Method for structuring a copper and/or permalloy layer by means of dry etching
Assignee: Siemens AG
•
Filing: 1988-06-06
•
Granted: 1989-06-13
•
Expires: 2008-06-06
Abstract
Abstract A copper and/or permalloy layer is structured by means of dry etching. A layer of tantalum is applied as a mask to a layer to be structured, and a photoresist layer is applied to the tantalum layer. Subsequently, the structure of the photoresist layer generated in a photolithographic manner is transferred onto the mask by reactive ion etching. This procedure is continued until the copper or permalloy layer to be structured is exposed. The structuring of the copper or permalloy layer then occurs by ion beam etching.
Inventors
- 👤 Peter Gulde
- 👤 Christian Scholz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 23:03
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/127; G11B5/31; G11B5/3163; H; H01; H01F; H01F41/00; H01F41/32; H01F41/34
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
112 words
A method for structuring by dry etching a copper or permalloy alloy layer on a substrate surface, comprising steps of: applying a tantalum layer to be made into a metallic mask for transferring a desired structure to said copper or permalloy alloy layer; photolithographically generating a photoresist layer having said desired structure on the tantalum layer; transferring onto the tantalum layer metallic mask the desired structure of the photoresist layer through reactive ion etching, and continuing this procedure until the copper or permalloy alloy layer to be structured is exposed; and employing ion beam etching in connection with the structured tantalum layer metallic mask to structure the copper or permalloy alloy layer.
Claim 2
Independent Claim
112 words
A method for structuring by dry etching a copper or permalloy alloy layer on a substrate surface, comprising steps of: applying a tantalum layer to be made into a metallic mask for transferring a desired structure to said copper or permalloy alloy layer; photolithographically generating a photoresist layer having said desired structure on the tantalum layer; transferring onto the tantalum layer metallic mask the desired structure of the photoresist layer through reactive ion etching, and continuing this procedure until the copper or permalloy alloy layer to be structured is exposed; and employing ion beam etching in connection with the structured tantalum layer metallic mask to structure the copper or permalloy alloy layer.
Claim 3
Dependent Claim
68 words
A method according to claim 1 wherein the tantalum layer metallic mask is supplied with a layer thickness such that the metallic mask is not completely eroded even after said step of ion beam etching based upon a selectivity relationship between an etching rate of the material of the copper or permalloy alloy layer compared to an etching rate of the material of the tantalum layer metallic mask.
Claim 4
Dependent Claim
62 words
A method according to claim 1 including the step of applying said photoresist layer with a layer thickness based on a selectivity between an etching rate of a material of the tantalum layer metallic mask compared to an etching rate of a material of the photoresist layer such that the photoresist layer is not completely eroded following the reactive ion etching step.
Claim 5
Dependent Claim
22 words
A method according to claim 1 including the step of applying as a gas in the reactive ion etching step sulfur hexafluoride.
Claim 6
Dependent Claim
71 words
A method according to claim 1 wherein the step of reactive ion etching is implemented at a gas pressure limit related to a bias provided during the reactive ion etching such that attacking of the resist is limited, said limit gas pressure being chosen such that a ratio of a photoresist remaining layer thickness following the etching process compared to an original layer thickness of the photoresist layer is above 0.5.
Claim 7
Dependent Claim
30 words
A method according to claim 5 wherein the ratio of the remaining layer thickness following the etching process to the original layer thickness of the photoresist layer is substantially 0.6.
Claim 8
Dependent Claim
50 words
A method according to claim 1 wherein for the reactive ion etching step, process variables for applied radio frequency power and flow quantity of the gas are set such that an etching rate for the tantalum layer metallic mask results which is close to a maximum etching rate of tantalum.
Claim 9
Dependent Claim
41 words
A method according to claim 7 wherein the reactive ion etching step is implemented with a radio frequency power chosen such that an etching rate of the tantalum material of the mask is 0.9 times the maximum etching rate of tantalum.
Claim 10
Dependent Claim
56 words
A method according to claim 7 wherein for the reactive ion etching step, a process variable selected for the applied radio frequency power is such that a selectivity defined as a ratio of an etching rate of the tantalum material for the mask compared to an etching rate of the photoresist layer is at a maximum.
Claim 11
Independent Claim
94 words
A method for structuring by dry etching a copper or permalloy alloy layer on a substrate surface, comprising steps of: applying a tantalum layer to be made into a metallic mask for transferring a desired structure to said copper or permalloy alloy layer; generating a layer having said desired structure on the tantalum layer; transferring onto the tantalum layer metallic mask the desired structure of the structured layer through reactive ion etching; and employing ion beam etching in connection with the structured tantalum layer metallic mask to structure the copper or permalloy alloy layer.
Claim 12
Independent Claim
94 words
A method for structuring by dry etching a copper or permalloy alloy layer on a substrate surface, comprising steps of: applying a tantalum layer to be made into a metallic mask for transferring a desired structure to said copper or permalloy alloy layer; generating a layer having said desired structure on the tantalum layer; transferring onto the tantalum layer metallic mask the desired structure of the structured layer through reactive ion etching; and employing ion beam etching in connection with the structured tantalum layer metallic mask to structure the copper or permalloy alloy layer.
Claim 13
Independent Claim
100 words
A method for structuring by dry etching a copper layer on a substrate surface, comprising steps of: applying a tantalum layer to be made into a metallic mask for transferring a desired structure to said copper layer; photolithographically generating a photoresist layer having said desired structure on the tantalum layer; transferring onto the tantalum layer metallic mask the desired structure of the photoresist layer through reactive ion etching, and continuing this procedure until the copper layer to be structured is exposed; and employing ion beam etching in connection with the structured tantalum layer metallic mask to structure the copper layer.
Claim 14
Independent Claim
100 words
A method for structuring by dry etching a copper layer on a substrate surface, comprising steps of: applying a tantalum layer to be made into a metallic mask for transferring a desired structure to said copper layer; photolithographically generating a photoresist layer having said desired structure on the tantalum layer; transferring onto the tantalum layer metallic mask the desired structure of the photoresist layer through reactive ion etching, and continuing this procedure until the copper layer to be structured is exposed; and employing ion beam etching in connection with the structured tantalum layer metallic mask to structure the copper layer.
Claim 15
Independent Claim
104 words
A method for structuring by dry etching a permalloy alloy layer on a substrate surface, comprising steps of: applying a tantalum layer to be made into a metallic mask for transferring said desired structure to said permalloy alloy layer; photolithographically generating a photoresist layer having said desired structure on the tantalum layer; transferring onto the tantalum layer metallic mask the desired structure of the photoresist layer through reactive ion etching, and continuing this procedure until the permalloy alloy layer to be structured is exposed; and employing ion beam etching in connection with the structured tantalum layer metallic mask to structure the permalloy alloy layer.
Claim 16
Independent Claim
104 words
A method for structuring by dry etching a permalloy alloy layer on a substrate surface, comprising steps of: applying a tantalum layer to be made into a metallic mask for transferring said desired structure to said permalloy alloy layer; photolithographically generating a photoresist layer having said desired structure on the tantalum layer; transferring onto the tantalum layer metallic mask the desired structure of the photoresist layer through reactive ion etching, and continuing this procedure until the permalloy alloy layer to be structured is exposed; and employing ion beam etching in connection with the structured tantalum layer metallic mask to structure the permalloy alloy layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-06-12 | 1992-12-12 | 1993-06-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-06-12 | 1996-12-12 | 1997-06-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-06-12 | 2000-12-12 | 2001-06-13 | $7700.00 | Window Closed / Lapsed |