Abstract
Abstract In a method of fabricating an aluminum surface for applying mirror-smooth fabrication to the surface of aluminum or aluminum alloy by combining an electrolytic anode dissolving effect to the surface and a polishing effect of removing the protruded portions of passivated films formed on the surface to be fabricated by lapping with abrasive grains, the voltage between the aluminum material and the tool electrode is set within 2.1±0.3 V, an electrolyte at less than 10% concentration is used as a passivation type electrolyte, the urging pressure of the tool electrode to the surface is set to less than 2.0 kgf/cm 2 and free abrasive grains with the average grain size of less than 1.0 μm are used as the abrasive grains. The temperature of the electrolyte is preferably set to lower than 15° C. The polishing material may comprise non-woven abrasive cloth made of ultrafine fibers.
Inventors
- 👤 Kenichi Katsumoto
- 👤 Shigeo Isoda
- 👤 Takahiro Yuuki
- 👤 Shiro Koike
- 👤 Yutaka Yamamoto
- 👤 Suguru Motonishi
- 👤 Tadashi Kawaguchi
- 👤 Tetsuya Gotoh
- 👤 Shiro Horiguchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 17:33
CPC Classifications
B; B23; B23H; B23H5/00; B23H5/06; B23H5/08
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
120 words
A method of fabricating an aluminum surface for applying mirror-smooth fabrication to the surface of aluminum or aluminum alloy by combining an electrolytic anode dissolving effect to said surface and a polishing effect of removing the protruded portions of passivated films formed on said surface to be fabricated by lapping with abrasive grains, setting the voltage between the aluminum material and the tool electrode to within 2.1±0.3 V, utilizing an electrolyte at less than 10% concentration as a passivation type electrolyte, setting the urging pressure of the tool electrode to the surface to be fabricated to less than 2.0 kgf/cm 2 and using free abrasive grains with the average grain size of less than 1.0 μm as said abrasive grains.
Claim 2
Independent Claim
120 words
A method of fabricating an aluminum surface for applying mirror-smooth fabrication to the surface of aluminum or aluminum alloy by combining an electrolytic anode dissolving effect to said surface and a polishing effect of removing the protruded portions of passivated films formed on said surface to be fabricated by lapping with abrasive grains, setting the voltage between the aluminum material and the tool electrode to within 2.1±0.3 V, utilizing an electrolyte at less than 10% concentration as a passivation type electrolyte, setting the urging pressure of the tool electrode to the surface to be fabricated to less than 2.0 kgf/cm 2 and using free abrasive grains with the average grain size of less than 1.0 μm as said abrasive grains.
Claim 3
Independent Claim
65 words
A method of fabricating an aluminum surface for applying mirror-smooth fabrication to the surface of aluminum or aluminum alloy by combining an electrolytic anode dissolving effect to said surface and a polishing effect of removing the protruded portions of passivated films formed on said surface to be fabricated by lapping with abrasive grains, and setting the temperature of the electrolyte to lower than 15° C.
Claim 4
Independent Claim
65 words
A method of fabricating an aluminum surface for applying mirror-smooth fabrication to the surface of aluminum or aluminum alloy by combining an electrolytic anode dissolving effect to said surface and a polishing effect of removing the protruded portions of passivated films formed on said surface to be fabricated by lapping with abrasive grains, and setting the temperature of the electrolyte to lower than 15° C.
Claim 5
Independent Claim
86 words
A method of applying composite electrolytic mirror-smooth fabrication to the surface of aluminum or aluminum alloy by urging an abrasive head which comprises securing an electrode to a rotational shaft and appending an abrasive cloth to the lower end face of said electrode by way of a buffer member under a predetermined axial urging pressure during rotation, wherein the abrasive cloth comprises a non-woven fabric sheet made of ultrafine fibers and which comprises controlling the urging pressure within a range not exceeding 0.5 kgf/cm 2 .
Claim 6
Independent Claim
86 words
A method of applying composite electrolytic mirror-smooth fabrication to the surface of aluminum or aluminum alloy by urging an abrasive head which comprises securing an electrode to a rotational shaft and appending an abrasive cloth to the lower end face of said electrode by way of a buffer member under a predetermined axial urging pressure during rotation, wherein the abrasive cloth comprises a non-woven fabric sheet made of ultrafine fibers and which comprises controlling the urging pressure within a range not exceeding 0.5 kgf/cm 2 .
Claim 7
Independent Claim
139 words
A method of fabricating an aluminum surface for applying mirror-smooth fabrication to the surface of aluminum or aluminum alloy by combining an electrolytic anode dissolving effect on said surface and a polishing effect of removing protruding portions of passivated films formed on said surface by lapping with abrasive grains, said method comprising the steps of: (a) setting the voltage between the aluminum material and the tool electrode to within 2.1±0.3 V; (b) utilizing an electrolyte at less than 10% concentration as a passivation type electrolyte; (c) setting the urging pressure of the tool electrode to the surface to be fabricated to less than 2.0 kgf/cm 2 ; (d) using free abrasive grains with an average grain size of less than 1.0 μm as said abrasive grains; and (e) setting the temperature of the electrolyte to lower than 15° C.
Claim 8
Independent Claim
139 words
A method of fabricating an aluminum surface for applying mirror-smooth fabrication to the surface of aluminum or aluminum alloy by combining an electrolytic anode dissolving effect on said surface and a polishing effect of removing protruding portions of passivated films formed on said surface by lapping with abrasive grains, said method comprising the steps of: (a) setting the voltage between the aluminum material and the tool electrode to within 2.1±0.3 V; (b) utilizing an electrolyte at less than 10% concentration as a passivation type electrolyte; (c) setting the urging pressure of the tool electrode to the surface to be fabricated to less than 2.0 kgf/cm 2 ; (d) using free abrasive grains with an average grain size of less than 1.0 μm as said abrasive grains; and (e) setting the temperature of the electrolyte to lower than 15° C.
Claim 9
Independent Claim
105 words
A method of applying composite electrolytic mirror-smooth fabrication to the surface of aluminum or aluminum alloy by urging an abrasive head against said surface, said method comprising the steps of: (a) securing an electrode to a rotational shaft; (b) appending an abrasive cloth to the lower end face of said electrode by way of a buffer member under a predetermined axial urging pressure during rotation, the abrasive cloth comprising a non-woven fabric sheet made of ultra fine fibers; (c) controlling the urging pressure within a range not exceeding 0.5 kgf/cm 2 ; and (e) setting the temperature of the electrolyte to lower than 15° C.
Claim 10
Independent Claim
105 words
A method of applying composite electrolytic mirror-smooth fabrication to the surface of aluminum or aluminum alloy by urging an abrasive head against said surface, said method comprising the steps of: (a) securing an electrode to a rotational shaft; (b) appending an abrasive cloth to the lower end face of said electrode by way of a buffer member under a predetermined axial urging pressure during rotation, the abrasive cloth comprising a non-woven fabric sheet made of ultra fine fibers; (c) controlling the urging pressure within a range not exceeding 0.5 kgf/cm 2 ; and (e) setting the temperature of the electrolyte to lower than 15° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-06-12 | 1992-12-12 | 1993-06-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-06-12 | 1996-12-12 | 1997-06-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-06-12 | 2000-12-12 | 2001-06-13 | $7700.00 | Window Closed / Lapsed |