Low shrink hybrid resins
Assignee: Reichhold Chemicals Inc
•
Filing: 1987-08-03
•
Granted: 1989-04-18
•
Expires: 2007-08-03
Abstract
Abstract Unsaturated polyester compositions comprising (a) an unsaturated polyester prepolymer and (b) a vinyl monomer copolymerizable with the prepolymer, which are cured by addition of (c) a polyisocyanate, (d) a peroxide catalyst and, optionally, (e) a peroxide activator and a urethane catalyst.
Inventors
- 👤 Douglas G. Vanderlaan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 20:17
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/67; C08G18/68; C08G63/00; C08G63/02; C08G63/12; C08G63/52; C08L; C08L67/00; C08L67/06
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
194 words
An hydroxyl functional unsaturated polyester resin composition for use in a molding composition consisting essentially of: (A) at least 70 parts by weight by an alpha, betaethylenically unsaturated polyester having an acid number of less than 40 and an hydroxyl number of about 20 to 300, and a molecular weight of about 300 to 20,000, consisting essentially of the reaction product of: (a) at least one alpha,beta-ethylenically unsaturated dicarboxylic acid, anhydride, or derivative thereof; (b) at least one other non-alpha,betaethylenically unsaturated dicarboxylic acid, polycaboxylic acid, anhydride, diester or corresponding derivative thereof; (c) at least one polyol; (B) not more than 30 parts by weight of an ethylenically unsaturated monomer polymerizable with (A); (C) a polyisocyanate in an amount such that the molar ratio of hydroxyl groups to isocyanate varies from about 0.5 to 2.0; (D) a radical initiator; and wherein the amount of the alpha, beta-ethylenically unsaturated carboxylic acid component of said composition varies from at least about 20 to about 35 mole % of the total dicarboxylic acid residue of said composition; and wherein said composition has shrinkage upon molding of less than 1%, and a Barcol hardness of about 15 to 21.
Claim 2
Dependent Claim
194 words
An hydroxyl functional unsaturated polyester resin composition for use in a molding composition consisting essentially of: (A) at least 70 parts by weight by an alpha, betaethylenically unsaturated polyester having an acid number of less than 40 and an hydroxyl number of about 20 to 300, and a molecular weight of about 300 to 20,000, consisting essentially of the reaction product of: (a) at least one alpha,beta-ethylenically unsaturated dicarboxylic acid, anhydride, or derivative thereof; (b) at least one other non-alpha,betaethylenically unsaturated dicarboxylic acid, polycaboxylic acid, anhydride, diester or corresponding derivative thereof; (c) at least one polyol; (B) not more than 30 parts by weight of an ethylenically unsaturated monomer polymerizable with (A); (C) a polyisocyanate in an amount such that the molar ratio of hydroxyl groups to isocyanate varies from about 0.5 to 2.0; (D) a radical initiator; and wherein the amount of the alpha, beta-ethylenically unsaturated carboxylic acid component of said composition varies from at least about 20 to about 35 mole % of the total dicarboxylic acid residue of said composition; and wherein said composition has shrinkage upon molding of less than 1%, and a Barcol hardness of about 15 to 21.
Claim 3
Dependent Claim
37 words
The composition of claim 1, wherein the amount of polyol used is such that the ratio of hydroxyl groups in the polyol (c) to the sum of carboxyl groups in (a) and (b) is greater than 1.
Claim 4
Dependent Claim
30 words
The composition of claim 1, wherein the polyol is at least one glycol selected from the group consisting of ethylene glycol, diethylene glycol, 1,4-butanediol, 1,3-propanediol, 1,5-pentanediol, 1,6-hexanediol and neopentyl glycol.
Claim 5
Dependent Claim
35 words
The composition of claim 1, wherein the alpha, beta-ethylenically unsaturated carboxylic acid is maleic anhydride, the non-ethylenically unsaturated carboxylic acid isophthalic acid, the polyhydric alcohol is diethylene glycol and the ethylenically unsaturated monomer is styrene.
Claim 6
Dependent Claim
31 words
The composition of claim 1, wherein (a) the alpha,beta-ethylenically unsaturated dicarboxylic acid is selected from the group consisting of maleic acid, fumaric acid, itaconic acid, methyl maleic acid and mixtures thereof.
Claim 7
Dependent Claim
38 words
The composition of claim 1, wherein (b) is selected from the group consisting of phthalic acid, phthalic anhydride, isophthalic acid, terephthalic acid, adipic acid, dodecanoic acid, glutaric acid, endomethylenetetrahydrophthalic anhydride, succinic acid, succinic anhydride, dimethylterephthalate and mixtures thereof.
Claim 8
Dependent Claim
27 words
The composition of claim 2, wherein said polyol is selected from the group consisting of glycerol, pentaerythritol, trimethylolethane, trimethylolpropane, 1,2,6-hexanetriol, sorbitol, inositol, polyvinyl alcohol and mixtures thereof.
Claim 9
Dependent Claim
52 words
The composition of claim 1, wherein the ethylenically unsaturated monomers are selected from the group consisting of styrene, ortho, meta and para alkyl styrenes, divinylbenzene, vinyl toluene, alpha-methyl styrene, chlorostyrenes, vinyl pyridine, acrylic acid, methacrylic acid, esters of acrylic acid, esters of methacrylic acid, diallylphthalate, isophthalic acid diallyl ester and mixtures thereof.
Claim 10
Dependent Claim
47 words
The composition of claim 1, wherein the polyisocyanate is an aliphatic, cycloaliphatic, or aromatic diisocyanate containing 6 to 18 carbon atoms, selected from the group consisting of 1,6-hexamethylene diisocyanate, 2,4' and 4,4' dicyclohexyl-methane diisocyanate, isophorone diisocyanate, 2,4- and 2,6-tolylene diisocyanate, 2,4' and 4,4'-diphenylmethane diisocyanate and mixtures thereof.
Claim 11
Dependent Claim
29 words
The composition of claim 1, wherein the hydroxyl functional unsaturated polyester has an acid number of about 0.1 to 5.0 and an hydroxyl number of about 50 to 150.
Claim 12
Dependent Claim
20 words
The composition of claim 1, wherein the hydroxyl functional unsaturated polyester has a molecular weight of about 500 to 2,000.
Claim 13
Dependent Claim
22 words
The composition of claim 1, wherein the tensile strength is about 9,000 psi and the % elongation at break is about 3.90.
Claim 14
Dependent Claim
21 words
A molded article formed from the composition of claim 1, selected from the group consisting of bowling balls and baseball bats.
Claim 15
Dependent Claim
30 words
The composition of claim 1, wherein the radical initiator is selected from the group consisting of benzoyl peroxide, methyl ethyl ketone hydroperoxide, cumene hydroperoxide, tert-butyl peroxybenzoate, cyclohexanone hydroperoxide, and azobisisobutyrodinitrile.
Claim 16
Dependent Claim
11 words
The composition of claim 1, also including a peroxide decomposition promoter.
Claim 17
Dependent Claim
27 words
The composition of claim 15, wherein the peroxide decomposition promoter is selected from the group consisting of cobalt naphthenate, cobalt octoate, dimethylaniline, diethylaniline, dimethyl-p-toluidine, and mixtures thereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-17 | 1992-10-17 | 1993-04-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-17 | 1996-10-17 | 1997-04-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-17 | 2000-10-17 | 2001-04-18 | $7700.00 | Window Closed / Lapsed |