Method of protecting ceramic bodies against mechanical and thermal action
Assignee: Vapor Technologies Inc
•
Filing: 1986-12-12
•
Granted: 1989-05-09
•
Expires: 2006-12-12
Abstract
Abstract Ceramic substrates, e.g. of silicon carbide or silicon nitride are protected against mechanical surface wear at high temperatures by an arc coating with a refractory metal followed by coating with another metal and then with a wear-reducing high density layer, e.g. of a metal oxide, nitride or carbide.
Inventors
- 👤 Eduard Pinkhasov
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:30
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B41/45; C04B41/52; C04B41/80; C04B41/81; C04B41/89; C23; C23C; C23C4/00; C23C4/02; C23C4/12; C23C4/131; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12542; Y10T428/12576; Y10T428/12583; Y10T428/1259
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
144 words
A method of protecting a ceramic body against mechanical and thermal deterioration, comprising the steps of: applying to a surface of said ceramic body, formed as a substrate, a thin layer of a refractory metal; thereafter depositing upon said refractory metal a layer of another metal; and depositing upon said layer of said other metal a high-density substantially impermeable layer of at least one protective compound selected from the group which consists of chromium oxide, zirconium oxide, titanium nitride, tungsten carbide, aluminum oxide, yttrium oxide and aluminum nitride, at least one of said layers being applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer.
Claim 2
Independent Claim
144 words
A method of protecting a ceramic body against mechanical and thermal deterioration, comprising the steps of: applying to a surface of said ceramic body, formed as a substrate, a thin layer of a refractory metal; thereafter depositing upon said refractory metal a layer of another metal; and depositing upon said layer of said other metal a high-density substantially impermeable layer of at least one protective compound selected from the group which consists of chromium oxide, zirconium oxide, titanium nitride, tungsten carbide, aluminum oxide, yttrium oxide and aluminum nitride, at least one of said layers being applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer.
Claim 3
Dependent Claim
61 words
The method defined in claim 1 wherein each of said layers is applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer.
Claim 4
Dependent Claim
23 words
The method defined in claim 2 wherein said layers are deposited in succession on said substrate without removing said substrate from said chamber.
Claim 5
Independent Claim
217 words
A method of protecting a ceramic body against mechanical and thermal deterioration, comprising the steps of: applying to a surface of said ceramic body, formed as a substrate, a thin layer of a refractory metal; thereafter depositing upon said refractory metal a layer of another metal; and depositing upon said layer of said other metal a high-density substantially impermeable layer of at least one protective compound selected from the group which consists of chromium oxide, zirconium oxide, titanium nitride, tungsten carbide, aluminum oxide, yttrium oxide and aluminum nitride, at least one of said layers being applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer, said layers being deposited in succession on said substrate without removing said substrate from said chamber, said high-density substantially impermeable layer being composed of Cr 2 O 3 , ZrO 2 , Y 2 O 3 or mixtures thereof, during the deposition of said high-density substantially impermeable layer an arc being struck between two electrodes at least one of which consists of chromium, zirconium or yttrium while oxygen is admitted to said chamber.
Claim 6
Independent Claim
217 words
A method of protecting a ceramic body against mechanical and thermal deterioration, comprising the steps of: applying to a surface of said ceramic body, formed as a substrate, a thin layer of a refractory metal; thereafter depositing upon said refractory metal a layer of another metal; and depositing upon said layer of said other metal a high-density substantially impermeable layer of at least one protective compound selected from the group which consists of chromium oxide, zirconium oxide, titanium nitride, tungsten carbide, aluminum oxide, yttrium oxide and aluminum nitride, at least one of said layers being applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer, said layers being deposited in succession on said substrate without removing said substrate from said chamber, said high-density substantially impermeable layer being composed of Cr 2 O 3 , ZrO 2 , Y 2 O 3 or mixtures thereof, during the deposition of said high-density substantially impermeable layer an arc being struck between two electrodes at least one of which consists of chromium, zirconium or yttrium while oxygen is admitted to said chamber.
Claim 7
Independent Claim
176 words
A method of protecting a ceramic body against mechanical and thermal deterioration, comprising the steps of: applying to a surface of said ceramic body, formed as a substrate, a thin layer of a refractory metal; thereafter depositing upon said refractory metal a layer of another metal; and depositing upon said layer of said other metal a high-density substantially impermeable layer of at least one protective compound, at least one of said layers being applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer, each of said layers being applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer.
Claim 8
Independent Claim
176 words
A method of protecting a ceramic body against mechanical and thermal deterioration, comprising the steps of: applying to a surface of said ceramic body, formed as a substrate, a thin layer of a refractory metal; thereafter depositing upon said refractory metal a layer of another metal; and depositing upon said layer of said other metal a high-density substantially impermeable layer of at least one protective compound, at least one of said layers being applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer, each of said layers being applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer.
Claim 9
Dependent Claim
23 words
The method defined in claim 5 wherein said layers are deposited in succession on said substrate without removing said substrate from said chamber.
Claim 10
Independent Claim
196 words
A method of protecting a ceramic body against mechanical and thermal deterioration, comprising the steps of: applying to a surface of said ceramic body, formed as a substrate, a thin layer of a refractory metal; thereafter depositing upon said refractory metal a layer of another metal; and depositing upon said layer of said other metal a high-density substantially impermeable layer of at least one protective compound, at least one of said layers being applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer, said layers being deposited in succession on said substrate without removing said substrate from said chamber, said high-density substantially impermeable layer being composed of Cr 2 O 3 , ZrO 2 , Y 2 O 3 or mixtures thereof and during the deposition of said high-density substantially impermeable layer an arc being struck between two electrodes at least one of which consists of chromium, zirconium or yttrium while oxygen is admitted to said chamber.
Claim 11
Independent Claim
196 words
A method of protecting a ceramic body against mechanical and thermal deterioration, comprising the steps of: applying to a surface of said ceramic body, formed as a substrate, a thin layer of a refractory metal; thereafter depositing upon said refractory metal a layer of another metal; and depositing upon said layer of said other metal a high-density substantially impermeable layer of at least one protective compound, at least one of said layers being applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer, said layers being deposited in succession on said substrate without removing said substrate from said chamber, said high-density substantially impermeable layer being composed of Cr 2 O 3 , ZrO 2 , Y 2 O 3 or mixtures thereof and during the deposition of said high-density substantially impermeable layer an arc being struck between two electrodes at least one of which consists of chromium, zirconium or yttrium while oxygen is admitted to said chamber.
Claim 12
Independent Claim
259 words
A method of protecting a ceramic body against mechanical and thermal deterioration, comprising the steps of: applying to a surface of said ceramic body, formed as a substrate, a thin layer of a refractory metal; thereafter depositing upon said refractory metal a layer of another metal; and depositing upon said layer of said other metal a high-density substantially impermeable layer of at least one protective compound, at least one of said layers being applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer, each of said layers being applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer, said layers being deposited in succession on said substrate without removing said substrate from said chamber, said high-density substantially impermeable layer is composed of Cr 2 O 3 , ZrO 2 , Y 2 O 3 or mixtures thereof and during the deposition of said high-density substantially impermeable layer an arc being struck between two electrodes at least one of which consists of chromium, zirconium or yttrium while oxygen is admitted to said chamber, said substrate being composed of silicon carbide or nitride.
Claim 13
Independent Claim
259 words
A method of protecting a ceramic body against mechanical and thermal deterioration, comprising the steps of: applying to a surface of said ceramic body, formed as a substrate, a thin layer of a refractory metal; thereafter depositing upon said refractory metal a layer of another metal; and depositing upon said layer of said other metal a high-density substantially impermeable layer of at least one protective compound, at least one of said layers being applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer, each of said layers being applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer, said layers being deposited in succession on said substrate without removing said substrate from said chamber, said high-density substantially impermeable layer is composed of Cr 2 O 3 , ZrO 2 , Y 2 O 3 or mixtures thereof and during the deposition of said high-density substantially impermeable layer an arc being struck between two electrodes at least one of which consists of chromium, zirconium or yttrium while oxygen is admitted to said chamber, said substrate being composed of silicon carbide or nitride.
Claim 14
Dependent Claim
14 words
The method defined in claim 8 wherein said refractory metal is titanium or tungsten.
Claim 15
Dependent Claim
12 words
The method defined in claim 9 wherein said other metal is chromium.
Claim 16
Dependent Claim
103 words
A ceramic body protected against mechanical and thermal deterioration by a refractory metal layer bonded directly to said body, a layer of another metal on said refractory metal layer and a high-density substantially impermeable layer of at least one protective compound, on said layer of said other metal, said refractory metal layer being titanium or tungsten and being applied in a thickness of 5 to 10 microns to a silicon carbide or nitride substrate, said other metal is chromium and said high-density substantially impermeable layer is composed of Cr 2 O 3 , ZrO 2 , Y 2 O 3 or mixtures thereof.
Claim 17
Dependent Claim
103 words
A ceramic body protected against mechanical and thermal deterioration by a refractory metal layer bonded directly to said body, a layer of another metal on said refractory metal layer and a high-density substantially impermeable layer of at least one protective compound, on said layer of said other metal, said refractory metal layer being titanium or tungsten and being applied in a thickness of 5 to 10 microns to a silicon carbide or nitride substrate, said other metal is chromium and said high-density substantially impermeable layer is composed of Cr 2 O 3 , ZrO 2 , Y 2 O 3 or mixtures thereof.
Claim 18
Independent Claim
122 words
A method of protecting a ceramic body against mechanical and thermal deterioration, comprising the steps of: applying to a surface of said ceramic body, formed as a substrate composed of silicon carbide or silicon nitride, a thin layer of a refractory metal; thereafter depositing upon said refractory metal a layer of another metal; and depositing upon said layer of said other metal a high-density substantially impermeable layer, each one of said layers being applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer.
Claim 19
Independent Claim
122 words
A method of protecting a ceramic body against mechanical and thermal deterioration, comprising the steps of: applying to a surface of said ceramic body, formed as a substrate composed of silicon carbide or silicon nitride, a thin layer of a refractory metal; thereafter depositing upon said refractory metal a layer of another metal; and depositing upon said layer of said other metal a high-density substantially impermeable layer, each one of said layers being applied by juxtaposing said substrate in an evacuated chamber with a pair of electrodes, at least one of which is composed of a material adapted to form the respective layer, and striking an arc between said electrodes to deposit said material on said substrate to form the respective layer.
Claim 20
Dependent Claim
14 words
The method defined in claim 12 wherein said refractory metal is titanium or tungsten.
Claim 21
Dependent Claim
12 words
The method defined in claim 13 wherein said other metal is chromium.
Claim 22
Independent Claim
103 words
A method of protecting a ceramic body against mechanical and thermal deterioration, comprising the steps of: applying to a surface of said ceramic body, formed as a substrate composed of silicon carbide or silicon nitride, a thin layer of a refractory metal; thereafter depositing upon said refractory metal a layer of another metal; and depositing upon said layer of said other metal a high-density substantially impermeable layer said refractory metal being titanium or tungsten said other metal being chromium, and said high-density substantially impermeable layer being composed of Cr 2 O 3 , ZrO 2 , Y 2 O 3 or mixtures thereof.
Claim 23
Independent Claim
103 words
A method of protecting a ceramic body against mechanical and thermal deterioration, comprising the steps of: applying to a surface of said ceramic body, formed as a substrate composed of silicon carbide or silicon nitride, a thin layer of a refractory metal; thereafter depositing upon said refractory metal a layer of another metal; and depositing upon said layer of said other metal a high-density substantially impermeable layer said refractory metal being titanium or tungsten said other metal being chromium, and said high-density substantially impermeable layer being composed of Cr 2 O 3 , ZrO 2 , Y 2 O 3 or mixtures thereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-08 | 1992-11-07 | 1993-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-08 | 1996-11-07 | 1997-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-08 | 2000-11-07 | 2001-05-09 | $7700.00 | Window Closed / Lapsed |