Reinforcing material
Assignee: Individual
•
Filing: 1986-11-13
•
Granted: 1989-04-11
•
Expires: 2006-11-13
Abstract
Abstract The invention relates to a reinforcing material for duroplastics and a process of preparing the same by embedding hollow body fillers (microspheres) in the interspaces of the fibers of a web, knitted fabric or stitch bonded products of fibers having a high modulus of elasticity. By virtue of the incorporation of the hollow body fillers, the particle diameter of which amounts to between 20 and 300 μm, the absorbing capacity for liquid curable resins can be adjusted to the desired value. The process of the subject invention teaches to incorporate the unexpanded preform of a hollow body filler into the interspaces of the fibers and to subject the so-obtained material for a sufficient period of time to the temperature necessary for the blowing process of the preform. The reinforcing material can be used for preparing light laminates of duroplastic materials (FIG. 1).
Inventors
- 👤 Klaus K. Kolzer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 22:10
CPC Classifications
D; D04; D04H; D04H3/00; D04H3/08; D04H3/12; B; B29; B29C; B29C51/00; B29C51/12; B29B; B29B15/00; B29B15/08; B29B15/10; B29B15/12; B29C67/00; B29C67/24; B29C70/00; B29C70/02; B29C70/021; B29C70/025; B29C70/04; B29C70/06; B29C70/10; B29C70/16; B29C70/20; B29C70/58; B29C70/66; D04H1/00; D04H1/40; D04H1/413; D04H1/42; D04H1/4209; D04H1/4218; D04H1/58; D04H1/587; D04H1/64; D04H3/002; D04H3/004; D04H3/005; D04H3/009; D04H3/02; D04H3/04; B29K; B29K2105/00; B29K2105/06; B29K2105/08; B29K2105/10; B29K2105/101; B29K2105/16; B29K2105/165; Y; Y10; Y10S; Y10S428/00; Y10S428/902; Y10T; Y10T428/00; Y10T428/249921; Y10T428/25; Y10T428/254; Y10T428/29; Y10T428/2982; Y10T428/30; Y10T442/00; Y10T442/20; Y10T442/2139
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
83 words
A reinforcing material for duroplastics in the form of a roving, a yarn or a loosely spun double yarn of continuous elementary filaments arranged parallel with a high modulus of elasticity, characterized by a substantial part of the parallel elementary filaments free of any binding agent being spread apart or separated, by the cavities between the elementary filaments being predominantly filled by hollow plastic microspheres with a diameter of 20 to 300 μm and the resin pick up and specific weight being reduced.
Claim 2
Dependent Claim
83 words
A reinforcing material for duroplastics in the form of a roving, a yarn or a loosely spun double yarn of continuous elementary filaments arranged parallel with a high modulus of elasticity, characterized by a substantial part of the parallel elementary filaments free of any binding agent being spread apart or separated, by the cavities between the elementary filaments being predominantly filled by hollow plastic microspheres with a diameter of 20 to 300 μm and the resin pick up and specific weight being reduced.
Claim 3
Dependent Claim
56 words
A reinforcing material according to claim 1 characterized by the hollow microspheres being embedded in such an amount, that the thickness of the unbonded roving, yarn or loosely spun double yarn produced is in particular the 5- to 10-fold of 2- to 30-fold, in particular the 5- to 10-fold of the thickness of the starting material.
Claim 4
Dependent Claim
89 words
A reinforcing material for duroplastics in the form of a web, knitted fabric or stitch bonded product of yarn, roving or loosely spun double yarn with continuous parallel arranged elementary filaments with a high modulus of elasticity characterized by a substantial part of the parallel elementary filaments free of any binding agent being spread apart or separated, by these cavities between the elementary filaments being predominantly filled by hollow plastic microspheres with a diameter of 20 to 300 μm and the resin pick up and specific weight being reduced.
Claim 5
Dependent Claim
89 words
A reinforcing material for duroplastics in the form of a web, knitted fabric or stitch bonded product of yarn, roving or loosely spun double yarn with continuous parallel arranged elementary filaments with a high modulus of elasticity characterized by a substantial part of the parallel elementary filaments free of any binding agent being spread apart or separated, by these cavities between the elementary filaments being predominantly filled by hollow plastic microspheres with a diameter of 20 to 300 μm and the resin pick up and specific weight being reduced.
Claim 6
Dependent Claim
41 words
A reinforcing material according to claim 3 whereby the hollow microspheres are embedded in such an amount that the thickness of the unbonded web, knitted fabric or stitch bonded product produced is 2- to 30-fold, the thickness of the starting material.
Claim 7
Dependent Claim
22 words
A reinforcing material according to claim 1, wherein the fibers with high modulus of elasticity consist of glass, carbonaceous or aramide fibers.
Claim 8
Dependent Claim
20 words
A reinforcing material according to claim 1, the true density of the hollow body filler being 0.02-0.2 kg/dm 3 .
Claim 9
Dependent Claim
31 words
A reinforcing material according to claim 1, characterized by the absorptive power for liquid curable resins, being adjusted to the desired value by the amount of the embedded hollow body filler.
Claim 10
Dependent Claim
15 words
A reinforcing material according to claim 1, wherein the hollow microspheres consist of a thermoplastic.
Claim 11
Dependent Claim
68 words
A duroplastic fiber composite with a low specific weight characterized by rovings, yarns or loosely spun double yarns of parallel arranged continous elementary filaments with a high modulus of elasticity, containing a reinforcing material, of which a substantial part is spread apart or moved apart and whose hollow cavities between the elementary filaments are predominantly filled with hollow plastic microspheres with a diameter of 20 to 300 μm.
Claim 12
Dependent Claim
68 words
A duroplastic fiber composite with a low specific weight characterized by rovings, yarns or loosely spun double yarns of parallel arranged continous elementary filaments with a high modulus of elasticity, containing a reinforcing material, of which a substantial part is spread apart or moved apart and whose hollow cavities between the elementary filaments are predominantly filled with hollow plastic microspheres with a diameter of 20 to 300 μm.
Claim 13
Dependent Claim
27 words
A composite according to claim 9, wherein the filaments comprise glass, the hollow plastic microspheres comprising a vinylidene chloride-acrylonitrile copolymer, the duroplastic comprising an unsaturated polyester resin.
References Cited (Backward Citations)
US4460642A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-10 | 1992-10-10 | 1993-04-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-10 | 1996-10-10 | 1997-04-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-10 | 2000-10-10 | 2001-04-11 | $7700.00 | Window Closed / Lapsed |