are composed of stainless steel and said elevated temperature is in the range of about 400° F. to about 1200° F.
Claim 8
Dependent Claim
33 words
The process of claim 1 wherein said portions of said metal body are composed of stainless steel and said elevated temperature is in the range of about 600° F. to about 1000° F.
Claim 9
Dependent Claim
33 words
The process of claim 1 wherein said portions of said metal body are composed of carbon steel and said elevated temperature is in the range of about 400° F. to about 1200° F.
Claim 10
Dependent Claim
33 words
The process of claim 1 wherein said portions of said metal body are composed of carbon steel and said elevated temperature is in the range of about 600° F. to about 800° F.
Claim 11
Dependent Claim
27 words
The process of claim 1 wherein said surfaces of said heated metal body are cooled to a temperature ranging from about ambient temperature to about 400° F.
Claim 12
Dependent Claim
27 words
The process of claim 1 wherein said surfaces of said heated metal body are cooled to a temperature ranging from about ambient temperature to about 212° F.
Claim 13
Dependent Claim
18 words
The process of claim 1 wherein said cooling is terminated within about one second to about one minute.
Claim 14
Dependent Claim
17 words
The process of claim 1 wherein said cooling is terminated within about three to about 30 seconds.
Claim 15
Dependent Claim
43 words
The process of claim 1 wherein the difference between said elevated temperature and the temperature to which said surfaces are cooled is sufficient to result in plastic flow of said surface to a depth equivalent of about two to about 50 grain sizes.
Claim 16
Dependent Claim
18 words
The process of claim 1 wherein said cooling of said surfaces is obtained by spraying a liquid thereon.
Claim 17
Dependent Claim
10 words
The process of claim 15 wherein said liquid is water.
Claim 18
Dependent Claim
102 words
The process of claim 1 wherein said portions of said metal body are heated to a temperature in the range of about 400° F. to about 1,300° F., said surfaces are cooled to a temperature ranging from about ambient temperature to about 400° F. by spraying a liquid thereon, terminating said spraying, whereby the temperature of said surfaces increases to approach the temperature of the bulk of said metal body, and then permitting said metal body to come to ambient temperature, so that the depth of said plastic flow is in the depth equivalent range of about 2 to about 50 grains.
Claim 19
Dependent Claim
45 words
The process of claim 17 wherein said portions of said metal body are heated to a temperature in the range of about 600° F. to about 1,200° F. and said surfaces are cooled to a temperature ranging from about ambient temperature to about 212° F.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-06-26 | 1992-12-26 | 1993-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-06-26 | 1996-12-26 | 1997-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-06-26 | 2000-12-26 | 2001-06-27 | $7700.00 | Window Closed / Lapsed |