Semi-permeable membranes prepared via reaction of cationic groups with nucleophilic groups
Assignee: Dow Chemical Co
•
Filing: 1987-08-17
•
Granted: 1989-06-13
•
Expires: 2007-08-17
Abstract
Abstract A novel composite membrane and methods of making the membrane are described. The discriminating layer of the membrane is prepared by reaction of a reactive cationic compound group with a compound bearing a nucleophilic moiety. At least one of the reactants bears an average of two or more reactive groups. The reaction product contains covalent bonds formed via charge eliminating reactions. In a preferred embodiment of the invention, the nucleophilic group is anionic and a coacervate is formed initially on a microporous substrate. The resulting membrane may be useful for reverse osmosis, gas or ultrafiltration separations.
Inventors
- 👤 Thomas E. Davis
- 👤 Donald L. Schmidt
- 👤 Jee I. Kau
- 👤 Ritchie A. Wessling
- 👤 Sharon S. Whipple
- 👤 Richard F. Fibiger
- 👤 Dale M. Pickelman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 09:00
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0081; B01D67/0088; B01D67/0093; B01D67/00933; B01D69/00; B01D69/08; B01D69/12; B01D69/125; B01D69/14; B01D71/00; B01D71/06; B01D71/40; B01D71/401; B01D71/404; B01D71/44; B01D71/46; B01D71/52; B01D71/521; B01D71/5211; B01D71/66; B01D71/68; B01D71/72; B01D71/76; B01D71/80; B01D71/82; B01D2323/00; B01D2323/30
Claims Analysis
Total Claims: 46
Claim 1
Independent Claim
84 words
Method of forming a semi-permeable membrane comprising: (a) contacting a permeable substrate bearing through physical contact or chemical bonding a plurality of reactive ionic groups of a first charge with a compound bearing reactive ionic groups of a charge opposite the first charge to form a coacervate layer, and (b) subjecting the coated substrate to reaction conditions effective to convert a plurality of the ionic bonds in the coacervate layer to covalent bonds thereby rendering the layer derived from the coacervate essentially water insoluble.
Claim 2
Dependent Claim
84 words
Method of forming a semi-permeable membrane comprising: (a) contacting a permeable substrate bearing through physical contact or chemical bonding a plurality of reactive ionic groups of a first charge with a compound bearing reactive ionic groups of a charge opposite the first charge to form a coacervate layer, and (b) subjecting the coated substrate to reaction conditions effective to convert a plurality of the ionic bonds in the coacervate layer to covalent bonds thereby rendering the layer derived from the coacervate essentially water insoluble.
Claim 3
Dependent Claim
36 words
The method as described in claim 1 wherein the substrate is a microporous polysulfone, a microporous cellulose ester or mixed cellulose ester with an adherent layer comprising a compound bearing ionic groups of a first charge.
Claim 4
Dependent Claim
31 words
The method as described in claim 2 wherein the ionic groups of the first charge are selected from the group consisting of sulfonium, quaternary ammonium, phosphonium, pyridinium, thiazolinium, imidazolinium and diazonium.
Claim 5
Dependent Claim
31 words
The method as described in claim 2 wherein the ionic groups of the charge opposite the first charge are selected from the group consisting of thioarylates, thioalkylates, arylates, alkylates and carboxylates.
Claim 6
Dependent Claim
18 words
The method as described in claim 4 wherein the ionic groups of the first charge are sulfonium groups.
Claim 7
Dependent Claim
38 words
The method as described in claim 5 wherein the adherent layer is a vinyl addition polymer containing at least 10 percent by weight of the reaction product of an ethylenically unsaturated monomer bearing at least one sulfonium group.
Claim 8
Dependent Claim
56 words
The method as described in claim 6 wherein the sulfonium-containing monomer corresponds to the formula ##STR56## wherein R 1 at each occurrence is independently a monovalent hydrocarbon radical, a monovalent inertlysubstituted hydrocarbon radical or both R 1 groups together with --S + < form a 5-, 6- or 7-member ring and A is a compatible anion.
Claim 9
Dependent Claim
16 words
The method as described in claim 7 wherein both R 1 groups together form a butylene.
Claim 10
Dependent Claim
15 words
The method as described in claim 7 wherein R 1 is methyl at each occurrence.
Claim 11
Dependent Claim
19 words
The method as described in claim 7 wherein R 1 is --C 2 H 4 OH at each occurrence.
Claim 12
Dependent Claim
62 words
The method as described in claim 6 wherein the remainder of the vinyl addition polymer is derived from monomers selected from the group consisting of monomers corresponding to the formula ##STR57## wherein F is a C 1 to C 20 alkyl, C 1 to C 20 hydroxyalkyl or corresponds to the formula ##STR58## and m is an integer from 1 to 20.
Claim 13
Dependent Claim
84 words
The method as described in claim 11 wherein the remainder of the vinyl addition polymer is derived from monomers selected from the group consisting of acrylamide, methacrylamide, styrene sulfonic acid, butadiene, isoprene, alkyl cyanoacrylate, vinyl benzyl chloride and its derivatives, styrene sulfonamide, vinyl acetate, acrylamide, methacrylamide, vinyl pyrrolidone and 2-sulfoethyl methacrylate, acrylonitrile, (C 1 to C 20 alkyl) methacrylates, (C 1 to C 20 alkyl) acrylate, (C 2 to C 20 hydroxyalkyl) methacrylates, p-tert-butylstyrene, p-tert-butyl-(α-methyl)styrene, dicyclopentenyl acrylate, isobornyl acrylate, isobornyl methacrylate and dicyclopentenyl methacrylate.
Claim 14
Dependent Claim
32 words
The method as described in claim 6 wherein the compound bearing reactive ionic groups of a charge opposite the first charge is a vinyl addition polymer bearing a plurality of carboxylate groups.
Claim 15
Dependent Claim
74 words
The method as described in claim 13 wherein the compound of a charge opposite the first charge is derived from monomers corresponding to the formulae ##STR59## wherein G + is Na + , K + , NH 4 + or other compatible cation and F is a C 1 to C 20 alkyl, C 2 to C 20 hydroxyalkyl or corresponds to the formula ##STR60## wherein m is an integer from 1 to 20.
Claim 16
Dependent Claim
25 words
The method as described in claim 11 wherein the permeable substrate bears through chemical bonding a plurality of reactive ionic groups of a first charge.
Claim 17
Dependent Claim
18 words
The method as described in claim 15 wherein the bonded ionic groups are sulfonium or quaternary ammonium groups.
Claim 18
Dependent Claim
15 words
The method as described in claim 15 wherein the bonded ionic groups are carboxylate groups.
Claim 19
Dependent Claim
28 words
The method as described in claim 2 wherein the ionic groups of the first charge are selected from the group consisting of thioarylates, thioalkylates, arylates, alkylates and carboxylates.
Claim 20
Dependent Claim
18 words
The method as described in claim 18 wherein the adherent layer is a vinyl addition polymer or carboxymethylcellulose.
Claim 21
Dependent Claim
23 words
The method as described in claim 19 wherein the adherent layer is a vinyl addition polymer which contains a plurality of carboxylate groups.
Claim 22
Dependent Claim
69 words
The method as described in claim 20 wherein the vinyl addition polymer is derived from monomers corresponding to the formulae ##STR61## wherein G + is Na + , K + , NH 4 + or other compatible cation and F is a C 1 to C 20 alkyl, C 2 to C 20 hydroxyalkyl or corresponds to the formula ##STR62## wherein m is an integer from 1 to 20.
Claim 23
Dependent Claim
27 words
The method as described in claim 18 wherein the compound bearing reactive ionic groups of a charge opposite the first charge bears a plurality of sulfonium groups.
Claim 24
Dependent Claim
46 words
The method as described in claim 22 wherein the compound bearing ionic groups of opposite charge to the first is a vinyl addition polymer containing at least 10 percent by weight of the reaction product of an ethylenically unsaturated monomer bearing at least one sulfonium group.
Claim 25
Dependent Claim
55 words
The method as described in claim 23 wherein the sulfonium-containing monomer corresponds to the formula ##STR63## wherein R 1 at each occurrence is independently a monovalent hydrocarbon radical, a monovalent inertly-substituted hydrocarbon radical or both R 1 groups together with --S + form a 5-, 6- or 7-member ring and A is a compatible anion.
Claim 26
Dependent Claim
16 words
The method as described in claim 24 wherein both R 1 groups together form a butylene.
Claim 27
Dependent Claim
15 words
The method as described in claim 24 wherein R 1 is methyl at each occurrence.
Claim 28
Dependent Claim
19 words
The method as described in claim 24 wherein R 1 is --C 2 H 4 OH at each occurrence.
Claim 29
Dependent Claim
35 words
The method as described in claim 1 wherein covalent bonds are formed in the coacervate layer by heating the layer to a temperature less than 125° C. and simultaneous removal of water from the layer.
Claim 30
Dependent Claim
48 words
The method as described in claim 24 wherein the remainder of the vinyl addition polymer is derived from monomers selected from the group consisting of acrylonitrile, C 1 to C 20 alkyl methacrylates, C 2 to C 20 hydroxyalkyl methacrylates, p-tert-butyl styrene, p-tert-butyl-(α-methyl)styrene, dicyclopentenyl acrylate and dicyclopentenyl methacrylate.
Claim 31
Dependent Claim
41 words
The method as described in claim 1 wherein the permeable substrate is sequentially contacted with first the compound bearing the first reactive ionic groups in an aqueous diluent followed by the compound bearing groups of opposite charge in an aqueous diluent.
Claim 32
Dependent Claim
43 words
The method as described in claim 30 further comprising repeating the sequence of contacting the substrate with compounds of the first charge and the compound of the opposite charge, so that a plurality of coatings of alternating charges is applied to the substrate.
Claim 33
Dependent Claim
26 words
The method as described in claim 31 further comprising rinsing the coacervate layer with water and partially curing each coacervate layer before repeating the contacting steps.
Claim 34
Independent Claim
105 words
The method of forming a semi-permeable membrane comprising: (a) contacting a porous support layer with a diluent containing a first compound which bears at least one reactive cationic group and a diluent containing a second compound which bears at least one reactive nucleophilic group, with the proviso that either the first or second compounds bear an average of more than one reactive group or at least one of the first or second compounds is polymerizable; and (b) reacting the first compound with the second compound so as to form on the support layer an adherent, essentially continuous, semi-permeable layer of a covalently bonded reaction product.
Claim 35
Independent Claim
105 words
The method of forming a semi-permeable membrane comprising: (a) contacting a porous support layer with a diluent containing a first compound which bears at least one reactive cationic group and a diluent containing a second compound which bears at least one reactive nucleophilic group, with the proviso that either the first or second compounds bear an average of more than one reactive group or at least one of the first or second compounds is polymerizable; and (b) reacting the first compound with the second compound so as to form on the support layer an adherent, essentially continuous, semi-permeable layer of a covalently bonded reaction product.
Claim 36
Dependent Claim
44 words
The method as described in claim 33 wherein the first compound bears a plurality of cationic groups and the first compound is first deposited on the support layer then the second compound contacts the support layer bearing an adherent layer of the first compound.
Claim 37
Dependent Claim
44 words
The method as described in claim 33 wherein the second compound bears a plurality of nucleophilic groups and the second compound is first deposited on the support layer then the first compound contacts the support layer bearing an adherent layer of the second compound.
Claim 38
Dependent Claim
28 words
The method as described in claim 33 wherein the first and second compounds are both a single compound bearing a plurality of sulfonium groups with a nucleophilic counterion.
Claim 39
Dependent Claim
22 words
The method as described in claim 36 wherein the nucleophilic counterion is hydroxide, bicarbonate or a C 2 to C 10 carboxylate.
Claim 40
Dependent Claim
20 words
The method as described in claim 37 wherein the nucleophile is the conjugate base of pivalic acid or citric acid.
Claim 41
Dependent Claim
21 words
The method as described in claim 36 wherein the sulfonium compound is an amphoteric polymer including a plurality of carboxylate groups.
Claim 42
Dependent Claim
21 words
The method as described in claim 35 wherein the second compound is polyethyleneimine and the first compound is a sulfonium compound.
Claim 43
Dependent Claim
42 words
The method as described in claim 33 wherein the support layer is microporous and has a first major surface and a second major surface and the first compound contacts the first surface while simultaneously the second compound contacts the second major surface.
Claim 44
Dependent Claim
19 words
The method as described in claim 33 wherein the diluents for both the first and second compounds are aqueous.
Claim 45
Dependent Claim
17 words
The method as described in claim 33 wherein the support layer is a semi-permeable reverse osmosis membrane.
Claim 46
Dependent Claim
27 words
The method as described in claim 35 wherein the first compound is an aryl cyclic sulfonium zwitterion and the second compound bears a plurality of nucleophilic groups.
References Cited (Backward Citations)
US2676166A
Cited
US2891025A
Cited
US3078259A
Cited
US3544499A
Cited
US3276598A
Cited
US3335100A
Cited
US3269991A
Cited
US3419431A
Cited
US3429839A
Cited
US3419430A
Cited
US3578458A
Cited
US3546142A
Cited
US3467604A
Cited
US3637432A
Cited
US3737045A
Cited
US3962165A
Cited
US4096154A
Cited
US3804797A
Cited
US3963662A
Cited
US3965032A
Cited
US3998776A
Cited
US4017372A
Cited
US4225407A
Cited
US4214096A
Cited
US4426489A
Cited
US4337185A
Cited
US4360434A
Cited
US4432875A
Cited
US4383073A
Cited
US4431768A
Cited
US4444977A
Cited
EP0124676A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-06-12 | 1992-12-12 | 1993-06-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-06-12 | 1996-12-12 | 1997-06-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-06-12 | 2000-12-12 | 2001-06-13 | $7700.00 | Window Closed / Lapsed |