Process for making composite bearing material produced thereby
Assignee: Federal Mogul World Wide LLC
•
Filing: 1987-08-31
•
Granted: 1989-04-04
•
Expires: 2007-08-31
Abstract
Abstract A process for making a composite bearing material comprising a steel backed, prealloyed, lead-bronze sintered powder metal matrix whereby the first sinter step includes induction heating the prealloyed powder and steel backing to above 650° C. and thereafter sintering the same at temperatures of about 850° C. in a second sintering furnace. A composite bearing material made by the same process and comprising a lead particle size averaging less than about 8 microns and having no lead islands larger than about 44 microns.
Inventors
- 👤 Robert G. Alexander
- 👤 George C. Pratt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 10:35
CPC Classifications
B; B22; B22F; B22F7/00; B22F7/02; B22F7/04; B22F2998/00; B22F2998/10; Y; Y10; Y10S; Y10S384/00; Y10S384/90; Y10S384/912; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12063; Y10T428/12104; Y10T428/12111; Y10T428/12118; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12903; Y10T428/12917; Y10T428/12924
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
76 words
A copper lead tin alloy with the lead content ranging between 8 and 35 percent by weight and the tin content ranging between 0.5 and 10.0 percent by weight, and the balance essentially all copper, the microstructure of which consists of interconnected lead islands in a copper-rich matrix, the average size of the lead islands being less than 8 microns and there being not more than 1 percent of the lead islands larger than 40 microns.
Claim 2
Dependent Claim
76 words
A copper lead tin alloy with the lead content ranging between 8 and 35 percent by weight and the tin content ranging between 0.5 and 10.0 percent by weight, and the balance essentially all copper, the microstructure of which consists of interconnected lead islands in a copper-rich matrix, the average size of the lead islands being less than 8 microns and there being not more than 1 percent of the lead islands larger than 40 microns.
Claim 3
Dependent Claim
27 words
A copper lead tin alloy as claimed in claim 1, with the lead content between 13 and 26 percent, and the tin between 0.5 and 5.0 percent.
Claim 4
Dependent Claim
115 words
A composite bearing material comprising a steel backing strip having a leaded-bronze bearing lining tenaciously bonded to at least one face thereof, said bearing lining being substantially fully dense and containing about 8 percent to about 35 percent lead, up to about 10 percent tin and the balance essentially all copper, said bearing lining furthr characterized by the lead constituted thereof being substantially uniformly distributed throughout the lining matrix in the form of fine-sized lead particles at a particle count of at least about 1550 per square millimeter, and having an average size less than about 8 microns, and wherein no more than about 0.4 percent of said lead particles are larger than 36 microns.
Claim 5
Dependent Claim
115 words
A composite bearing material comprising a steel backing strip having a leaded-bronze bearing lining tenaciously bonded to at least one face thereof, said bearing lining being substantially fully dense and containing about 8 percent to about 35 percent lead, up to about 10 percent tin and the balance essentially all copper, said bearing lining furthr characterized by the lead constituted thereof being substantially uniformly distributed throughout the lining matrix in the form of fine-sized lead particles at a particle count of at least about 1550 per square millimeter, and having an average size less than about 8 microns, and wherein no more than about 0.4 percent of said lead particles are larger than 36 microns.
Claim 6
Dependent Claim
48 words
A composite bearing material as claimed in claim 3, with an interlayer of nickel bonded to said bearing lining and with an overlay of lead based alloy bonded to said interlayer, the thickness of the interlayer being 0.001-0.005 mm, and the thickness of the overlayer being 0.01-0.05 mm.
Claim 7
Dependent Claim
26 words
A composite bearing material as claimed in claim 4 with the lead content between 13 and 26 percent, and the tin between 0.5 and 5.0 percent.
Claim 8
Dependent Claim
104 words
A process for producing steel backed strip with a lining of copper-lead-tin alloy in which copper-lead-tin alloy powder is spread onto steel strip, the temperature of the strip is raised in an induction coil to a temperature in excess of 700° C., the temperature being subsequently raised by other means to approximately 800°-850° C. to sinter the powder particles to one another and to the steel, the total time spent by the strip between 650° and 850° C. being less than two minutes, the whole heating operation being carried out in a reducing atmosphere, and the sintered layer being subsequently roll compacted and re-sintered.
Claim 9
Dependent Claim
104 words
A process for producing steel backed strip with a lining of copper-lead-tin alloy in which copper-lead-tin alloy powder is spread onto steel strip, the temperature of the strip is raised in an induction coil to a temperature in excess of 700° C., the temperature being subsequently raised by other means to approximately 800°-850° C. to sinter the powder particles to one another and to the steel, the total time spent by the strip between 650° and 850° C. being less than two minutes, the whole heating operation being carried out in a reducing atmosphere, and the sintered layer being subsequently roll compacted and re-sintered.
References Cited (Backward Citations)
US2040053A
Cited
US2280103A
Cited
US2635020A
Cited
US2970933A
Cited
US2986464A
Cited
US3154844A
Cited
US3445909A
Cited
US3730705A
Cited
US4002472A
Cited
US4206268A
Cited
US4406857A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-04-03 | 1992-10-03 | 1993-04-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-04-03 | 1996-10-03 | 1997-04-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-04-03 | 2000-10-03 | 2001-04-04 | $7700.00 | Window Closed / Lapsed |