Process for the preparation of aqueous polyurethane dispersions and solutions
Assignee: Bayer AG
•
Filing: 1987-02-27
•
Granted: 1989-05-09
•
Expires: 2007-02-27
Abstract
Abstract The present invention therefore relates to a process for the preparation of aqueous solutions or dispersions of polyurethane-polyureas by the reaction in the aqueous phase of prepolymers which contain chemically built-in hydrophilic groups and/or external emulsifiers which are not bound chemically as well as at least two free isocyanate groups with organic compounds containing at least two primary and/or secondary amino groups, characterized in that the isocyanate prepolymer which has been hydrophilically modified and/or contains an external emulsifier is mixed, in the absence of water, with compounds containing at the most one free primary or secondary amino group and at least one blocked group which releases a free primary or secondary amino group in the presence of water and a total of at least two at least partially blocked primary and/or secondary amino groups, and the mixture is subsequently mixed with water. The invention also relates to the dispersions or solutions obtained by this process and to their use for coating flexible and rigid substrates.
Inventors
- 👤 Josef Pedain
- 👤 Klaus Nachtkamp
- 👤 Klaus Noll
- 👤 Jurgen Grammel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 10:15
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/0804; C03; C03C; C03C25/00; C08G18/10; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31551
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
189 words
A process for the preparatio of aqueous dispersions of polyurthane polyureas by the reaction of (1) prepolymers which have at least two free isocyanate groups and contatin chemically fixed hydrophilic groups or external emulsifiers which are not chemically fixed with (2) organic compounds containingn at least two groups selected from the group consisting of primary and secondary amino groups characterized in that the isocyanate-contatining prepolymer component (1), which is hydrophilically modified or contains an external emulsifier, is mixed, in the absence of water, with the organic compound component (2) which contains at least two groups selected from the group consisting of primary and secondary amino groups wherein at most one amino group is a free primary or secondary amino group and at least one amino group is a blocked amino group which is substantially inert toward isocyanate groups at room temperature in the absence of moisture and which releases a free primary or secondary amino group in the presence of water, and the mixture obtained is subsequently mixed with an amount of water sufficient to provide aqueous dispersions with a solids content of less than about 70% by weight.
Claim 2
Dependent Claim
189 words
A process for the preparatio of aqueous dispersions of polyurthane polyureas by the reaction of (1) prepolymers which have at least two free isocyanate groups and contatin chemically fixed hydrophilic groups or external emulsifiers which are not chemically fixed with (2) organic compounds containingn at least two groups selected from the group consisting of primary and secondary amino groups characterized in that the isocyanate-contatining prepolymer component (1), which is hydrophilically modified or contains an external emulsifier, is mixed, in the absence of water, with the organic compound component (2) which contains at least two groups selected from the group consisting of primary and secondary amino groups wherein at most one amino group is a free primary or secondary amino group and at least one amino group is a blocked amino group which is substantially inert toward isocyanate groups at room temperature in the absence of moisture and which releases a free primary or secondary amino group in the presence of water, and the mixture obtained is subsequently mixed with an amount of water sufficient to provide aqueous dispersions with a solids content of less than about 70% by weight.
Claim 3
Dependent Claim
46 words
The process according to claim 1, characterized in that the nature and proportions of the reactants are chosen so that from about 0.25 to 1.5 free plus blocked amino groups which are reactive with isocyanate groups are present for each isocyanate group of the isocyanate prepolymer.
Claim 4
Dependent Claim
241 words
A process for the production of an aqueous dispersion of a polyurethane polyurea comprising mixing in the absence of water (a) a hydrophilic NCO-prepolymer having (i) an average isocyanate functionality of from about 1.8 to 2.2, (ii) an average molecular weight of from about 500 to 10,000, and (iii) its hydrophilic properties contributed by dispersing centers selected from the group consisting of chemically incorporated cationic or anionic groups present in said NCO-prepolymer in from about 0.1 to 100 milliequivalents per 100 g of NCO-prepolymer, chemically incorporated ethylene oxide units present in said NCO-prepolymer in from about 0.5 to 30% by weight, based on the weight of the NCO polymer, and external emulsifiers present in about 1 to 30% by weight, based on the weight of the NCO-prepolymer, with (b) a polyamine having (i) at least two amino groups selected from the group consisting of primary amino groups and secondary amino groups, (ii) at most one free primary of secondary amino group, (iii) at least one blocked amino group which is substantially inert toard isocyanate groups at room temperature in the absence of moisture and which releases a free primary or secondary amino group in the presence of water, and (iv) a molecular weight of from about 60 to 500, and subsequently mixing the mixture of components (a) and (b) with an amount of water sufficient to provide an aqueous dispersion with a solids content of less than about 70% by weight.
Claim 5
Dependent Claim
241 words
A process for the production of an aqueous dispersion of a polyurethane polyurea comprising mixing in the absence of water (a) a hydrophilic NCO-prepolymer having (i) an average isocyanate functionality of from about 1.8 to 2.2, (ii) an average molecular weight of from about 500 to 10,000, and (iii) its hydrophilic properties contributed by dispersing centers selected from the group consisting of chemically incorporated cationic or anionic groups present in said NCO-prepolymer in from about 0.1 to 100 milliequivalents per 100 g of NCO-prepolymer, chemically incorporated ethylene oxide units present in said NCO-prepolymer in from about 0.5 to 30% by weight, based on the weight of the NCO polymer, and external emulsifiers present in about 1 to 30% by weight, based on the weight of the NCO-prepolymer, with (b) a polyamine having (i) at least two amino groups selected from the group consisting of primary amino groups and secondary amino groups, (ii) at most one free primary of secondary amino group, (iii) at least one blocked amino group which is substantially inert toard isocyanate groups at room temperature in the absence of moisture and which releases a free primary or secondary amino group in the presence of water, and (iv) a molecular weight of from about 60 to 500, and subsequently mixing the mixture of components (a) and (b) with an amount of water sufficient to provide an aqueous dispersion with a solids content of less than about 70% by weight.
Claim 6
Dependent Claim
23 words
The process of claim 3 wherein the blocked amino groups are blocked with compounds selected from the group consisting of aldehydes and ketones.
Claim 7
Dependent Claim
30 words
The process of claim 3 wherein the equivalent ratio of isocyanate groups of the NCO-prepolymer to free plus blocked amino groups of the polyamine is between about 4:1 and 1:1.5.
Claim 8
Dependent Claim
12 words
An aqueous polyurethane polyurea dispersion produced by the process of claim 3.
Claim 9
Dependent Claim
17 words
The aqueous polyurethane polyurea dispersion of claim 6 wherein the particle size is from about 20-200 mm.
Claim 10
Dependent Claim
20 words
The aqueous polyurethane polyurea dispersion of claim 6 wherein the solids content is from about 40 to 70% by weight.
Claim 11
Dependent Claim
12 words
An aqeuous polyurethane polyurea dispersion produced by the process of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-08 | 1992-11-07 | 1993-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-08 | 1996-11-07 | 1997-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-08 | 2000-11-07 | 2001-05-09 | $7700.00 | Window Closed / Lapsed |