Claim 1

Independent Claim 148 words

A process of manufacturing a polarization preserving birefringent optical fiber comprising the steps of: heating a composite of a core member and cladding member of soft glasses; drawing the core and cladding members to unite and reduce the dimensions of the core and cladding members, to thereby form a fiber; transporting the drawn core and cladding through a molten metallic bath, having a predetermined temperature gradient transverse to the transportation path, at sufficient speed and at sufficient said temperature gradient to coat the drawn fiber with a sufficient variation in coating thickness about the cladding to provide an anisotropic compressional strain, when the molten metal solidifies about the cladding, to create an anisotropy of the refractive index of the core member sufficient for polarization preservation, and cooling the coated molten metal to provide the desired variation in coating thickness to thereby form a metal-coated polarization preserving optical fiber.

Claim 2

Dependent Claim 148 words

A process of manufacturing a polarization preserving birefringent optical fiber comprising the steps of: heating a composite of a core member and cladding member of soft glasses; drawing the core and cladding members to unite and reduce the dimensions of the core and cladding members, to thereby form a fiber; transporting the drawn core and cladding through a molten metallic bath, having a predetermined temperature gradient transverse to the transportation path, at sufficient speed and at sufficient said temperature gradient to coat the drawn fiber with a sufficient variation in coating thickness about the cladding to provide an anisotropic compressional strain, when the molten metal solidifies about the cladding, to create an anisotropy of the refractive index of the core member sufficient for polarization preservation, and cooling the coated molten metal to provide the desired variation in coating thickness to thereby form a metal-coated polarization preserving optical fiber.

Claim 3

Dependent Claim 37 words

The process of claim 1 wherein the core had an initial diameter of 0.5 mm and was loosely fitted within a cladding cylinder of an inner diameter of 1 mm and an outer diameter of 0.5 inches.

Claim 4

Dependent Claim 22 words

The process of claim 1 wherein the composite core and cladding are heated within the range of 700° C. to 800° C.

Claim 5

Dependent Claim 24 words

The process of claim 2 wherein the composite core and cladding were drawn to a reduced dimension of approximately one thousandth its original size.

Claim 6

Dependent Claim 21 words

The process of claim 3 wherein the drawn fiber was transported in the range of 0.5 to 1 meters per second.

Claim 7

Dependent Claim 26 words

The process of claim 5 wherein the temperature gradient varies by approximately 10° C. to 20° C. across the drawn fiber in the molten metallic bath.

Claim 8

Dependent Claim 166 words

A process of forming a polarization preserving birefringent fiber optic member comprising: inserting a solid glass rod core member into a hollow cylindrical tube of a different index of refraction; heating the rod and tubes to a temperature range to soften the rod and tube sufficiently for drawing them into a reduced elongated cylindrical drawn fiber and at the same time drawing them into a fiber; transporting the drawn fiber through a liquid coating bath having a predetermined temperature gradient transverse to the transportation path, at sufficient speed and at sufficient said temperature gradient to deposit a sufficient variation in coating thickness about the drawn fiber to provide an anisotropic compressional strain, when the liquid solidifies about the fiber, to create an anisotropy of index of refraction of the core member sufficient to preserve polarization of transmitted light, and cooling the coated fiber to provide the desired anisotropic variation in coating thickness and to form an optical fiber coated with solidified liquid as a fiber jacket.

Claim 9

Dependent Claim 166 words

A process of forming a polarization preserving birefringent fiber optic member comprising: inserting a solid glass rod core member into a hollow cylindrical tube of a different index of refraction; heating the rod and tubes to a temperature range to soften the rod and tube sufficiently for drawing them into a reduced elongated cylindrical drawn fiber and at the same time drawing them into a fiber; transporting the drawn fiber through a liquid coating bath having a predetermined temperature gradient transverse to the transportation path, at sufficient speed and at sufficient said temperature gradient to deposit a sufficient variation in coating thickness about the drawn fiber to provide an anisotropic compressional strain, when the liquid solidifies about the fiber, to create an anisotropy of index of refraction of the core member sufficient to preserve polarization of transmitted light, and cooling the coated fiber to provide the desired anisotropic variation in coating thickness and to form an optical fiber coated with solidified liquid as a fiber jacket.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1992-04-24	1992-10-24	1993-04-25	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1996-04-24	1996-10-24	1997-04-25	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	2000-04-24	2000-10-24	2001-04-25	$7700.00	Window Closed / Lapsed

Polarization preserving optical fiber and method of manufacturing

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag