Production of optical recording medium
Assignee: Kuraray Co Ltd
•
Filing: 1987-07-10
•
Granted: 1989-06-20
•
Expires: 2007-07-10
Abstract
Abstract A process for producing an optical recording medium, comprising heat-treating an optical recording medium formed of a thin metal film on the minutely roughened surface of a plastic substrate, the medium being capable of strongly absorbing laser light of a specific wavelength region thereby being able to be written upon.
Inventors
- 👤 Hideki Kobayashi
- 👤 Minoru Ikeda
- 👤 Koichi Saito
- 👤 Shiro Nagata
- 👤 Koichi Horino
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 09:33
CPC Classifications
G; G11; G11B; G11B7/00; G11B7/24; G11B7/241; G11B7/242; G11B7/243; G11B2007/24302; G11B2007/24306; G11B2007/24308; G11B7/004; G11B7/0045; G11B7/00452; G11B7/252; G11B7/253; G11B7/2533; G11B7/2534; G11B7/2535; Y; Y10; Y10S; Y10S430/00; Y10S430/146
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
125 words
A process for producing an optical recording medium, which comprises: laminating a thin metal film ranging in thickness from 5 to 200 nm onto the minutely toughened surface of a plastic substrate; and heat-treating said laminated structure at a temperature which is greater than 40° C. and which at the same time is a temperature within the range of a temperature 80° C. lower than the glass transition temperature of the plastic substrate to a temperature 60° C. higher than the glass transition temperature of the plastic substrate; said optical recording medium upon exposure to laser light of a specific wavelength region, being deformed by the formation of bubbles on the thin metal layer of the recording medium which provide for the recording of information.
Claim 2
Dependent Claim
125 words
A process for producing an optical recording medium, which comprises: laminating a thin metal film ranging in thickness from 5 to 200 nm onto the minutely toughened surface of a plastic substrate; and heat-treating said laminated structure at a temperature which is greater than 40° C. and which at the same time is a temperature within the range of a temperature 80° C. lower than the glass transition temperature of the plastic substrate to a temperature 60° C. higher than the glass transition temperature of the plastic substrate; said optical recording medium upon exposure to laser light of a specific wavelength region, being deformed by the formation of bubbles on the thin metal layer of the recording medium which provide for the recording of information.
Claim 3
Dependent Claim
31 words
The process for producing an optical recording medium as claims in claim 1, wherein said heat treating is conducted for not less than 1 minute and not more than 120 minutes.
Claim 4
Dependent Claim
66 words
The process for producing an optical recording medium as claimed in claim 2, wherein the heat treatment is performed at a temperature higher than 40° C. and within a range where the lower end is lower by 20° C. than the glass transition point of the plastic substrate and the upper end is higher by 60° C. than the glass transition point of the plastic substrate.
Claim 5
Dependent Claim
66 words
The process for producing an optical recording medium as claimed in claim 3, wherein the heat treatment is performed at a temperature higher than 40° C. and within a range where the lower end is lower by 20° C. than the glass transition point of the plastic substrate and the upper end is higher by 40° C. than the glass transition point of the plastic substrate.
Claim 6
Dependent Claim
22 words
The process for producing an optical recording medium as claimed in claim 4, wherein the heat treatment is performed at high humidity.
Claim 7
Dependent Claim
23 words
The process for producing an optical recording medium as claimed in claim 4, wherein the heat treatment is performed on a flat plate.
Claim 8
Dependent Claim
60 words
The process for producing an optical recording medium as claimed in claim 23, wherein the plastic substrate has such a regularly roughened surface structure that the regular pitch, measured in the direction parallel to the average surface level, is smaller than the wavelength of the laser light used for writing and reading, and the depth is 0.05 to 1 μm.
Claim 9
Dependent Claim
31 words
The process for producing an optical recording medium as claimed in claim 23, wherein the thin metal film is produced from a metal having a melting point higher than 400° C.
Claim 10
Dependent Claim
35 words
The process for producing an optical recording medium as claimed in claim 8, wherein the thin metal film is produced from platinum, gold, aluminum, chromium, titanium, iron, nickel, silver, or copper, or an alloy thereof.
Claim 11
Dependent Claim
38 words
The process for producing an optical recording medium as claimed in claim 1, wherein the optical recording medium, before writing, has a reflectivity of 5 to 60% when it is struck with laser light through the plastic substrate.
Claim 12
Dependent Claim
30 words
The process for producing an optical recording medium as claimed in claim 1, wherein the minutely roughened structure on the substrate surface is formed by injection molding a plastic material.
Claim 13
Dependent Claim
31 words
The process for producing an optical recording medium as claimed in claim 1, wherein the minutely roughened structure on the substrate surface is formed by injection compression molding a plastic material.
Claim 14
Dependent Claim
30 words
The process for producing an optical recording medium as claimed in claim 1, wherein the minutely roughened structure on the substrate surface is formed by compression molding a plastic material.
Claim 15
Dependent Claim
29 words
The process for producing an optical recording medium as claimed in claim 1, wherein the minutely roughened structure on the substrate surface is formed by the photopolymer (2P) process.
Claim 16
Dependent Claim
23 words
The process for producing an optical recording medium as claimed in claim 1, wherein the metal layer is protected with a protective layer.
Claim 17
Dependent Claim
24 words
The process for producing an optical recording medium as claimed in claim 1, wherein the plastic material of the substrate is a thermoplastic resin.
Claim 18
Dependent Claim
34 words
The process for producing an optical recording medium as claimed in claim 16, wherein the thermoplastic resin is a polyester resin, a polyolefin resin, a polyamide resin, a polycarbonate resin, or a polymethacrylate resin.
Claim 19
Dependent Claim
46 words
A process for making permanent recordings on the optical recording medium of claim 1, which comprises: causing a semiconductor laser beam to strike the plastic substrate, thereby inducing the local decomposition of the plastic substrate which causes gas evolution that forms bubbles which have increased reflectivity.
References Cited (Backward Citations)
US3454445A
Cited
US3452133A
Cited
JPS5774834A
Cited
US4539572A
Cited
US4365257A
Cited
JPS58151222A
Cited
US4616237A
Cited
US4601861A
Cited
US4583102A
Cited
JPS60210493A
Cited
JPS6120719A
Cited
JPS6179626A
Cited
US4729805A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-06-19 | 1992-12-19 | 1993-06-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-06-19 | 1996-12-19 | 1997-06-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-06-19 | 2000-12-19 | 2001-06-20 | $7700.00 | Window Closed / Lapsed |