US4820355A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for fabricating monolithic aluminum structures
Assignee: Boeing North American Inc
•
Filing: 1987-03-30
•
Granted: 1989-04-11
•
Expires: 2007-03-30
Abstract
Abstract A method for forming monolithic structures from a plurality of aluminum or aluminum alloy sheets is provided which integrates a method for producing a selective fine grain structure in each of the sheets, with roll bonding and superplastic forming. The sheets are subjected to isothermal aging or controlled slow cooling to obtain a desired grain size in each of the respective sheets. Different heating and cooling treatments can be individually applied to each of the sheets so that the sheets can be tailored to have a fine grain or a coarser grain. Stop-off material is applied at selected areas of the sheets, and the resulting stack of sheets is subjected to cold roll bonding to bond adjacent surfaces of the sheets where stop-off material has not been applied. The roll bonding step also serves to plastically deform the sheets. The roll-bonded stack of sheets is then subjected to rapid heating for recrystallization of one or more of the sheets into a fine grain structure. After recrystallization, the sheets are subjected to superplastic forming into the desired monolithic structure.
Inventors
- 👤 Clifford C. Bampton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 21:05
CPC Classifications
B; B21; B21D; B21D47/00; B21D53/00; B21D53/02; B21D53/04; B21D53/045; B23; B23K; B23K20/00; B23K20/04; B23K20/18; B23K20/22; B23K20/233; B23K20/2336; B23K20/24; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/4935; Y10T29/49366; Y10T29/49369; Y10T29/49371; Y10T428/00; Y10T428/12; Y10T428/12292; Y10T428/12493; Y10T428/12736; Y10T428/12764
Claims Analysis
Total Claims: 37
Claim 1
Independent Claim
130 words
A process for producing a monolithic aluminum alloy structure from a plurality of aluminum alloy sheets which comprises the steps of: imparting a desired microstructure selectively to said sheets by isothermal aging or by aging under controlled slow cooling; providing stop-off material at selected areas of opposing surfaces of the sheets where it is desired that the sheets not be bonded together; stacking the sheets; cold roll bonding said stack of sheets to bond those portions thereof where said stop-off material has not been applied; rapidly heating the roll bonded stack of sheets under conditions to recrystallize the alloy in one or more of the sheets into a fine grain structure; and superplastically forming said stack of sheets at elevated temperature and pressure into a desired monolithic aluminum alloy structure.
Claim 2
Dependent Claim
130 words
A process for producing a monolithic aluminum alloy structure from a plurality of aluminum alloy sheets which comprises the steps of: imparting a desired microstructure selectively to said sheets by isothermal aging or by aging under controlled slow cooling; providing stop-off material at selected areas of opposing surfaces of the sheets where it is desired that the sheets not be bonded together; stacking the sheets; cold roll bonding said stack of sheets to bond those portions thereof where said stop-off material has not been applied; rapidly heating the roll bonded stack of sheets under conditions to recrystallize the alloy in one or more of the sheets into a fine grain structure; and superplastically forming said stack of sheets at elevated temperature and pressure into a desired monolithic aluminum alloy structure.
Claim 3
Dependent Claim
19 words
The process of claim 1, including the step of cooling said stack of sheets prior to said superplastic forming.
Claim 4
Dependent Claim
113 words
The process of claim 1, wherein said desired microstructure is obtained by: heating at least one of said sheets to a solid solution temperature to dissolve at least some of the precipitating constituents in said alloy sheet; cooling said at least one sheet by water quenching to a temperature below said solution temperature; subjecting said at least one sheet to isothermal heating at an overaging temperature above the precipitation hardening temperature but below said solution treating temperature; and plastically deforming and softening the alloy of said at least one sheet to obtain a fine grain microstructure by further heating and aging said alloy at a temperature equal to or below said overaging temperature.
Claim 5
Dependent Claim
31 words
The process of claim 3, said overaging temperature ranging from about 660° F. to about 750° F., and said further heating and aging temperature being at or below about 455° F.
Claim 6
Dependent Claim
28 words
The process of claim 3, said overaging temperature ranging from about 660° F. to about 750° F., and said softening comprising slow cooling down to about 390° F.
Claim 7
Dependent Claim
48 words
The process of claim 1, wherein said desired microstructure is obtained by heating at least one of said sheets to a solid solution temperature to dissolve at least some of the precipitating constituents in said alloy sheet; and subjecting said at least one sheet to controlled slow cooling.
Claim 8
Dependent Claim
31 words
The process of claim 6, said controlled slow cooling being carried out at a rate of about 36° F. per hour, and softening the alloy of said at least one sheet.
Claim 9
Dependent Claim
32 words
The process of claim 1, said roll bonding being carried out at ambient temperature and under conditions to effect a substantial reduction in thickness of the sheets in said stack of sheets.
Claim 10
Dependent Claim
35 words
The process of claim 1, said rapid heating to recrystallize said alloy taking place at a rate ranging from about 1° F. to about 1000° F. per minute, to a temperature of about 960° F.
Claim 11
Dependent Claim
28 words
The process of claim 1, said stop-off material being a thermally decomposable material and providing a slight billowing of adjacent sheets during said rapid heating and recrystallization step.
Claim 12
Dependent Claim
53 words
The process of claim 10, including: introducing tubing into the stack of sheets in communication with the billowed areas between adjacent sheets of the stack; and injecting gas through said tubing and into the unbonded billowed areas between the sheets of the stack to generate superplastic forming pressure during said superplastic forming step.
Claim 13
Dependent Claim
71 words
The process of claim 1, said stop-off material being a non-decomposable material, and including: indexing the non-bonded areas between adjacent sheets containing stop-off material; introducing tubing into the stack of sheets in communication with said indexed areas between adjacent sheets of the stack; and injecting gas through said tubing and into the indexed unbonded areas between the sheets of the stack to generate superplastic forming pressure during said superplastic forming step.
Claim 14
Dependent Claim
55 words
A process for producing a three-sheet aluminum alloy truss core sandwich structure according to claim 1, including carrying out the initial aging treatment for imparting a desired microstructure to said sheets under conditions to obtain different final grain sizes in the alloy of the respective sheets in the stack of sheets subjected to superplastic forming.
Claim 15
Dependent Claim
51 words
The process of claim 13, wherein said aging treatment is carried out so that the center alloy sheet has a very fine grain size and the outer alloy sheets have a relatively coarse grain size, whereby said center sheet can be stretched by superplastic forming farther than the two outer sheets.
Claim 16
Independent Claim
197 words
A method for producing a monolithic aluminum or aluminum alloy structure formed of a plurality of aluminum or aluminum alloy workpiece components, comprising: heating at least one of the workpiece components to a first desired maximum temperature; fluid quenching said at least one of the workpiece components to a desired minimum temperature; further heating said at least one of the workpiece components to a second desired maximum temperture below the highest temperature attained prior to fluid quenching and imparting a desired grain structure to said at least one component; applying a stop-off material at selected areas of opposing surfaces of the workpiece components; assembling said workpiece components into a stack; applying cold roll bonding pressure at outer surfaces of the workpiece components in said stack, said pressure being of sufficient magnitude to plastically deform the components and to bond the components together at those areas thereof where said stop-off material has not been applied; heating the roll bonded stack of workpiece components, said heating being at a sufficient rate and at a sufficient temperature to recrystallize the matrix around the precipitates therein; and superplastically forming at least one of the workpiece components into the desired monolithic structure.
Claim 17
Independent Claim
197 words
A method for producing a monolithic aluminum or aluminum alloy structure formed of a plurality of aluminum or aluminum alloy workpiece components, comprising: heating at least one of the workpiece components to a first desired maximum temperature; fluid quenching said at least one of the workpiece components to a desired minimum temperature; further heating said at least one of the workpiece components to a second desired maximum temperture below the highest temperature attained prior to fluid quenching and imparting a desired grain structure to said at least one component; applying a stop-off material at selected areas of opposing surfaces of the workpiece components; assembling said workpiece components into a stack; applying cold roll bonding pressure at outer surfaces of the workpiece components in said stack, said pressure being of sufficient magnitude to plastically deform the components and to bond the components together at those areas thereof where said stop-off material has not been applied; heating the roll bonded stack of workpiece components, said heating being at a sufficient rate and at a sufficient temperature to recrystallize the matrix around the precipitates therein; and superplastically forming at least one of the workpiece components into the desired monolithic structure.
Claim 18
Dependent Claim
44 words
The method of claim 15, further including heating said at least one of the workpiece components to a third desired maximum temperture subsequent to said heating to the second desired maximum temperature, the third desired maximum temperature being below the second desired maximum temperature.
Claim 19
Dependent Claim
14 words
The method of claim 15, wherein said desired minimum temperature is approximately room temperature.
Claim 20
Dependent Claim
62 words
The method of claim 15, wherein said stop-off material is thermally decomposable and releases gas upon heating to a selected temperature so that at least one of the workpiece components billows outwardly in the selected areas where the stop-off material has been applied, whereby the workpiece components adjacent to the selected areas at least partially define a cavity between the workpiece components.
Claim 21
Dependent Claim
47 words
The method of claim 18, further including providing a tube extending into the stack of workpiece components and in communication with the billowed areas for passage of a pressurized fluid therethrough and into the cavities, for said superplastic forming of at least one of the workpiece components.
Claim 22
Dependent Claim
45 words
The method of claim 15, further including cooling at least one of the workpiece components at a controlled rate to below approximately 390° F., following said further heating step, the cooling rate being in the range of approximately 18° F. to 50° F. per hour.
Claim 23
Dependent Claim
19 words
The method of claim 15, wherein at least one of the workpiece components comprises 7,000 series aluminum alloy material.
Claim 24
Dependent Claim
19 words
The method of claim 15, wherein at least one of the workpiece components comprises 2,000 series aluminum alloy material.
Claim 25
Dependent Claim
15 words
The method of claim 15, wherein said first desired maximum temperature is approximately 920° F.
Claim 26
Dependent Claim
22 words
The method of claim 15, wherein said second desired maximum temperature is approximately 750° F. for a duration of approximately 8 hours.
Claim 27
Independent Claim
168 words
A method of producing a monolithic aluminum or aluminum alloy structure formed of a plurality of aluminum or aluminum alloy sheets, comprising: heating at least one of the sheets to a desired maximum temperature; cooling the sheets at a controlled rate to a desired minimum temperature and imparting a desired grain structure to said at least one sheet; providing stop-off material at selected areas of opposing surfaces of the sheets where it is desired that the sheets not be bonded together; assembling said sheets into a stack; applying cold roll bonding pressure at outer surfaces of the sheets in said stack, said pressure being of sufficient magnitude to plastically deform the sheets and to bond the sheets together at those areas thereof where stop-off material has not been applied; further heating the roll bonded stack of sheets in order to recrystallize the matrix around the precipitates in the sheets and diffusion strengthen the bond; and superplastically forming at least one of the sheets into the desired monolithic structure.
Claim 28
Independent Claim
168 words
A method of producing a monolithic aluminum or aluminum alloy structure formed of a plurality of aluminum or aluminum alloy sheets, comprising: heating at least one of the sheets to a desired maximum temperature; cooling the sheets at a controlled rate to a desired minimum temperature and imparting a desired grain structure to said at least one sheet; providing stop-off material at selected areas of opposing surfaces of the sheets where it is desired that the sheets not be bonded together; assembling said sheets into a stack; applying cold roll bonding pressure at outer surfaces of the sheets in said stack, said pressure being of sufficient magnitude to plastically deform the sheets and to bond the sheets together at those areas thereof where stop-off material has not been applied; further heating the roll bonded stack of sheets in order to recrystallize the matrix around the precipitates in the sheets and diffusion strengthen the bond; and superplastically forming at least one of the sheets into the desired monolithic structure.
Claim 29
Dependent Claim
14 words
The method of claim 25, wherein the desired maximum temperature is approximately 920° F.
Claim 30
Dependent Claim
14 words
The method of claim 25, wherein said cooling is carried out by water quenching.
Claim 31
Dependent Claim
18 words
The method of claim 25, wherein the cooling is performed at the rate of 36° F. per hour.
Claim 32
Dependent Claim
14 words
The method of claim 25, wherein the desired minimum temperature is approximately room temperature.
Claim 33
Dependent Claim
38 words
The method of claim 25, said further heating being carried out at a rate ranging from about 1° F. to about 1,000° F., per minute, to a final temperature ranging from about 450° F. to about 990° F.
Claim 34
Dependent Claim
51 words
The method of claim 25, wherein one of the sheets has a grain structure different from at least one of the remaining sheets prior to said superplastic forming step, so that at least one of the sheets has a superplastic deformation property different from at least one of the other sheets.
Claim 35
Dependent Claim
77 words
The method of claim 25, wherein said stop-off material is thermally decomposable and releases a gas upon heating to a selected temperature during said further heating step, to produce a billowed area at adjacent surfaces of the sheets, the billowed area defining a cavity and allowing insertion of a tube through at least one of the sheets, the tube communicating with the cavity to provide pressurized gas for superplastic forming of the sheets into the desired structure.
Claim 36
Independent Claim
279 words
A method of producing a monolithic aluminum or aluminum alloy structure formed of a plurality of heat treatable aluminum or aluminum alloy sheets, comprising: heating the sheets to approximately 920° F.; fluid quenching the sheets to a desired minimum temperature immediately after said heating; isothermally heating the sheets at approximately 750° F. for approximately 8 hours; isothermally heating the sheets at approximately 455° F. for approximately 24 hours in order to soften the sheets; positioning the sheets in a stack so that the sheets have opposing surfaces; applying stop-off material to at least one selected areas of the opposing surfaces of the sheets in order to prevent bonding of the sheets at said area; cooling the sheets to approximately room temperature; applying a rolling pressure at ambient temperature to outer surfaces of the sheets in order to concurrently roll bond the sheets at desired portions thereof and plastically deform the sheets; rapidly heating the sheets to a desired maximum temperature to recrystallize the alloy in said sheets, said rapid heating being sufficient to provide a desired fine grain structure to the sheets; providing a tunnel between at least two of the opposing surfaces of the sheets at edge portions of the sheets for insertion of a tube therebetween, the tube providing a passageway for pressurized gas between the sheets to said area where the stop-off material has been applied; heating the sheets to superplastic forming temperature; and injecting pressurized gas through the tube into the area between the sheets where stop-off material has been applied, the pressurized gas being sufficient to superplastically deform and elongate at least a portion of the sheets in order to provide the desired structure.
Claim 37
Independent Claim
279 words
A method of producing a monolithic aluminum or aluminum alloy structure formed of a plurality of heat treatable aluminum or aluminum alloy sheets, comprising: heating the sheets to approximately 920° F.; fluid quenching the sheets to a desired minimum temperature immediately after said heating; isothermally heating the sheets at approximately 750° F. for approximately 8 hours; isothermally heating the sheets at approximately 455° F. for approximately 24 hours in order to soften the sheets; positioning the sheets in a stack so that the sheets have opposing surfaces; applying stop-off material to at least one selected areas of the opposing surfaces of the sheets in order to prevent bonding of the sheets at said area; cooling the sheets to approximately room temperature; applying a rolling pressure at ambient temperature to outer surfaces of the sheets in order to concurrently roll bond the sheets at desired portions thereof and plastically deform the sheets; rapidly heating the sheets to a desired maximum temperature to recrystallize the alloy in said sheets, said rapid heating being sufficient to provide a desired fine grain structure to the sheets; providing a tunnel between at least two of the opposing surfaces of the sheets at edge portions of the sheets for insertion of a tube therebetween, the tube providing a passageway for pressurized gas between the sheets to said area where the stop-off material has been applied; heating the sheets to superplastic forming temperature; and injecting pressurized gas through the tube into the area between the sheets where stop-off material has been applied, the pressurized gas being sufficient to superplastically deform and elongate at least a portion of the sheets in order to provide the desired structure.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-10 | 1992-10-10 | 1993-04-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-10 | 1996-10-10 | 1997-04-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-10 | 2000-10-10 | 2001-04-11 | $7700.00 | Window Closed / Lapsed |