Method of manufacturing a contoured elastomeric pad
Assignee: Boeing Co
•
Filing: 1987-05-28
•
Granted: 1989-04-25
•
Expires: 2007-05-28
Abstract
Abstract Uncured elastomeric sheet material (42) is built up on the outer surface of a production article (36) constructed from composite materials. A vacuum bag system (20, 24, 26, 30, 32) is used for holding the uncured elastomer member (60) against the composite article (36) while the elastomer member (60) is being cured under heat and pressure. Such curing causes the elastomer member (60) to shrink. The elastomer member (60) is then resized by cutting it into sections (66). The sections (66) are placed back on the composite article (36) and each is positioned on such article (36) at a location best conforming to it in shape. This leaves gaps (68) between the sections (66). Additional uncured elastomer (70) is applied to fill the gaps (68) and bridge across the gaps (68), to in that manner splice the sections (66) together. A vacuum bag (20, 24, 26, 30, 32) is again applied and the bag assembly (20, 24, 26, 30, 32 ) is again cured under heat and pressure, to cure the additional elastomer material (70). The elastomer member (60") formed in this manner substantially conforms in size and shape to the production composite article (36) and can be used as a pressure pad in the manufacture of additional articles (36) of the composite material.
Inventors
- 👤 James F. Yeager
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 06:42
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/04; B29C70/28; B29C70/30; B29C70/34; B29C70/342; B29C33/00; B29C33/38; B29C33/40; B29C33/405; B29C37/00; B29C37/005; B29C41/00; B29C41/02; B29C41/12; B29C43/00; B29C43/32; B29C43/36; B29C43/3642; B29C43/54; B29C70/54; B29C70/549; B29D; B29D22/00; B29C2043/3644; B29C2043/3655; B29C2791/00; B29C2791/001; B29C2793/00; B29C43/02; B29C43/10; B29C43/12; B29K; B29K2021/00; B29K2083/00; B29K2105/00; B29K2105/24; B29K2105/243; B29K2105/246; B29K2821/00; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1052; Y10T156/1062; Y10T156/1075
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
193 words
A method of manufacturing a contoured pressure pad of a type used for applying pressure to a contoured composite part during curing of said part, comprising: providing a previously manufactured composite part of the desired size and contour, to serve as a form for the pressure pad; applying uncured, heat curable elastomer to said part, to form on said part an uncured elastomeric member of desired thickness; heat curing said elastomeric member while it is on said part; and resizing the elastomeric member to correct for shrinkage caused by the heat curing, comprising: cutting the cured elastomeric member into sections; positioning the sections on the part, each on a region of the part to which it substantially conforms in size and shape; applying additional uncured elastomeric material to fill gaps between the sections and splicing the sections together; and heat curing the additional uncured elastomeric material while the elastomeric member is on the part, to unify the elastomeric member and substantially conform its inner surface to the contour of the part, enabling the member to be used as a pressure pad in the manufacture of additional parts of the same size and shape.
Claim 2
Independent Claim
193 words
A method of manufacturing a contoured pressure pad of a type used for applying pressure to a contoured composite part during curing of said part, comprising: providing a previously manufactured composite part of the desired size and contour, to serve as a form for the pressure pad; applying uncured, heat curable elastomer to said part, to form on said part an uncured elastomeric member of desired thickness; heat curing said elastomeric member while it is on said part; and resizing the elastomeric member to correct for shrinkage caused by the heat curing, comprising: cutting the cured elastomeric member into sections; positioning the sections on the part, each on a region of the part to which it substantially conforms in size and shape; applying additional uncured elastomeric material to fill gaps between the sections and splicing the sections together; and heat curing the additional uncured elastomeric material while the elastomeric member is on the part, to unify the elastomeric member and substantially conform its inner surface to the contour of the part, enabling the member to be used as a pressure pad in the manufacture of additional parts of the same size and shape.
Claim 3
Dependent Claim
54 words
The method of claim 1, comprising obtaining the uncured, heat curable elastomer in sheet form, cutting pieces from said sheet elastomer and applying the pieces to the part to cover the part, including pressing the elastomer tightly to the part surface to remove all entrapped air, and joining the pieces by overlapping the pieces.
Claim 4
Dependent Claim
57 words
The method of claim 1, comprising using a previously manufactured composite part which has not yet been trimmed to its final net trimmed dimensions, and which includes a border portion, and during the manufacture of the pressure pad applying the elastomer to said border portion, so that the pressure pad will have a substantially corresponding border portion.
Claim 5
Dependent Claim
88 words
The method of claim 1, comprising perforating the uncured, heat curable elastomer, providing a vacuum bag over the uncured elastomeric member and sealing it about said member and the part on which the member is formed, and evacuating the region between the bag and the part, to cause atmospheric pressure to push the bag into pressure applying engagement with the uncured elastomeric member, and then placing the bagged assembly into a chamber and subjecting it to heat and pressure within said chamber for curing the uncured elastomeric member.
Claim 6
Dependent Claim
38 words
The method of claim 1, comprising removing the elastomeric member from the part following curing, and filling any voids or incomplete splices on the side of the member which was against the part with an elastomeric filler material.
Claim 7
Dependent Claim
85 words
The method of claim 1, comprising using a previously manufactured composite part which has not yet been trimmed to its final net trimmed dimensions, and which includes a border portion, and obtaining the uncured, heat curable elastomer in sheet form, cutting pieces from said sheet elastomer and applying the pieces to the part to cover the part, including its said border portion, and including pressing the elastomer tightly to the part surface to remove all entrapped air, and joining the pieces by overlapping the pieces.
Claim 8
Dependent Claim
88 words
The method of claim 6, comprising perforating the uncured, heat curable elastomer, providing a vacuum bag over the uncured elastomeric member and sealing it about said member and the part on which the member is formed, and evacuating the region between the bag and the part, to cause atmospheric pressure to push the bag into pressure applying engagement with the uncured elastomeric member, and then placing the bagged assembly into a chamber and subjecting it to heat and pressure within said chamber for curing the uncured elastomeric member.
Claim 9
Independent Claim
141 words
A method of manufacturing a contoured elastomeric pad, comprising: providing a form having a contoured forming surface; applying uncured, heat curable elastomer to said form, to form on said form an uncured elastomeric member of desired thickness; heat curing said elastomeric member while it is on said form; and resizing the elastomeric member to correct for shrinkage caused by the heat curing, comprising: cutting the cured elastomeric member into sections; positioning the sections on the form, each on a region of the form to which it substantially conforms in size and shape; applying additional uncured elastomeric material to fill gaps between the sections and splicing the sections together; and heat curing the additional uncured elastomeric material while the elastomeric member is on the form, to unify the elastomeric member and substantially conform its inner surface to the contour of the form.
Claim 10
Independent Claim
141 words
A method of manufacturing a contoured elastomeric pad, comprising: providing a form having a contoured forming surface; applying uncured, heat curable elastomer to said form, to form on said form an uncured elastomeric member of desired thickness; heat curing said elastomeric member while it is on said form; and resizing the elastomeric member to correct for shrinkage caused by the heat curing, comprising: cutting the cured elastomeric member into sections; positioning the sections on the form, each on a region of the form to which it substantially conforms in size and shape; applying additional uncured elastomeric material to fill gaps between the sections and splicing the sections together; and heat curing the additional uncured elastomeric material while the elastomeric member is on the form, to unify the elastomeric member and substantially conform its inner surface to the contour of the form.
Claim 11
Dependent Claim
54 words
The method of claim 8, comprising obtaining the uncured, heat curable elastomer in sheet form, cutting pieces from said sheet elastomer and applying the pieces to the form to cover the form, including pressing the elastomer tightly to the form surface to remove all entrapped air, and joining the pieces by overlapping the pieces.
Claim 12
Dependent Claim
88 words
The method of claim 3, comprising perforating the uncured, heat curable elastomer, providing a vacuum bag over the uncured elastomeric member and sealing it about said member and the form on which the member is formed, and evacuating the region between the bag and the form, to cause atmospheric pressure to push the bag into pressure applying engagement with the uncured elastomeric member, and then placing the bagged assembly into a chamber and subjecting it to heat and pressure within said chamber for curing the uncured elastomeric member.
References Cited (Backward Citations)
US2297204A
Cited
US2313508A
Cited
US2290640A
Cited
US2568292A
Cited
US3165569A
Cited
US3308223A
Cited
US3860470A
Cited
US3773598A
Cited
US3795559A
Cited
US3883627A
Cited
US4456496A
Cited
US4219601A
Cited
US4352843A
Cited
US4405539A
Cited
US4401496A
Cited
US4435242A
Cited
US4620890A
Cited
US4554036A
Cited
US4652319A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-24 | 1992-10-24 | 1993-04-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-24 | 1996-10-24 | 1997-04-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-24 | 2000-10-24 | 2001-04-25 | $7700.00 | Window Closed / Lapsed |