Ceramic composite structures having intrinsically fitted encasement members thereon & methods of making the same
Assignee: Lanxide Technology Co LP
•
Filing: 1988-06-24
•
Granted: 1989-04-18
•
Expires: 2008-06-24
Abstract
Abstract A method is provided of producing a self-supporting ceramic composite structure having one or more encasement members, such as an encasing steel sleeve, joined to it by growth of the ceramic material to engagement surface(s) of the encasement member(s). A parent metal is contacted with a body of filler which is encased by the encasement member(s). The resulting assembly is heated to melt and oxidize the parent metal, e.g., aluminum, to form a polycrystalline material comprising an oxidation reaction product which grows through the doby of filler and stops at the engagement surface(s) of the encasement member(s) which thereby determines the surface geometry of the grown ceramic matrix. Upon cooling, the encasement member(s) is shrink-fitted about the ceramic composite body. The invention also provides the resultant articles, for example, a ceramic composite body having a stainless steel member affixed thereto.
Inventors
- 👤 Marc S. Newkirk
- 👤 H. Daniel Lesher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 08:33
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/64; C04B35/65; C04B35/652; F; F41; F41A; F41A21/00; F41A21/02; Y; Y10; Y10S; Y10S264/00; Y10S264/25; Y10S264/36
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
310 words
A method for producing a ceramic composite body maintained under compressive stress by an encasement member, said composite body comprising (1) a ceramic matrix obtained by oxidation of a parent metal to form a polycrystalline material comprising (i) an oxidation reaction product of said parent metal with an oxidant and (2) a mass of filler embedded by said matrix, the method comprising steps of: (a) heating a parent metal to a temperature region above its melting point but below the melting point of its oxidation reaction product to form a body of molten parent metal; (b) contacting said molten parent metal with a mass of filler material in the presence of an oxidant, at least a portion of said filler being contained within an encasement member and said filler being in conforming engagement with at least a portion of an interior surface of said encasement member, whereby said interior surface defines a surface boundary of said mass of filler material so that formation of oxidation reaction product will occur in a direction toward and into said dmass of filler material; and (c) at aid temperature region (1) reacting said molten metal with said oxidant to form said oxidation reaction product, (2) maintaining at least a portion of said oxidation reaction product in contact with and between said molten parent metal and said oxidant, to progressively draw molten parent metal through the oxidation reaction product towards the oxidant so that fresh oxidation reaction product forms within said filler at an interface between s aid oxdant and previously formed oxidation reaction product, and (3) continuing said reaction until said polycrystalline material has infiltrated said filler to at least a portion of said surface boundary to produce said ceramic composite body, and (4) recovering said ceramic composite body having said encasement member intrinsically fitted thereon for maintaining said composite body under compressive stress.
Claim 2
Independent Claim
310 words
A method for producing a ceramic composite body maintained under compressive stress by an encasement member, said composite body comprising (1) a ceramic matrix obtained by oxidation of a parent metal to form a polycrystalline material comprising (i) an oxidation reaction product of said parent metal with an oxidant and (2) a mass of filler embedded by said matrix, the method comprising steps of: (a) heating a parent metal to a temperature region above its melting point but below the melting point of its oxidation reaction product to form a body of molten parent metal; (b) contacting said molten parent metal with a mass of filler material in the presence of an oxidant, at least a portion of said filler being contained within an encasement member and said filler being in conforming engagement with at least a portion of an interior surface of said encasement member, whereby said interior surface defines a surface boundary of said mass of filler material so that formation of oxidation reaction product will occur in a direction toward and into said dmass of filler material; and (c) at aid temperature region (1) reacting said molten metal with said oxidant to form said oxidation reaction product, (2) maintaining at least a portion of said oxidation reaction product in contact with and between said molten parent metal and said oxidant, to progressively draw molten parent metal through the oxidation reaction product towards the oxidant so that fresh oxidation reaction product forms within said filler at an interface between s aid oxdant and previously formed oxidation reaction product, and (3) continuing said reaction until said polycrystalline material has infiltrated said filler to at least a portion of said surface boundary to produce said ceramic composite body, and (4) recovering said ceramic composite body having said encasement member intrinsically fitted thereon for maintaining said composite body under compressive stress.
Claim 3
Dependent Claim
11 words
The method of claim 1, wherein said parent metal comprises aluminum.
Claim 4
Dependent Claim
30 words
The method of claim 2, wherein said oxidant comprises an oxygen-containing gas, said oxidation reaction product comprises alumina, and said temperature region is from about 850° C. to 1450° C.
Claim 5
Dependent Claim
11 words
The method of claim 3, wherein said oxygen-containing gas comprises air.
Claim 6
Dependent Claim
43 words
The method of any of claim 1, 2, 3, or 4, wherein said oxidant comprises a vapor-phase oxidant used in combination with at least one of a solid oxidant and a liquid oxidant incorporated into at least a portion of said filler material.
Claim 7
Dependent Claim
35 words
The method of claim 5, wherein said solid oxidant comprises a material selected from the group consisting of silica, boron, and metal borides which are reducible under the process conditions set forth in steps (a)-(c).
Claim 8
Dependent Claim
30 words
The method of any of claim 1, 3 or 4, wherein said parent metal comprises a metal selected from the group consisting of aluminum, silicon, titanium, tin, zirconium, and hafnium.
Claim 9
Independent Claim
31 words
The method of claims 1, 2, 3, or 4, wherein said filler comprises a material selected from the group consisting of silica, silicon carbide, alumina, zirconia, magnesium aluminate, and mixtures thereof.
Claim 10
Independent Claim
23 words
The method of any of claims 1, 2, 3 or 4, wherein said parent metal is combined with at least one dopant material.
Claim 11
Dependent Claim
26 words
The method of claim 1, wherein said oxidant comprises a vapor-phase oxidant, and said encasement member and said filler material are permeable to said vapor-phase oxidant.
Claim 12
Dependent Claim
19 words
The method of claim 10, wherein said encasement member comprises an inner reticulated liner and an outer, rigid sleeve.
Claim 13
Independent Claim
43 words
The method of any of claims 1, 2, 3 or 4, wherein said encasement member comprises a metal selected from the group consisting of a stainless steel, and INCONEL metal, a FECRAL metal, a FECRALLOY metal, a HASTALLOY metal and an INCOLOY metal.
Claim 14
Dependent Claim
25 words
The method of claim 1 or claim 2, wherein said encasement member comprises a metal selected from the group consisting of titanium, zirconium and steel.
Claim 15
Dependent Claim
28 words
The method of claim 1, wherein said encasement member comprises a material having a coefficient of thermal expansion which is greater than that of said ceramic composite body.
Claim 16
Dependent Claim
42 words
The method of claim 1 or claim 2, wherein said encasement member includes a protective layer which prevents any substantial attack by said parent metal, filler and oxidant upon said encasement member under the process conditions s et forth in steps (a)-(c).
Claim 17
Dependent Claim
46 words
The method of claim 1, wherein said parent metal is shaped to a pattern configured at least in a region thereof inversely to a bore of a gun barrel and embedding at least a portion of said pattern in said filler prior to step (a) therein.
References Cited (Backward Citations)
US2741822A
Cited
US3255027A
Cited
US3298842A
Cited
US3296002A
Cited
US3419404A
Cited
US3473987A
Cited
US3421863A
Cited
US3437468A
Cited
US3789096A
Cited
US3473938A
Cited
US3538231A
Cited
US3864154A
Cited
US3973977A
Cited
US4435455A
Cited
EP0116809A1
Cited
EP0155831A2
Cited
US4641450A
Cited
EP0169067A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-17 | 1992-10-17 | 1993-04-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-17 | 1996-10-17 | 1997-04-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-17 | 2000-10-17 | 2001-04-18 | $7700.00 | Window Closed / Lapsed |