Inverse shape replication method of making ceramic composite articles
Assignee: Lanxide Technology Co LP
•
Filing: 1986-01-27
•
Granted: 1989-05-09
•
Expires: 2006-01-27
Abstract
Abstract A method of producing a self-supporting ceramic composite body having therein at least one cavity which inversely replicates the geometry of a positive mold of parent metal. The method, includes embedding the mold of parent metal within a conformable bed of filler to provide there in a cavity shaped and filled by the mold. The assembly is heated to melt the parent metal mold, e.g., an aluminum parent metal mold, and contacted with an oxidant to oxidize the molten parent metal to form a polycrystalline material which grows through the surrounding bed of filler, the molten metal being drawn through the growing polycrystalline material to be oxidized at the interface between the oxidant and previously formed oxidation reaction product whereby the cavity formerly filled by the mold of parent metal is eventually evacuated of the metal. There remains behind a cavity whose shape inversely replicates the original shape of the mold. The method provides ceramic composite articles having therein at least one cavity inversely replicating the shape of the mold which supplied the parent metal for oxidation.
Inventors
- 👤 Marc S. Newkirk
- 👤 Andrew W. Urquhart
- 👤 H. Daniel Lesher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 23:23
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/71; C04B35/74; C04B35/01; C04B35/10; C04B35/111; C04B35/117; C04B35/622; C04B35/64; C04B35/65; C04B35/652; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/32; C04B2235/3217; C04B2235/34; C04B2235/3418; C04B2235/38; C04B2235/3817; C04B2235/3826; C04B2235/40; C04B2235/401; C04B2235/402; C04B2235/42; C04B2235/428; C04B2235/60; C04B2235/602; C04B2235/6028; C04B2235/70; C04B2235/80; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249987
Claims Analysis
Total Claims: 39
Claim 1
Independent Claim
436 words
A method for producing a self-supporting ceramic composite body having therein at least one cavity which inversely replicates the geometry of a mold of shaped parent metal, said composite body comprising (1) a ceramic matrix obtained by oxidation of molten parent metal to form a polycrystalline material comprising an oxidation reaction product of said parent metal with an oxidant; and (2) a filler embedded by said matrix, the method comprising the steps of: (a) shaping a parent metal to provide a mold of shaped parent metal; (b) embedding said mold of shaped parent metal within a bed of conformable filler to inversely replicate therein the geometry of said mold of shaped parent metal, said filler being characterized by (1) being permeable to said oxidant under the process conditions in step (c) and being permeable to infiltration by the growth of the oxidation reaction product through said bed of conformable filler, (2) retaining sufficient conformability to provide for accommodation of the melting-point volume change of said parent metal and differential thermal expansion between said parent metal and said bed of conformable filler under the process conditions in step (c) and (3) at least in a support zone thereof enveloping said mold of shaped parent metal, being intrinsically self-bonding only at a temperature above the melting point of said parent metal but below and sufficiently close to the oxidation reaction temperature to allow said accommodation, whereby said filler has sufficient cohesive strength to retain the inversely replicated geometry within said bed of conformable filler under the process conditions in step (c); (c) heating said embedded mold of shaped parent metal to a temperature above its melting point but below the melting point of said oxidation reaction product to form a body of molten parent metal and, at said temperature, (1) reacting the moleten parent metal with said oxidant to form said oxidation reaction product, (2) maintaining at least a portion of said oxidation reaction product in contact with and between said body of molten metal and said oxidant, to progressively draw molten metal from said body of molten metal through the oxidation reaction product and into said bed of filler to concurrently form said cavity in said bed of filler as fresh oxidation reaction product continues to form at an interface between said oxidant and previously formed oxidation reaction product, and (3) continuing said reacting for a time sufficient to at least partially embed said bed of conformable filler with said oxidation reaction product by growth of the oxidation reaction product to form said composite body having said cavity therein; and (d) recovering the resulting self-supporting composite body.
Claim 2
Independent Claim
436 words
A method for producing a self-supporting ceramic composite body having therein at least one cavity which inversely replicates the geometry of a mold of shaped parent metal, said composite body comprising (1) a ceramic matrix obtained by oxidation of molten parent metal to form a polycrystalline material comprising an oxidation reaction product of said parent metal with an oxidant; and (2) a filler embedded by said matrix, the method comprising the steps of: (a) shaping a parent metal to provide a mold of shaped parent metal; (b) embedding said mold of shaped parent metal within a bed of conformable filler to inversely replicate therein the geometry of said mold of shaped parent metal, said filler being characterized by (1) being permeable to said oxidant under the process conditions in step (c) and being permeable to infiltration by the growth of the oxidation reaction product through said bed of conformable filler, (2) retaining sufficient conformability to provide for accommodation of the melting-point volume change of said parent metal and differential thermal expansion between said parent metal and said bed of conformable filler under the process conditions in step (c) and (3) at least in a support zone thereof enveloping said mold of shaped parent metal, being intrinsically self-bonding only at a temperature above the melting point of said parent metal but below and sufficiently close to the oxidation reaction temperature to allow said accommodation, whereby said filler has sufficient cohesive strength to retain the inversely replicated geometry within said bed of conformable filler under the process conditions in step (c); (c) heating said embedded mold of shaped parent metal to a temperature above its melting point but below the melting point of said oxidation reaction product to form a body of molten parent metal and, at said temperature, (1) reacting the moleten parent metal with said oxidant to form said oxidation reaction product, (2) maintaining at least a portion of said oxidation reaction product in contact with and between said body of molten metal and said oxidant, to progressively draw molten metal from said body of molten metal through the oxidation reaction product and into said bed of filler to concurrently form said cavity in said bed of filler as fresh oxidation reaction product continues to form at an interface between said oxidant and previously formed oxidation reaction product, and (3) continuing said reacting for a time sufficient to at least partially embed said bed of conformable filler with said oxidation reaction product by growth of the oxidation reaction product to form said composite body having said cavity therein; and (d) recovering the resulting self-supporting composite body.
Claim 3
Dependent Claim
12 words
The method of claim 1, wherein said oxidant comprises a vapor-phase oxidant.
Claim 4
Dependent Claim
14 words
The method of claim 1, wherein said parent metal comprises an aluminum parent metal.
Claim 5
Dependent Claim
14 words
The method of claim 2, wherein said parent metal comprises an aluminum parent metal.
Claim 6
Dependent Claim
14 words
The method of claim 1, wherein said oxidant comprises a solid at said temperature.
Claim 7
Dependent Claim
22 words
The method of claim 5, wherein said oxidant comprises an oxidant selected from the group consisting of silica, boron and reducible boride.
Claim 8
Dependent Claim
12 words
The method of claim 2, wherein said oxidant comprises an oxygen-containing gas.
Claim 9
Dependent Claim
12 words
The method of claim 2, wherein said oxidant comprises a nitrogen-containing gas.
Claim 10
Dependent Claim
17 words
The method of claim 5 or claim 6, wherein said parent metal comprises an aluminum parent metal.
Claim 11
Dependent Claim
26 words
The method of claim 1 or 2, wherein said parent metal comprises a material selected from the group consisting of silicon, titanium, tin, zirconium and hafnium.
Claim 12
Dependent Claim
60 words
The method of claim 1, claim 2 or claim 3, wherein said oxidant comprises a material selected from the group consisting of an oxygen-containing gas, a nitrogen-containing gas, a halogen, sulphur, phosphorus, arsenic, carbon, boron, selenium, tellurium, an H 2 /H 2 O mixture, methane, ethane, propane, acetylene, ethylene, propylene, and a CO/CO 2 mixture, or compounds or mixtures thereof.
Claim 13
Dependent Claim
13 words
The method of claim 2 or claim 3, wherein said oxidant comprises air.
Claim 14
Dependent Claim
16 words
The method of claim 2, wherein said oxidant comprises an H 2 /H 2 O mixture.
Claim 15
Dependent Claim
13 words
The method of claim 2, wherein said oxidant comprises a CO/CO 2 mixture.
Claim 16
Dependent Claim
14 words
The method of claim 2 or claim 3, wherein said oxidant comprises forming gas.
Claim 17
Dependent Claim
46 words
The method of claim 1, claim 2 or claim 3, wherein said filler comprises a material selected from the group consisting of hollow bodies, particulates, powders, fibers, whiskers, spheres, bubbles, steelwool, plates, aggregate, wires, rods, bars, platelets, pellets, tubes, refractory fiber cloth, tubules, or mixtures thereof.
Claim 18
Dependent Claim
50 words
The method of claim 1, claim 2 or claim 3, wherein said filler comprises a material selected from the group consisting of at least one single metal oxide of a metal selected from the group consisting of aluminum, cerium, hafnium, lanthanum, neodymium, praseodymium, samarium, scandium, thorium, uranium, yttrium, and zirconium.
Claim 19
Dependent Claim
51 words
The method of claim 1, claim 2 or claim 3, wherein said filler comprises a material selected from the group consisting of at least one of aluminum oxide, silica, silicon carbide, silicon aluminum oxynitride, zirconium oxide, barium titanate, boron nitride, silicon nitride, magnesium aluminate, ferrous alloys, iron-chromium-aluminum alloy, carbon and aluminum.
Claim 20
Dependent Claim
17 words
The method of claim 1, claim 2 or claim 3, wherein said filler comprises a solid oxidant.
Claim 21
Dependent Claim
22 words
The method of claim 18, wherein said filler comprises a material selected from the group consisting of silica, silicon carbide and alumina.
Claim 22
Dependent Claim
24 words
The method of claim 3, wherein said oxidant comprises an oxygen-containing gas and said temperature is from about 850° C. to about 1450° C.
Claim 23
Dependent Claim
24 words
The method of claim 3, wherein said oxidant comprises an oxygen-containing gas and said temperature is from about 900° C. to about 1350° C.
Claim 24
Dependent Claim
14 words
The method of claim 1, wherein said oxidant comprises a liquid at said temperature.
Claim 25
Dependent Claim
14 words
The method of claim 1, further comprising doping said parent metal with a dopant.
Claim 26
Dependent Claim
14 words
The method of claim 2, further comprising doping said parent metal with a dopant.
Claim 27
Dependent Claim
14 words
The method of claim 3, further comprising doping said parent metal with a dopant.
Claim 28
Dependent Claim
21 words
The method of claim 24, claim 25 or claim 26, wherein at least one dopant is alloyed into the parent metal.
Claim 29
Dependent Claim
49 words
The method of claim 24, claim 25 or claim 26, wherein at least one dopant is applied as a alyer of dopant material onto a surface of said parent metal, and including forming the oxidation reaction product through and beyond the depth of the applied layer of dopant material.
Claim 30
Dependent Claim
24 words
The method of claim 24, claim 25 or claim 26, further comprising providing at least one dopant material at least partially within said filler.
Claim 31
Dependent Claim
43 words
The method of claim 24, claim 25 or claim 26, wherein said dopant comprises a source of at least two materials from the group consisting of magnesium, zinc, silicon, germanium, tin, lead, boron, sodium, lithium, calcium, phosphorus, yttrium, and a rare earth metal.
Claim 32
Dependent Claim
25 words
The method of claim 30, wherein said rare earth metal comprises a material selected from the group consisting of lanthanum, cerium, praseodymium, neodymium and samarium.
Claim 33
Dependent Claim
45 words
The method of claim 24, claim 25 or claim 26, wherein said dopant material comprises a source of at least one material selected from the group consisting of magnesium, zinc, silicon, germanium, tin, lead, boron, sodium, lithium, calcium, phosphorus, yttrium and a rare earth metal.
Claim 34
Dependent Claim
25 words
The method of claim 32, wherein said rare earth metal comprises a material selected from the group consisting of lanthanum, cerium, praseodymium, neodymium and samarium.
Claim 35
Independent Claim
27 words
The method of claims 1, 2, 3, 21, 22 or 24, further comprising incorporating a bonding agent into said filler, at least in said support zone thereof.
Claim 36
Dependent Claim
32 words
The method of claim 24, wherein said polycrystalline material further comprises an initiation surface of a spinel formed as an oxidation reaction product of said parent metal, said dopant and said oxidant.
Claim 37
Dependent Claim
34 words
The method of claim 35, wherein said dopant comprises at least one material selected from the group consisting of magnesium and a source of magnesium, and said parent metal comprises an aluminum parent metal.
Claim 38
Dependent Claim
34 words
The method of claim 24, claim 25 or claim 26, further comprising at least one of alloying a dopant with said parent metal and applying an alloy to a surface of said parent metal.
Claim 39
Dependent Claim
20 words
The method of claim 37, further comprising incorporating at least one dopant into at least a portion of said filler.
References Cited (Backward Citations)
US2741822A
Cited
US3255027A
Cited
US3298842A
Cited
US3296002A
Cited
US3419404A
Cited
US3473987A
Cited
US3421863A
Cited
US3437468A
Cited
US3789096A
Cited
US3473938A
Cited
US3538231A
Cited
US3864154A
Cited
US3973977A
Cited
EP0116809A1
Cited
EP0155831A2
Cited
EP0169067A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-08 | 1992-11-07 | 1993-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-08 | 1996-11-07 | 1997-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-08 | 2000-11-07 | 2001-05-09 | $7700.00 | Window Closed / Lapsed |